Microcrystalline silicon solar cells deposited at high rates

Hydrogenated microcrystalline silicon (μc-Si:H) thin-film solar cells were prepared at high rates by very high frequency plasma-enhanced chemical vapor deposition under high working pressure. The influence of deposition parameters on the deposition rate (RD) and the solar cell performance were comprehensively studied in this paper, as well as the structural, optical, and electrical properties of the resulting solar cells. Reactor-geometry adjustment was done to achieve a stable and homogeneous discharge under high pressure. Optimum solar cells are always found close to the transition from microcrystalline to amorphous growth, with a crystallinity of about 60%. At constant silane concentration, an increase in the discharge power did hardly increase the deposition rate, but did increase the crystallinity of the solar cells. This results in a shift of the μc-Si:H∕a-Si:H transition to higher silane concentration, and therefore leads to a higher RD for the optimum cells. On the other hand, an increase in the t...

[2]  G. H. Bauer,et al.  Analysis of high-rate a-Si:H deposition in a VHF plasma , 1993 .

[3]  Arvind Shah,et al.  Influences of a high excitation frequency (70 MHz) in the glow discharge technique on the process plasma and the properties of hydrogenated amorphous silicon , 1992 .

[4]  Y. Mai,et al.  Structure adjustment during high-deposition-rate growth of microcrystalline silicon solar cells , 2004 .

[5]  J. Müller,et al.  Microcrystalline silicon for large area thin film solar cells , 2003 .

[6]  S. Suzuki,et al.  Growth of device grade c-Si film at over 50 /s using PECVD , 2002 .

[7]  Reinhard Carius,et al.  Improvement of grain size and deposition rate of microcrystalline silicon by use of very high frequency glow discharge , 1994 .

[8]  O. Vetterl,et al.  Structural Properties of Microcrystalline Si Solar Cells , 2001 .

[9]  Chuang‐Chuang Tsai,et al.  Control of silicon network structure in plasma deposition , 1989 .

[10]  Hiroyuki Fujiwara,et al.  Fundamental aspects of low-temperature growth of microcrystalline silicon , 2003 .

[11]  Michael Grimm,et al.  Intrinsic microcrystalline silicon prepared by hot-wire chemical vapour deposition for thin film solar cells , 2003 .

[12]  H. Okamoto,et al.  Correlation between Microstructure and Photovoltaic Performance of Polycrystalline Silicon Thin Film Solar Cells , 2002 .

[13]  Diego Fischer,et al.  Microcrystalline silicon and micromorph tandem solar cells , 1999 .

[14]  J. Meier,et al.  High rate growth of microcrystalline silicon by VHF-GD at high pressure , 2003 .

[15]  A. Matsuda.  Formation kinetics and control of microcrystallite in μc-Si:H from glow discharge plasma , 1983 .

[16]  A. Howling,et al.  Frequency effects in silane plasmas for plasma enhanced chemical vapor deposition , 1992 .

[17]  B. Rech,et al.  Texture etched ZnO:Al coated glass substrates for silicon based thin film solar cells , 1999 .

[18]  Bernd Rech,et al.  Intrinsic microcrystalline silicon: A new material for photovoltaics , 2000 .

[19]  A. Matsuda,et al.  High Rate Deposition of Microcrystalline Silicon Using Conventional Plasma-Enhanced Chemical Vapor Deposition , 1998 .

[20]  H. Shirai,et al.  Role of Atomic Hydrogen During Growth of Hydrogenated Amorphous Silicon in the “Chemical Annealing” , 1991 .

[21]  J. Müller,et al.  Comprehensive study of microcrystalline silicon solar cells deposited at high rate using 13.56 MHz plasma-enhanced chemical vapor deposition , 2002 .

[22]  S. Vepřek.  Chemistry and Solid State Physics of Microcrystalline Silicon , 1989 .

[23]  F. Finger,et al.  Relationships between structure, spin density and electronic transport in ?solar-grade' microcrystalline silicon films , 2002 .

[24]  Susumu Suzuki,et al.  High rate growth of microcrystalline silicon using a high-pressure depletion method with VHF plasma , 2001 .

[25]  R. Schropp,et al.  Growth mechanism of microcrystalline silicon at high pressure conditions , 2004 .

[26]  S. M. Sze,et al.  Physics of semiconductor devices , 1969 .

[27]  M. Stutzmann,et al.  Microcrystalline Silicon Prepared by Hot-Wire Chemical Vapour Deposition for Thin Film Solar Cell Applications , 2002 .

[28]  E. Taglauer,et al.  Surface hydrogen content and passivation of silicon deposited by plasma induced chemical vapor deposition from silane and the implications for the reaction mechanism , 1989 .

[29]  Kenjiro Nakamura,et al.  Roles of Atomic Hydrogen in Chemical Annealing , 1995 .

[30]  A. Matsuda,et al.  High rate growth of microcrystalline silicon at low temperatures , 2000 .

[31]  B. Rech,et al.  Thickness dependence of microcrystalline silicon solar cell properties , 2001 .

[32]  A. Matsuda,et al.  Preparation of microcrystalline silicon films at ultra high-rate of 10 nm/s using high-density plasma , 2004 .