Investigation on optimal detection position of DC electromagnetic NDT in crack characterization for high-speed rail track

Due to the long-term harsh working environment and cyclic loadings, Rolling Contact Fatigue (RCF) crack will occur on the tread of the rail. Therefore, a fast quantitative detection of cracks periodically is essential to guarantee the operation safety of the high-speed rail track. Electromagnetic Nondestructive testing (NDT) technique is one of the effective methods for quantitative crack characterization in conduction metals. For high-speed Electromagnetic NDT, because of the relative motion between the rail and detection device, motion induced eddy current (MIEC) is generated in the surface of the rail, which causes the magnetic field distribution inside the rail more complicated due to the dragging effect, and the literatures focus on the investigation on the optimal detection position is rare. Hence, to obtain the optimal detection sensitivity and strength, it is essential to investigate the optimal detection position in electromagnetic NDT for crack characterization in high speed. This paper perform a deep investigation on the optimal detection position in direct current (DC) electromagnetic NDT by numerical simulation, and the influence of detecting position on the detecting signal at different speeds is investigated. The results show that the DC Electromagnetic NDT can be used for quantitative crack depth characterization, and the optimal detection position with strongest detection signal and high sensitivity for crack depth characterization is located near the inner edge of the excitation coil on the opposite side of the direction of the probe motion. According to the findings in this paper, the high-speed DC electromagnetic NDT method can be applied to other moving metal components crack characterization, such as rotating metal components and pipelines.

[1]  Klaus Hempelmann,et al.  A new type of RCF, experimental investigations and theoretical modelling , 2002 .

[2]  Gao Yun.  Velocity Effect Analysis of Dynamic Magnetization in High Speed Detection for Rail Crack Using MFL Method , 2013 .

[3]  Kevin Koch,et al.  Rail base corrosion problem for North American transit systems , 2009 .

[4]  G. Tian,et al.  Velocity effect analysis of dynamic magnetization in high speed magnetic flux leakage inspection , 2014 .

[5]  Javier Ignacio Etcheverry,et al.  Magnetic flux leakage: Experimental and numerical study of the influence of induced currents , 2013 .

[6]  Y. Shin.  Numerical prediction of operating conditions for magnetic flux leakage inspection of moving steel sheets , 1997 .

[7]  Uwe Zerbst,et al.  Introduction to the damage tolerance behaviour of railway rails – a review , 2009 .

[8]  Tsutomu Yamada,et al.  Detection of Damage and Crack in Railhead by Using Eddy Current Testing , 2011 .

[9]  Stuart L. Grassie,et al.  Rolling contact fatigue on the British railway system: treatment , 2005 .

[10]  Clive Roberts,et al.  High-speed inspection of rails using ACFM techniques , 2009 .

[11]  Guan Jia,et al.  Investigation of signal features of pulsed eddy current testing technique by experiments , 2013 .

[12]  Elena Kabo,et al.  Material defects in rolling contact fatigue — influence of overloads and defect clusters , 2002 .

[13]  Yunze He,et al.  Pulsed eddy current technique for defect detection in aircraft riveted structures , 2010 .

[14]  W. Zhong,et al.  Experimental investigation between rolling contact fatigue and wear of high-speed and heavy-haul railway and selection of rail material , 2011 .

[15]  Gui Yun Tian,et al.  Review of railway rail defect non-destructive testing and monitoring , 2016 .

[16]  Yu Zhou.  Prediction of the Rail Head Checks Propagation Based on Three Dimensional Reconstruction , 2018 .