Formation of epitaxial cobalt silicide films on (1 0 0) Si using Co/Ti, Co/Nb, and Co/Hf bilayers

Abstract Formation of epitaxial cobalt silicide films on (1 0 0)Si using Co/Ti, Co/Hf, and Co/Nb bilayers has been investigated. The crystallographic orientations of the silicide films formed after annealing these metal bilayers on (1 0 0)Si at 800°C were found to depend strongly upon what thin metal layer was used as an epitaxy promoter. Perfect epitaxy of CoSi 2 was obtained using Co/Ti/(1 0 0)Si. Local epitaxy of CoSi 2 was obtained using Co/Hf/(1 0 0)Si, while epitaxy of CoSi 2 was not obtained for the Co/Nb/(1 0 0)Si system. Epitaxial growth of CoSi 2 in these Co/metal/Si systems seems to be related to the formation and decomposition of stable reaction barriers like Co–Ti–O and Hf–Si–O compounds at high temperatures. These stable reaction barriers formed at high temperatures make uniform diffusion of Co atoms possible, resulting in the growth of epitaxial CoSi 2 .