The effect of oxidation pre-treatment on the cyclic life of EB-PVD thermal barrier coatings with platinum-aluminide bond coats

[1]  M. Lance,et al.  As-deposited mixed zone in thermally grown oxide beneath a thermal barrier coating , 2001 .

[2]  D. Clarke,et al.  Microstructural study of the theta-alpha transformation in alumina scales formed on nickel-aluminides , 2000 .

[3]  K. Stiller,et al.  Microstructure of oxide scales on aluminide diffusion coatings after short time oxidation at 1050 °C , 2004 .

[4]  D. Clarke,et al.  Evaluation of interface degradation during cyclic oxidation of EB-PVD thermal barrier coatings and correlation with TGO luminescence , 2004 .

[5]  D. Clarke,et al.  Effect of Yttrium and Erbium Ions on Epitaxial Phase Transformations in Alumina , 2003 .

[6]  D. Clarke,et al.  Oxidation-induced failure of EB-PVD thermal barrier coatings , 2001 .

[7]  Woo Y. Lee,et al.  Synthesis and cyclic oxidation behavior of a (Ni, Pt) Al coating on a desulfurized Ni-base superalloy , 1999 .

[8]  E. Jordan,et al.  Mechanism of spallation in platinum aluminide/electron beam physical vapor-deposited thermal barrier coatings , 1999 .

[9]  L. Giannuzzi,et al.  Phase transformations of thermally grown oxide on (Ni,Pt)Al bondcoat during electron beam physical vapor deposition and subsequent oxidation , 2003 .

[10]  E. Jordan,et al.  The effect of bond coat grit blasting on the durability and thermally grown oxide stress in an electron beam physical vapor deposited thermal barrier coating , 2003 .

[11]  David R. Clarke,et al.  Nondestructive evaluation of the oxidation stresses through thermal barrier coatings using Cr3+ piezospectroscopy , 1996 .

[12]  D. Clarke,et al.  The effect of grit blasting on the oxidation behavior of a platinum-modified nickel-aluminide coating , 2001 .

[13]  Anthony G. Evans,et al.  Mechanisms controlling the durability of thermal barrier coatings , 2001 .

[14]  E. Jordan,et al.  Surface geometry and strain energy effects in the failure of a (Ni, Pt)Al/EB-PVD thermal barrier coating , 2004 .

[15]  Jong‐Lam Lee,et al.  Structural and Chemical Analyses of a Thermally Grown Oxide Scale in Thermal Barrier Coatings Containing a Platinum–Nickel–Aluminide Bondcoat , 2000 .

[16]  Brace M. Warnes,et al.  Clean diffusion coatings by chemical vapor deposition , 1997 .