A soluble and air-stable organic semiconductor with high electron mobility

Electronic devices based on organic semiconductors offer an attractive alternative to conventional inorganic devices due to potentially lower costs, simpler packaging and compatibility with flexible substrates. As is the case for silicon-based microelectronics, the use of complementary logic elements—requiring n- and p-type semiconductors whose majority charge carriers are electrons and holes, respectively—is expected to be crucial to achieving low-power, high-speed performance. Similarly, the electron-segregating domains of photovoltaic assemblies require both n- and p-type semiconductors. Stable organic p-type semiconductors are known, but practically useful n-type semiconductor materials have proved difficult to develop, reflecting the unfavourable electrochemical properties of known, electron-demanding polymers. Although high electron mobilities have been obtained for organic materials, these values are usually obtained for single crystals at low temperatures, whereas practically useful field-effect transistors (FETs) will have to be made of polycrystalline films that remain functional at room temperature. A few organic n-type semiconductors that can be used in FETs are known, but these suffer from low electron mobility, poor stability in air and/or demanding processing conditions. Here we report a crystallographically engineered naphthalenetetracarboxylic diimide derivative that allows us to fabricate solution-cast n-channel FETs with promising performance at ambient conditions. By integrating our n-channel FETs with solution-deposited p-channel FETs, we are able to produce a complementary inverter circuit whose active layers are deposited entirely from the liquid phase. We expect that other complementary circuit designs can be realized by this approach as well.

[1]  A. J. Lovinger,et al.  n-Channel Organic Transistor Materials Based on Naphthalene Frameworks , 1996 .

[2]  A. Rademacher,et al.  Lösliche Perylen‐Fluoreszenzfarbstoffe mit hoher Photostabilität , 1982 .

[3]  Zhenan Bao,et al.  Complementary circuits with organic transistors , 1996 .

[4]  G. Horowitz,et al.  Growth and Characterization of Sexithiophene Single Crystals , 1995 .

[5]  J. Rogers,et al.  Facile deposition processes for semiconducting molecular solids , 1999 .

[6]  R. Sarpeshkar,et al.  Large-scale complementary integrated circuits based on organic transistors , 2000, Nature.

[7]  Theo Siegrist,et al.  The crystal structure of the high-temperature polymorph of α–hexathienyl (α–6T/HT) , 1995 .

[8]  C. M. Hart,et al.  Low-cost all-polymer integrated circuits , 1998, Proceedings of the 24th European Solid-State Circuits Conference.

[9]  C. M. Hart,et al.  Organic field-effect transistors and all-polymer integrated circuits , 1999 .

[10]  Robert C. Haddon,et al.  C60 thin film transistors , 1995 .

[11]  Zhenan Bao,et al.  New Air-Stable n-Channel Organic Thin Film Transistors , 1998 .

[12]  Gilles Horowitz,et al.  Organic Field‐Effect Transistors , 1998 .

[13]  M. Fox Polymeric and supramolecular arrays for directional energy and electron transport over macroscopic distances , 1992 .

[14]  Howard E. Katz,et al.  Field-Effect Transistors Based on Thiophene Hexamer Analogues with Diminished Electron Donor Strength , 1999 .

[15]  D. M. Leeuw,et al.  Stability of n-type doped conducting polymers and consequences for polymeric microelectronic devices , 1997 .

[16]  Masaaki Yokoyama,et al.  Bipolar‐charge‐transporting organic photoconductors , 1991 .

[17]  D. Fichou,et al.  Growth and structural characterization of the Quasi–2D single crystal of α‐octithiophene , 1996 .