Kinetics of Intermetallic Compound Formation at the Interface Between Sn-3.0Ag-0.5Cu Solder and Cu-Zn Alloy Substrates

The growth kinetics of an intermetallic compound (IMC) layer formed between Sn-3.5Ag-0.5Cu (SAC) solders and Cu-Zn alloy substrates was investigated for samples aged at different temperatures. Scallop-shaped Cu6Sn5 formed after soldering by dipping Cu or Cu-10 wt.%Zn wires into the molten solder at 260°C. Isothermal aging was performed at 120°C, 150°C, and 180°C for up to 2000 h. During the aging process, the morphology of Cu6Sn5 changed to a planar type in both specimens. Typical bilayer of Cu6Sn5 and Cu3Sn and numerous microvoids were formed at the SAC/Cu interfaces after aging, while Cu3Sn and microvoids were not observed at the SAC/Cu-Zn interfaces. IMC growth on the Cu substrate was controlled by volume diffusion in all conditions. In contrast, IMC growth on Cu-Zn specimens was controlled by interfacial reaction for a short aging time and volume diffusion kinetics for a long aging time. The growth rate of IMCs on Cu-Zn substrates was much slower due to the larger activation energy and the lower layer growth coefficient for the growth of Cu-Sn IMCs. This effect was more prominent at higher aging temperatures.

[1]  Jin Yu,et al.  Effects of sulfide-forming element additions on the Kirkendall void formation and drop impact reliability of Cu/Sn-3.5Ag solder joints , 2009 .

[2]  Hyuck-Mo Lee,et al.  Wettability and interfacial reactions of Sn-based Pb-free solders with Cu–xZn alloy under bump metallurgies , 2009 .

[3]  Young-Ho Kim,et al.  Sn-Ag-Cu and Sn-Cu solders: Interfacial reactions with platinum , 2004 .

[4]  Li Wang,et al.  Intermetallic compounds growth between Sn–3.5Ag lead-free solder and Cu substrate by dipping method , 2005 .

[5]  Young-Ho Kim,et al.  A new solder wetting layer for Pb-free solders , 2009 .

[6]  D. R. Frear,et al.  Morphology, kinetics, and thermodynamics of solid-state aging of eutectic SnPb and Pb-free solders (Sn–3.5Ag, Sn–3.8Ag–0.7Cu and Sn–0.7Cu) on Cu , 2002 .

[7]  Jin Yu,et al.  Interfacial reactions of Sn-Ag-Cu solders modified by minor Zn alloying addition , 2006 .

[8]  S. Jung,et al.  Effect of isothermal aging on intermetallic compound layer growth at the interface between Sn-3.5Ag-0.75Cu solder and Cu substrate , 2004 .

[9]  Jin Yu,et al.  Effect of Zn on the intermetallics formation and reliability of Sn-3.5Ag solder on a Cu pad , 2007 .

[10]  Da-Yuan Shih,et al.  Effects of Minor Additions of Zn on Interfacial Reactions of Sn-Ag-Cu and Sn-Cu Solders with Various Cu Substrates during Thermal Aging , 2007 .

[11]  Feng Gao,et al.  Depressing effect of 0.2wt.%Zn addition into Sn-3.0Ag-0.5Cu solder alloy on the intermetallic growth with Cu substrate during isothermal aging , 2006 .

[12]  Won Kyoung Choi,et al.  Effect of soldering and aging time on interfacial microstructure and growth of intermetallic compounds between Sn-3.5Ag solder alloy and Cu substrate , 2000 .

[13]  Jenq-Gong Duh,et al.  Interfacial Reaction of Sn and Cu-xZn Substrates After Reflow and Thermal Aging , 2010 .

[14]  Bo-In Noh,et al.  Wettability and interfacial reactions of Sn–Ag–Cu/Cu and Sn–Ag–Ni/Cu solder joints , 2009 .

[15]  S. Jung,et al.  Reaction diffusions of Cu6Sn5 and Cu3Sn intermetallic compound in the couple of Sn-3.5Ag eutectic solder and copper substrate , 2003 .

[16]  Chunqing Wang,et al.  Electronic structure mechanism for the wettability of Sn-based solder alloys , 2002 .

[17]  C. Kao,et al.  Strong Zn concentration effect on the soldering reactions between Sn-based solders and Cu , 2006 .

[18]  Kazuaki Ano,et al.  Kirkendall void formation in eutectic SnPb solder joints on bare Cu and its effect on joint reliability , 2005 .