Three-dimensional printing of hierarchical liquid-crystal-polymer structures

Fibre-reinforced polymer structures are often used when stiff lightweight materials are required, such as in aircraft, vehicles and biomedical implants. Despite their very high stiffness and strength1, such lightweight materials require energy- and labour-intensive fabrication processes2, exhibit typically brittle fracture and are difficult to shape and recycle3,4. This is in stark contrast to lightweight biological materials such as bone, silk and wood, which form by directed self-assembly into complex, hierarchically structured shapes with outstanding mechanical properties5–11, and are circularly integrated into the environment. Here we demonstrate a three-dimensional (3D) printing approach to generate recyclable lightweight structures with hierarchical architectures, complex geometries and unprecedented stiffness and toughness. Their features arise from the self-assembly of liquid-crystal polymer molecules into highly oriented domains during extrusion of the molten feedstock material. By orienting the molecular domains with the print path, we are able to reinforce the polymer structure according to the expected mechanical stresses, leading to stiffness, strength and toughness that outperform state-of-the-art 3D-printed polymers by an order of magnitude and are comparable with the highest-performance lightweight composites1,12. The ability to combine the top-down shaping freedom of 3D printing with bottom-up molecular control over polymer orientation opens up the possibility to freely design and realize structures without the typical restrictions of current manufacturing processes.3D printing of liquid-crystal polymers can create lightweight hierarchical structures with very high stiffness and toughness.

[1]  N. Moszner,et al.  Chain orientation in melt-extruded samples of Vectra A, Vectra B, and blends in relation to the mechanical properties , 1998 .

[2]  Donald G. Baird,et al.  Effects of processing conditions on short TLCP fiber reinforced FDM parts , 1998 .

[3]  Yasuaki Seki,et al.  Biological materials: Structure and mechanical properties , 2008 .

[4]  R. Ritchie,et al.  Bioinspired structural materials. , 2014, Nature Materials.

[5]  J. Lewis,et al.  3D Printing of Liquid Crystal Elastomeric Actuators with Spatially Programed Nematic Order , 2018, Advanced materials.

[6]  Fritz Vollrath,et al.  Liquid crystalline spinning of spider silk , 2001, Nature.

[7]  L. Yeo,et al.  A Novel Acoustomicrofluidic Nebulization Technique Yielding New Crystallization Morphologies , 2018, Advanced materials.

[8]  W. Cong,et al.  Additive manufacturing of carbon fiber reinforced thermoplastic composites using fused deposition modeling , 2015 .

[9]  Markus J. Buehler,et al.  Nonlinear material behaviour of spider silk yields robust webs , 2012, Nature.

[10]  W. Burghardt,et al.  Orientation dynamics in commercial thermotropic liquid crystalline polymers in transient shear flows , 2007 .

[11]  P. Wright,et al.  Anisotropic material properties of fused deposition modeling ABS , 2002 .

[12]  James Pe,et al.  Engineering Design with Polymers and Composites , 2005 .

[13]  T. Peijs,et al.  High-performance liquid-crystalline polymer films for monolithic “composites” , 2016 .

[14]  Cedric P. Ambulo,et al.  Four-dimensional Printing of Liquid Crystal Elastomers. , 2017, ACS applied materials & interfaces.

[15]  R. Ritchie,et al.  On the Mechanistic Origins of Toughness in Bone , 2010 .

[16]  María López-Valdeolivas,et al.  4D Printed Actuators with Soft-Robotic Functions. , 2018, Macromolecular rapid communications.

[17]  Jan-Anders E. Månson,et al.  Assessing the life cycle costs and environmental performance of lightweight materials in automobile applications , 2011 .

[18]  Rathanawan Magaraphan,et al.  Thermal and mechanical properties of polylactic acid (PLA) and bagasse carboxymethyl cellulose (CMCB) composite by adding isosorbide diesters , 2015 .

[19]  Joshua M. Pearce,et al.  Mechanical properties of components fabricated with open-source 3-D printers under realistic environmental conditions , 2014 .

[20]  Joël Cugnoni,et al.  Thin ply composites: Experimental characterization and modeling of size-effects , 2014 .

[21]  S. Warner,et al.  Towards understanding the increase in strength of thermotropic polyesters with heat treatment , 1994 .

[22]  G. Groeninckx,et al.  Morphology and mechanical-properties of thermoplastic composites containing a thermotropic liquid-crystalline polymer , 1990 .

[23]  K. McDonnell,et al.  Fabrication of Continuous Carbon, Glass and Kevlar fibre reinforced polymer composites using Additive Manufacturing , 2017 .

[24]  Yuvraj Singh Negi,et al.  Effect of aluminum nitride on thermomechanical properties of high performance PEEK , 2007 .

[25]  Johannes E. Schindelin,et al.  Fiji: an open-source platform for biological-image analysis , 2012, Nature Methods.

[26]  A. Greiner,et al.  Preparation and characterization of fibres from a thermotropic liquid crystal polyester with non-coplanar biphenylene units , 1993 .

[27]  Circular economy: Getting the circulation going , 2016, Nature.

[28]  Syed H. Masood,et al.  Dynamic mechanical properties of ABS material processed by fused deposition modelling , 2012 .

[29]  Ingo Burgert,et al.  Exploring the micromechanical design of plant cell walls. , 2006, American journal of botany.

[30]  Mario Viani,et al.  Molecular mechanistic origin of the toughness of natural adhesives, fibres and composites , 1999, Nature.

[31]  Rob Boom,et al.  Recycling of composite materials , 2012 .

[32]  Bor-Kuan Chen,et al.  Synthesis and properties of liquid crystalline polymers with low Tm and broad mesophase temperature ranges , 2005 .

[33]  Richard Weinkamer,et al.  Nature’s hierarchical materials , 2007 .

[34]  S. Picken,et al.  Structure and rheology of aramid solutions: x-ray scattering measurements , 1990 .

[35]  R. Libanori,et al.  Mineral Nano‐Interconnectivity Stiffens and Toughens Nacre‐like Composite Materials , 2017, Advanced materials.