High temperature Seebeck coefficient and resistance measurement system for thermoelectric materials in the thin disk geometry.

A versatile apparatus to measure the cross-plane Seebeck coefficient and the resistivity of bulk samples shaped as disks or thin plates, over a temperature range of 300 K-620 K with possible extension to higher temperatures, is presented. It is constructed from readily available equipment and instrumentation with parts that are easily manufactured. The Seebeck coefficient is measured over an average region of the sample under steady-state conditions. The sample resistance is measured using a four-point alternating current method and scaled to room temperature measurements with known geometry to calculate resistivity. A variety of sample shapes are supported. Most importantly, the support of the thin disk geometry allows for the very same samples to be used in a laser flash instrument. The design allows for rough vacuum, high vacuum, or purging with inert gases in the sample chamber. Measurements on thermoelectric ZnSb and a Ni reference material are presented.

[1]  J. R. Culham,et al.  Review of Thermal Conductance Models for Joints Incorporating Enhancement Materials , 2003 .

[2]  O. Boffoue,et al.  Experimental setup for the measurement of the electrical resistivity and thermopower of thin films and bulk materials , 2005 .

[3]  G. J. Snyder,et al.  A high temperature apparatus for measurement of the Seebeck coefficient. , 2011, The Review of scientific instruments.

[4]  F. Disalvo,et al.  Thermoelectric cooling and power generation , 1999, Science.

[5]  A. Burkov.  Measurements of Resistivity and Thermopower: Principles and Practical Realization , 2005 .

[6]  Ctirad Uher,et al.  Apparatus for Seebeck coefficient and electrical resistivity measurements of bulk thermoelectric materials at high temperature , 2005 .

[7]  R. J. Jenkins,et al.  Flash Method of Determining Thermal Diffusivity, Heat Capacity, and Thermal Conductivity , 1961 .

[8]  Eckhard Müller,et al.  Macroscopic thermoelectric inhomogeneities in (AgSbTe2)x(PbTe)1−x , 2005 .

[9]  T. Tritt,et al.  Sample probe to measure resistivity and thermopower in the temperature range of 300–1000K , 2006 .

[10]  A. T. Burkov,et al.  Experimental set-up for thermopower and resistivity measurements at 100-1300 K , 2001 .

[11]  Z. Q. Lu,et al.  Round-robin measurements of two candidate materials for a Seebeck coefficient Standard Reference Material™ , 2009 .

[12]  G. J. Snyder,et al.  Doping of p‐type ZnSb: Single parabolic band model and impurity band conduction , 2011 .

[13]  C. Uher,et al.  High temperature Seebeck coefficient metrology , 2010 .

[14]  D. Chung,et al.  Carbon black pastes as coatings for improving thermal gap-filling materials , 2006 .

[15]  C. Domenicali,et al.  Thermoelectric Power and Electrical Resistivity of Dilute Alloys of Silicon in Copper, Nickel, and Iron , 1955 .

[16]  T. Tritt.  Electrical and Thermal Transport Measurement Techniques for Evaluation of the Figure-of-Merit of Bulk Thermoelectric Materials , 2005 .