Dissolution of UK high-level waste glass under simulated hyperalkaline conditions of a colocated geological disposal facility

We report analysis of chemical durability of UK HLW MW+25% simulant glass under model hyperalkaline conditions of a colocated geological disposal facility. Glass powders and monoliths were dissolved for 168 days in saturated Ca(OH). Dissolution in the presence of high concentrations of Ca (>200 mg/L) was an order of magnitude lower than dissolution in water. Dissolution of Si did not occur until a Ca:Si ratio of <2 was achieved. The mechanism of dissolution involved the incorporation of Ca into the hydrated surface (initial, incubation regime), the precipitation of C-S-H phases, including a range of compositions in the C-(N)-(A)-S-H and M-S-H systems (intermediate regime), and the precipitation of C-S-H phases (the residual regime). Thermodynamic analysis and consideration of the CaO-SiO-HO phase diagram suggest that the rate-limiting step of glass dissolution in Ca-rich solutions is Ca-Si equilibrium, involving the precipitation of C-S-H phases, which change in chemical composition as a function of solution chemistry. In low SA/V ratio experiments, the dissolution progressed only to the initial incubation regime, resulting from fewer surface sites for Ca incorporation. Overall, these results suggest that Ca and Si in solution play an important role in the long-term durability of UK HLW in Ca-rich solutions. © 2013 The Authors. International Journal of Applied Glass Science published by John Wiley & Sons Ltd on behalf of The American Ceramic Society and Wiley Periodicals, Inc.

[1]  N. Hyatt,et al.  Formation of alteration products during dissolution of vitrified ILW in a high-pH calcium-rich solution , 2013 .

[2]  S. Gin,et al.  Antagonist effects of calcium on borosilicate glass alteration , 2013 .

[3]  N. Hyatt,et al.  Encapsulation of TRISO particle fuel in durable soda-lime-silicate glasses , 2013 .

[4]  N. Hyatt,et al.  Dissolution of vitrified wastes in a high-pH calcium-rich solution , 2013 .

[5]  Andreas C Scheinost,et al.  Np(V/VI) redox chemistry in cementitious systems: XAFS investigations on the speciation under anoxic and oxidizing conditions , 2013 .

[6]  N. Hyatt,et al.  Chemical durability of vitrified wasteforms: effects of pH and solution composition , 2012, Mineralogical Magazine.

[7]  P. Frugier,et al.  Characterization of Alteration Phases on HLW Glasses After 15 Years of PCT Leaching , 2012 .

[8]  P. Frugier,et al.  Glass–water interphase reactivity with calcium rich solutions , 2011 .

[9]  P. Hrma Crystallization during processing of nuclear waste glass , 2010 .

[10]  C. Jantzen,et al.  The Product Consistency Test (PCT): How and Why it Was Developed , 2008 .

[11]  Patrick Jollivet,et al.  Insight into silicate-glass corrosion mechanisms. , 2008, Nature materials.

[12]  Jean-Eric Lartigue,et al.  SON68 nuclear glass dissolution kinetics: Current state of knowledge and basis of the new GRAAL model , 2008 .

[13]  Eric M. Pierce,et al.  An experimental study of the dissolution rates of simulated aluminoborosilicate waste glasses as a function of pH and temperature under dilute conditions , 2008 .

[14]  J. Crovisier,et al.  Long-term corrosion of two nuclear waste reference glasses (MW and SON68): A kinetic and mineral alteration study , 2006 .

[15]  H. Taylor,et al.  Solubility and structure of calcium silicate hydrate , 2004 .

[16]  S. Gin,et al.  SON 68 nuclear glass alteration kinetics between pH 7 and pH 11.5 , 2001 .

[17]  D. P. Trivedi,et al.  Single-pass flow-through experiments on a simulated waste glass in alkaline media at 40°C.: I. Experiments conducted at variable solution flow rate to glass surface area ratio , 2000 .

[18]  S. Gin Protective Effect of the Alteration Gel: A Key Mechanism in the Long-Term Behavior of Nuclear Waste Glass , 2000 .

[19]  David L. Parkhurst,et al.  USER'S GUIDE TO PHREEQC A COMPUTER PROGRAM FOR SPECIATION, REACTION-PATH, ADVECTIVE-TRANSPORT, AND INVERSE GEOCHEMICAL CALCULATIONS , 1995 .

[20]  U. R. Berner,et al.  Evolution of pore water chemistry during degradation of cement in a radioactive waste repository environment , 1992 .

[21]  N. Godon,et al.  R717 Glass Alteration in the Presence of Mortar: Effect of the Cement Grade , 1991 .

[22]  Hamlin M. Jennings,et al.  Aqueous Solubility Relationships for Two Types of Calcium Silicate Hydrate , 1986 .

[23]  B. Grambow,et al.  Leach Testing of Waste Glasses Under Near-Saturation Conditions , 1983 .