An atomistic study of brittle fracture: Toward explicit failure criteria from atomistic modeling

Atomistic techniques are used to study brittle fracture under opening mode and mixed mode loading conditions. The influence of the discreteness of the lattice and of the lattice-trapping effect on crack propagation is studied using an embedded atom potential for nickel to describe the crack tip. The recently developed FEAt (Finite Element-Atomistic) coupling scheme provides the atomistic core region with realistic boundary conditions. Several crystallographically distinct crack-tip configurations are studied and commonly reveal that brittle cracks under general mixed mode loading situations follow an energy criterion (G-criterion) rather than an opening-stress criterion (Kl-criterion). However, if there are two competing failure modes, they seem to unload each other, which leads to an increase in lattice trapping. Blunted crack tips are studied in the last part of the paper and are compared to the atomically sharp cracks. Depending on the shape of the blunted crack tip, the observed failure modes differ significantly and can drastically disagree with what one would anticipate from a continuum mechanical analysis.

[1]  G. Beltz,et al.  Dislocation nucleation from a crack tip: A formulation based on anisotropic elasticity , 1994 .

[2]  P. Anderson,et al.  Lattice and continuum predictions of crack‐tip stability , 1994 .

[3]  Brodbeck,et al.  Instability dynamics of fracture: A computer simulation investigation. , 1994, Physical review letters.

[4]  Zhou,et al.  Crack blunting effects on dislocation emission from cracks. , 1994, Physical review letters.

[5]  John R. Rice,et al.  The activation energy for dislocation nucleation at a crack , 1994 .

[6]  B. Lawn.  Fracture of Brittle Solids by Brian Lawn , 1993 .

[7]  Zhou,et al.  Dislocation nucleation and crack stability: Lattice Green's-function treatment of cracks in a model hexagonal lattice. , 1993, Physical review. B, Condensed matter.

[8]  Murray S. Daw,et al.  The embedded-atom method: a review of theory and applications , 1993 .

[9]  Zhou,et al.  Lattice imperfections studied by use of lattice Green's functions. , 1992, Physical review. B, Condensed matter.

[10]  James R. Rice,et al.  Dislocation Nucleation from a Crack Tip" an Analysis Based on the Peierls Concept , 1991 .

[11]  M. Daw,et al.  Some aspects of forces and fields in atomic models of crack tips , 1991 .

[12]  H. Fischmeister,et al.  Crack propagation in b.c.c. crystals studied with a combined finite-element and atomistic model , 1991 .

[13]  P. Gumbsch,et al.  A quantum mechanical calculation of the theoretical strength of metals , 1991 .

[14]  A. Argon,et al.  Activation analysis of dislocation nucleation from crack tip in α-Fe , 1991 .

[15]  G. Schoeck.  Dislocation emission from crack tips , 1991 .

[16]  Cheung,et al.  Brittle-ductile transition in intrinsic fracture behavior of crystals. , 1990, Physical Review Letters.

[17]  Foiles,et al.  Embedded-atom-method functions for the fcc metals Cu, Ag, Au, Ni, Pd, Pt, and their alloys. , 1986, Physical review. B, Condensed matter.

[18]  G. Dienes,et al.  Effect of atomic crack tip geometry on local stresses , 1985 .

[19]  M. Mullins.  Atomic simulation of cracks under mixed mode loading , 1984 .

[20]  M. Finnis,et al.  Crack-Tip Blunting Versus Cleavage Extension , 1983 .

[21]  M. A. Dokainish,et al.  Simulation of the (001) plane crack in α-iron employing a new boundary scheme , 1982 .

[22]  J. E. Sinclair.  The influence of the interatomic force law and of kinks on the propagation of brittle cracks , 1975 .

[23]  B. Lawn,et al.  An atomistic study of cracks in diamond-structure crystals , 1972, Proceedings of the Royal Society of London. A. Mathematical and Physical Sciences.

[24]  Robb Thomson,et al.  Lattice Trapping of Fracture Cracks , 1971 .

[25]  R. Latanision,et al.  Atomistics of fracture , 1970 .

[26]  E. Kröner,et al.  Elasticity theory of materials with long range cohesive forces , 1967 .