(Pr, Ho)-Fe-B magnets for low-temperature applications

We have investigated the effect of HoH2 hydride addition on the hysteresis loop parameters of sintered Pr-Fe-Ti-Al-Cu-B magnets. The magnets were prepared by traditional powder metallurgy technology, and 3 wt.% HoH2 was added to the powder at the fine-milling stage. The magnets exhibited a monotonic increase in all hysteretic parameters with decreasing temperature down to 4.2 K. The coercive force and maximum energy product at 295 K (4.2 K) were 1344 (5402) kA/m and 221 (336) kJ/m3, respectively. The structure of the magnets was studied in detail by scanning electron microscopy and energy dispersive X-ray spectroscopy, which demonstrated the formation of the so-called “core-shell” structure, which is assumed to favor the marked improvement in the hysteretic properties of the samples analyzed. The surface domain structure was measured in the directions perpendicular and parallel to the magnet texture using magnetic force microscopy. The data obtained indicated fine labyrinth-like and strip domain patterns in the directions perpendicular and parallel to the magnet texture, with an average domain width of 1.2–1.8 µm.We have investigated the effect of HoH2 hydride addition on the hysteresis loop parameters of sintered Pr-Fe-Ti-Al-Cu-B magnets. The magnets were prepared by traditional powder metallurgy technology, and 3 wt.% HoH2 was added to the powder at the fine-milling stage. The magnets exhibited a monotonic increase in all hysteretic parameters with decreasing temperature down to 4.2 K. The coercive force and maximum energy product at 295 K (4.2 K) were 1344 (5402) kA/m and 221 (336) kJ/m3, respectively. The structure of the magnets was studied in detail by scanning electron microscopy and energy dispersive X-ray spectroscopy, which demonstrated the formation of the so-called “core-shell” structure, which is assumed to favor the marked improvement in the hysteretic properties of the samples analyzed. The surface domain structure was measured in the directions perpendicular and parallel to the magnet texture using magnetic force microscopy. The data obtained indicated fine labyrinth-like and strip domain patterns ...

[1]  A. A. Lukin,et al.  Influence of heat treatment on the structural and magnetic characteristics of (Nd x Pr 1-x ) 2 Fe 14 B-based magnetic material for low-temperature application , 2016 .

[2]  Xiaolian Liu,et al.  Coercivity enhancement of Dy-free Nd–Fe–B sintered magnets by intergranular adding Ho63.4Fe36.6 alloy , 2016 .

[3]  G. Burkhanov,et al.  Role of terbium hydride additions in the formation of microstructure and magnetic properties of sintered Nd-Pr-Dy-Fe-B magnets , 2013, Inorganic Materials: Applied Research.

[4]  R. Nagaoka,et al.  Development of a 2 m Pr2Fe14B Cryogenic Permanent Magnet Undulator at SOLEIL , 2013 .

[5]  J. Liu,et al.  The partitioning of La and Y in Nd–Fe–B magnets: A first-principles study , 2013 .

[6]  Shuai Guo,et al.  The mechanism of enhanced magnetic properties of sintered permanent magnets by substitution of Pr for Nd , 2012 .

[7]  Z. Altounian,et al.  The partitioning of Dy and Tb in NdFeB magnets: A first-principles study , 2012 .

[8]  Y. B. Kim,et al.  Spin reorientation and magnetocrystalline anisotropy of (Nd1-xPrx)2Fe14B , 1999 .

[9]  Armstrong,et al.  Compton scattering studies of the temperature dependence of the spin moment in HoFe2. , 1993, Physical review letters.

[10]  C. Rillo,et al.  Structural and magnetic study of Ho2Fe14BHx (x = 0–3.1) , 1991 .

[11]  Wen-Sheng Chang,et al.  Hydrogen induced radial anisotropic R‐Fe‐B magnet (R=Pr,Dy) , 1991 .

[12]  Satoshi Hirosawa,et al.  Magnetization and magnetic anisotropy of R2Fe14B measured on single crystals , 1986 .

[13]  W. Wallace,et al.  Differences in the low temperature magnetic anisotropy of Nd2Fe14B and Pr2Fe14B interpreted on a crystal field model , 1985 .

[14]  K. Buschow New Permanent-Magnet Materials , 1986, Nature.