Micromachining of SrTiO3 steps for high-Tc step edge junction dc SQUIDs

In this paper, we establish a model of the micromachined SrTiO3 substrate steps for high-T-c direct-current (dc) superconducting quantum interference devices (SQUIDs). The step angle is determined by the local ion milling rate and re-deposition rate, which is caused by back sputtering of ion milling. At dynamic balance, the maximum possible step angle is predicted to be 75degrees with an ion beam incidence angle of 45degrees, which agrees well with the measured value of 71degrees. In order to obtain a better step sidewall profile, we consider the influences of Nb metal mask micromachining. To avoid a rounded angle at the step upper corner, the minimum thickness of the Nb mask should be 440 nm when the desired step height is 300 nm. At optimized process conditions, steps with sharp, steep angles, and flawless profiles have been fabricated. Nine of the twelve dc SQUIDs thus obtained exhibited resistively shunted junction current-voltage behavior and magnetic field modulation at 77 K.

[1]  K. Müller,et al.  Possible highTc superconductivity in the Ba−La−Cu−O system , 1986 .

[2]  M. Siegel,et al.  Correlation of YBa2Cu3O7 step‐edge junction characteristics with microstructure , 1995 .

[3]  D. Dimos,et al.  Orientation dependence of grain-boundary critical currents in YBa2Cu3O7- delta bicrystals. , 1988, Physical review letters.

[4]  Willi Zander,et al.  Microstructure of epitaxial YBa2Cu3O7 films on step-edge SrTiO3 substrates , 1991 .

[5]  C. Vittoria,et al.  Planar superconducting YBCO microwave mixer employing an engineered grain boundary weak link junction , 1994, IEEE Transactions on Applied Superconductivity.

[6]  G. Ovsyannikov,et al.  High-temperature superconducting bi-crystal Josephson junctions with asymmetric current biasing: the DC-SQUID configuration , 2002 .

[7]  Zhang Jia-Shu,et al.  Predicting Hyper-Chaotic Time Series Using Adaptive Higher-Order Nonlinear Filter , 2001 .

[8]  Jian Zhang,et al.  Practical high Tc Josephson junctions and dc SQUIDs operating above 85 K , 1991 .

[9]  C. Jia,et al.  The microstructure of epitaxial YBa2Cu3O7 films on steep steps in LaAlO3 substrates , 1992 .

[10]  K. A. Müller,et al.  Possible High T cSuperconductivity in the Ba — La — Cu — O System , 1993 .

[11]  Nathan Newman,et al.  Bi‐epitaxial grain boundary junctions in YBa2Cu3O7 , 1991 .

[12]  Wang Jing,et al.  Analysis of step etching on SrTiO3 substrates for the step-edge YBCO Josephson junctions , 2001 .

[13]  J. Burch,et al.  Substrate step‐edge YBa2Cu3O7 rf SQUIDs , 1991 .

[14]  W. Gallagher,et al.  Improved process for high‐Tc superconducting step‐edge junctions , 1993 .