AFM observation of surface topography of fibre Bragg gratings fabricated in germanium-boron codoped fibres and hydrogen-loaded fibres

This paper reports the measurement of the surface topology of optical fibres containing a fibre Bragg grating (FBG) using an atomic force microscope (AFM). The AFM observation was made on FBGs fabricated via the phase mask technique in germanium–boron codoped optical fibres, in hydrogen-loaded germanium–boron codoped fibres and in standard telecommunications optical fibres. The surface images reveal that a spatial corrugation pattern was induced by the UV-irradiation, with a period that is half of the period of the phase mask. This UV-induced surface structure was found only on the side of the fibre facing towards the incident UV-irradiation and did not appear on the rear surface. The AFM probe scanned a 10×10 μm2 surface area at seven sites along the 6.0 mm length of fibre that was exposed to the UV-irradiation. The amplitude of the spatial corrugation pattern observed on the AFM image was quantified for each site. It was found that the amplitude in a range of 0.7–3.2 nm was a function of UV-laser intensity distribution and the type of fibre. Hydrogen loaded optical fibres exhibited a corrugation with an amplitude twice as large as that observed in the Ge–B doped fibres that were not hydrogen-loaded. This correlates with the increase in photosensitivity produced by the hydrogen loading. A similar UV-induced spatial corrugation was also observed on standard telecom fibres, but without inducing the refractive index change in the fibre core. The observation of surface topology provides an insight into the structural changes induced during FBG fabrication. UV-induced densification and laser ablation could account for the formation of the surface troughs.

[1]  K. Hill,et al.  Photosensitivity in optical fiber waveguides: Application to reflection filter fabrication , 1978 .

[2]  Qiang Zeng,et al.  Hydrogen speciation in hydrogen-loaded, germania-doped silica glass: a combined NMR and FTIR study of the effects of UV irradiation and heat treatment , 1999 .

[3]  P. J. Lemaire,et al.  Thermal stability analysis of UV-induced fiber Bragg gratings , 1997 .

[4]  Ralph P. Tatam,et al.  Fibre Bragg gratings fabricated using a wavelength tuneable laser source and a phase mask based interferometer , 1996 .

[5]  Hans G. Limberger,et al.  Compaction- and photoelastic-induced index changes in fiber Bragg gratings , 1996 .

[6]  Paul J. Lemaire,et al.  Reliability of optical fibers exposed to hydrogen: prediction of long-term loss increases , 1991 .

[7]  Pascal Bernage,et al.  TEM CHARACTERIZATION OF STRUCTURAL CHANGES IN GLASS ASSOCIATED TO BRAGG GRATING INSCRIPTION IN A GERMANOSILICATE OPTICAL FIBRE PREFORM , 1994 .

[8]  Ralph P. Tatam,et al.  The influence of hydrogen loading and the fabrication process on the mechanical strength of optical fibre Bragg gratings , 2002 .

[9]  H. N. Rourke,et al.  Thermal decay of fiber Bragg gratings written in boron and germanium codoped silica fiber , 1997 .

[10]  D. Hand,et al.  Photoinduced refractive-index changes in germanosilicate fibers. , 1990, Optics letters.

[11]  Bertrand Poumellec,et al.  Densification involved in the UV-based photosensitivity of silica glasses and optical fibers , 1997 .

[12]  Bertrand Poumellec,et al.  UV induced densification during Bragg grating inscription in Ge:SiO2 preforms , 1995 .

[13]  P. Lemaire,et al.  High pressure H/sub 2/ loading as a technique for achieving ultrahigh UV photosensitivity and thermal sensitivity in GeO/sub 2/ doped optical fibres , 1993 .