Investigation on Blistering Behavior for n-type Silicon Solar Cells

Abstract Thermal treatment with different gas environment before the Al 2 O 3 ALD passivation process plays a key role to the presence of blistering. The specific silanol group vibration peaks in FT-IR spectra confirm the mechanism of the blistering free surface formation. The blistering affects not only the appearance but also the implied Voc of the cells, that is to say, the quality of the passivation [10]. The hydrogen containing species (by-product of the ALD process) will bond to the SiO 2 (both Si and O atom site) which grows after the thermal treatment with oxygen. Due to the good diffusivity within the SiO 2 layer, the amount of hydrogen out-diffusing towards the SiN X ARC layer after firing can be reduced to achieve blistering free silicon solar cells.

[1]  Jung‐Il Jin,et al.  Competition in low ordered smectics between incommensurate phases and two-dimensional modulated ones for dimesogenic compounds , 1998 .

[2]  Hydrogen diffusion as the rate-limiting mechanism of stress development in dielectric films , 2004 .

[3]  R. Mertens,et al.  Blistering in ALD Al2O3 passivation layers as rear contacting for local Al BSF Si solar cells , 2012 .

[4]  Paul F. McMillan,et al.  Hydroxyl sites in SiO2 glass: a note on infrared and Raman spectra , 1986 .

[5]  Ronald D. Schrimpf,et al.  Dual behavior of H+ at Si–SiO2 interfaces: Mobility versus trapping , 2002 .

[6]  F. Koch,et al.  Hydrogen permeation barrier performance characterization of vapor deposited amorphous aluminum oxide films using coloration of tungsten oxide , 2002 .

[7]  J. Pankove,et al.  Hydrogen in semiconductors , 1991 .

[8]  Pierre Morin,et al.  Hydrogen desorption and diffusion in PECVD silicon nitride. Application to passivation of CMOS active pixel sensors , 2007 .

[9]  Younes Messaddeq,et al.  Peak separation by derivative spectroscopy applied to ftir analysis of hydrolized silica , 2008 .

[10]  D. Pysch,et al.  Post-Deposition Thermal Treatment of Ultrafast Spatial ALD Al2O3 for the Rear Side Passivation of p-Type PERC Solar Cells , 2013 .

[11]  G. Vaccaro,et al.  Structural organization of silanol and silicon hydride groups in the amorphous silicon dioxide network , 2011 .

[12]  K. Nakamoto,et al.  Stretching Frequencies as a Function of Distances in Hydrogen Bonds , 1955 .

[13]  G. Walrafen,et al.  Infrared absorbance spectra and interactions involving OH groups in fused silica , 1978 .

[14]  S. George,et al.  Low-Temperature Al2O3 Atomic Layer Deposition , 2004 .