Microstructure and thermal stability of polypropylene/ bagasse composite foams: Design of optimum void fraction using response surface methodology

Wood–plastic composite foams (WPCFs), consisting of polypropylene and bagasse as wood fiber, were produced using tandem extrusion. The simultaneous effects of different material parameters including bagasse loading and particle size, melt viscosity of the used thermoplastic, type and content of chemical blowing agent on the microstructure, and physical properties of the obtained composite foams have been evaluated. Special sandwich morphology has been observed for these foams. Void fraction of WPCFs was measured and optimized using an experimental design method, response surface methodology. The maximum determined void fraction of the prepared WPCFs was 54%, which was obtained at the middle values of blowing agent content and bagasse particle size. Employing a mixture of endothermic–exothermic blowing agents has also caused the optimum amount of void fraction. Moreover, thermal behavior of wood– plastic composites was studied and the effects of all material parameters on decomposition behavior of polymer and bagasse fibers were investigated. The results verify that both bagasse content and bagasse particle size considerably influence the thermal stability of the microcomposites.

[1]  Farkhondeh Hemmati,et al.  A study on fire retardancy and durability performance of bagasse fiber/polypropylene composite for outdoor applications , 2013 .

[2]  S. M. B. Nachtigall,et al.  Effect of chemical and physical foaming additives on the properties of PP/wood flour composites , 2013 .

[3]  L. Famá,et al.  Tensile and fracture behaviour of PP/wood flour composites , 2012 .

[4]  Jin Kuk Kim,et al.  Effects of extruder parameters and silica on physico-mechanical and foaming properties of PP/wood-fiber composites , 2012 .

[5]  S. Lashgari,et al.  Improving the Interfacial Adhesion of Highly Filled PP—Bagasse Composites Designed by Taguchi Method , 2011 .

[6]  Yan Li,et al.  Interfacial studies of sisal fiber reinforced high density polyethylene (HDPE) composites , 2008 .

[7]  A. Błędzki,et al.  Influence of Processing Temperature on Microcellular Injection-Moulded Wood–Polypropylene Composites , 2006 .

[8]  Andrzej K. Bledzki,et al.  Injection moulded microcellular wood fibre-polypropylene composites , 2006 .

[9]  Rui Yang,et al.  Thermal oxidation products and kinetics of polyethylene composites , 2006 .

[10]  A. Błędzki,et al.  Effects of the chemical foaming agents, injection parameters, and melt‐flow index on the microstructure and mechanical properties of microcellular injection‐molded wood‐fiber/polypropylene composites , 2005 .

[11]  Chul B. Park,et al.  Development of an extrusion system for producing fine‐celled HDPE/wood‐fiber composite foams using CO2 as a blowing agent , 2004 .

[12]  L. Matuana,et al.  Foam extrusion of high density polyethylene/wood-flour composites using chemical foaming agents , 2003 .

[13]  S. Selke,et al.  Microcellular foam of polymer blends of HDPE/PP and their composites with wood fiber , 2003 .

[14]  A. Błędzki,et al.  Microcellular Wood Fibre Reinforced Polypropylene Composites in an Injection Moulding Process , 2002 .

[15]  J. Pawlicki,et al.  Wood-thermoplastic composites , 2000 .

[16]  Chul B. Park,et al.  Cell morphology and property relationships of microcellular foamed pvc/wood‐fiber composites , 1998 .

[17]  Chul B. Park,et al.  Processing and cell morphology relationships for microcellular foamed PVC/wood-fiber composites , 1997 .

[18]  C. Picard,et al.  Thermal degradation of sugar cane bagasse , 1988 .