Fatigue and Shear Properties of Novel Lead-free Solder Joints with Low Melting Temperatures

The reliability of Sn–Ag–Cu (SAC)-based solder alloys has been extensively researched since the ban on lead in the electronics industry. Recently, solder alloys with the ability to reflow at lower temperatures have been gaining growing attention due to the reduced defects in complex assemblies. In this study, individual solder joints were tested using the Instron micromechanical testing system to investigate the shear and fatigue properties. Two new solder alloys (Sn–58Bi–0.5Sb–0.15Ni and Sn–42Bi–0.5Sb) with low melting temperatures were studied and compared to Sn–3.5Ag and Sn–3.0Ag–0.8Cu–3.0Bi. Electroless nickel immersion silver (ENIG) was the board surface finish for all solder alloys. Sn–3.5Ag solder alloy with an organic surface protection (OSP) surface finish was also tested for comparison. Three strain rates were selected for the shear tests. The shear strength of each solder alloy was measured. A constant strain rate was utilized for the cyclic fatigue tests. The fatigue life of each alloy at different stress amplitudes was measured. The results showed that Sn–3.0Ag–0.8Cu–3.0Bi demonstrated superior shear and fatigue properties but was more susceptible to brittle failure. For the Sn–3.5Ag solder alloy, the OSP surface provided better interfacial toughness than the ENIG surface finish.

[1]  Li-li Gao,et al.  Recent advances on SnBi low-temperature solder for electronic interconnections , 2021, Journal of Materials Science: Materials in Electronics.

[2]  P. Lall,et al.  Fatigue Performance of Aged SAC-Bi Solder Joint under Varying Stress Cycling , 2021, 2021 20th IEEE Intersociety Conference on Thermal and Thermomechanical Phenomena in Electronic Systems (iTherm).

[3]  P. Lall,et al.  Fatigue Performance of Ball Grid Array Components at Elevated Temperature , 2021, 2021 20th IEEE Intersociety Conference on Thermal and Thermomechanical Phenomena in Electronic Systems (iTherm).

[4]  Hyejun Kang,et al.  Ultrasonic-Assisted Dispersion of ZnO Nanoparticles to Sn-Bi Solder: A Study on Microstructure, Spreading, and Mechanical Properties , 2021, Journal of Materials Engineering and Performance.

[5]  S. Jung,et al.  Interfacial Reactions and Mechanical Properties of Sn–58Bi Solder Joints with Ag Nanoparticles Prepared Using Ultra-Fast Laser Bonding , 2021, Materials.

[6]  P. Lall,et al.  Effect of Varying Amplitude Cycling on SAC-Bi Solder Joint Fatigue , 2020, 2020 19th IEEE Intersociety Conference on Thermal and Thermomechanical Phenomena in Electronic Systems (ITherm).

[7]  Jianhao Wang,et al.  New challenges of miniaturization of electronic devices: Electromigration and thermomigration in lead-free solder joints , 2020 .

[8]  P. Lall,et al.  The Effect of Bi on the Mechanical Properties of Aged SAC Solder Joint , 2020, 2020 19th IEEE Intersociety Conference on Thermal and Thermomechanical Phenomena in Electronic Systems (ITherm).

[9]  P. Lall,et al.  Fatigue Performance of Doped SAC Solder Joints in BGA Assembly , 2020, 2020 19th IEEE Intersociety Conference on Thermal and Thermomechanical Phenomena in Electronic Systems (ITherm).

[10]  P. Lall,et al.  Investigation on the Mechanical Behavior Evolution Occurring in Lead Free Solder Joints Exposed to Thermal Cycling , 2020, 2020 IEEE 70th Electronic Components and Technology Conference (ECTC).

[11]  S. Hamasha,et al.  Effects of Surface Finish on the Shear Fatigue of SAC-Based Solder Alloys , 2020, IEEE Transactions on Components, Packaging and Manufacturing Technology.

[12]  P. Lall,et al.  Effect of Surface Finish on the Fatigue Behavior of Bi-based Solder Joints , 2019, 2019 18th IEEE Intersociety Conference on Thermal and Thermomechanical Phenomena in Electronic Systems (ITherm).

[13]  Yu Qiu,et al.  Shear strength and fracture surface analysis of Sn58Bi/Cu solder joints under a wide range of strain rates , 2018, Microelectron. Reliab..

[14]  S. Hamasha,et al.  Effect of Long-Term Room Temperature Aging on the Fatigue Properties of SnAgCu Solder Joint , 2018 .

[15]  S. Hamasha,et al.  Fatigue Properties of Lead-free Doped Solder Joints , 2018, 2018 17th IEEE Intersociety Conference on Thermal and Thermomechanical Phenomena in Electronic Systems (ITherm).

[16]  P. Borgesen,et al.  Effect of Cycling Amplitude Variations on SnAgCu Solder Joint Fatigue Life , 2018, IEEE Transactions on Components, Packaging and Manufacturing Technology.

[17]  Dongyang Li,et al.  The shear strength and fracture mode of Sn-xBi (x=0, 2.5, 5, 15)/Cu solder joints , 2017, 2017 18th International Conference on Electronic Packaging Technology (ICEPT).

[18]  Lu Fang,et al.  Review of board-level solder joint reliability under environmental stress , 2016, 2016 Prognostics and System Health Management Conference (PHM-Chengdu).

[19]  Peter Borgesen,et al.  Effects of Strain Rate and Amplitude Variations on Solder Joint Fatigue Life in Isothermal Cycling , 2016 .

[20]  Richard J. Coyle,et al.  Thermal Fatigue Evaluation of Pb-Free Solder Joints: Results, Lessons Learned, and Future Trends , 2015 .

[21]  Peter Borgesen,et al.  Solder joint reliability under realistic service conditions , 2013, Microelectron. Reliab..

[22]  Liu Yang,et al.  Shear strength and brittle failure of low-Ag SAC-Bi-Ni solder joints during ball shear test , 2013, International Conference on Electronic Packaging Technology.

[23]  Mingyu Li,et al.  Inhomogeneous deformation and microstructure evolution of Sn-Ag-based solder interconnects during thermal cycling and shear testing , 2012, Microelectron. Reliab..

[24]  Peter Borgesen,et al.  Recrystallization and Precipitate Coarsening in Pb-Free Solder Joints During Thermomechanical Fatigue , 2012, Journal of Electronic Materials.

[25]  Z. Zhang,et al.  Interfacial microstructure and mechanical properties of SnBi/Cu joints by alloying Cu substrate , 2012 .

[26]  Ganesh Subbarayan,et al.  Microstructural coarsening in Sn-Ag-based solders and its effects on mechanical properties , 2009 .

[27]  Xingke Zhao,et al.  Effect of thermal-shearing cycling on Ag3Sn microstructural coarsening in SnAgCu solder , 2009 .

[28]  Tai Chong Chai,et al.  The mechanics of the solder ball shear test and the effect of shear rate , 2006 .

[29]  Y. Miyashita,et al.  Influence of frequency on low cycle fatigue behavior of Pb-free solder 96.5Sn–3.5Ag , 2003 .

[30]  Katsuaki Suganuma,et al.  Effect of composition and cooling rate on microstructure and tensile properties of Sn–Zn–Bi alloys , 2003 .

[31]  Y. Miyashita,et al.  Fatigue crack growth behaviour of lead‐containing and lead‐free solders , 2002 .

[32]  Yoshiharu Mutoh,et al.  Low cycle fatigue and fatigue crack growth behaviour of Sn–Ag eutectic solder , 2002 .

[33]  Y. Miyashita,et al.  Low-cycle fatigue behavior of Sn-Ag, Sn-Ag-Cu, and Sn-Ag-Cu-Bi lead-free solders , 2002 .

[34]  F. Akkara,et al.  Reliability of New SAC-Bi Solder Alloys in Thermal Cycling with Aging , 2020 .

[35]  P. Lall,et al.  FATIGUE AND SHEAR PROPERTIES OF HIGH RELIABLE SOLDER JOINTS FOR HARSH APPLICATIONS , 2018 .