Electrochemical oxidation of highly oriented pyrolytic graphite during potential cycling in sulfuric acid solution

Abstract Oxidation of highly oriented pyrolytic graphite (HOPG) under potential cycling conditions is investigated to understand the stability of graphite used in polymer electrolyte fuel cells (PEFCs) under their dynamic operation conditions. Electrochemical methods, AFM and XPS are applied to examine the surface oxidation of HOPG. The current peaks corresponding to quinone–hydroquinone redox reaction begin to appear on cyclic voltammograms after potential cycling between 0.6 V and 0.8 V vs. SHE (standard hydrogen electrode), indicating that the surface of HOPG is partially oxidized to form surface functional groups containing oxygen, whereas HOPG is relatively stable during potential cycling between 0.4 V and 0.6 V. An increase in potential range to 0.8–1.0 V extends the oxidation and forms pits on the surface of HOPG that is caused by the loss of surface carbon through the oxidation to gaseous products. The high rate of potential cycling accelerates the surface oxidation of HOPG.

[1]  C. Pittman,et al.  Surface characterization of carbon fibers using angle-resolved XPS and ISS , 1995 .

[2]  Minoru Inaba,et al.  Gas crossover and membrane degradation in polymer electrolyte fuel cells , 2006 .

[3]  Hubert A. Gasteiger,et al.  Instability of Pt ∕ C Electrocatalysts in Proton Exchange Membrane Fuel Cells A Mechanistic Investigation , 2005 .

[4]  K. Ota,et al.  Consumption Rate of Pt under Potential Cycling , 2007 .

[5]  Karren L. More,et al.  Microstructural Changes of Membrane Electrode Assemblies during PEFC Durability Testing at High Humidity Conditions , 2005 .

[6]  L. Pino,et al.  Relationship between physicochemical properties and electrooxidation behaviour of carbon materials , 1991 .

[7]  J. Tascón,et al.  Comparative study of the air and oxygen plasma oxidation of highly oriented pyrolytic graphite: a scanning tunneling and atomic force microscopy investigation , 2000 .

[8]  Rodney L. Borup,et al.  Durability of PEFCs at High Humidity Conditions , 2005 .

[9]  T. Abe,et al.  Mechanism for Electrochemical Oxidation of Highly Oriented Pyrolytic Graphite in Sulfuric Acid Solution , 2007 .

[10]  J. Willsau,et al.  The influence of Pt-activation on the corrosion of carbon in gas diffusion electrodes. A DEMS study , 1984 .

[11]  T. Abe,et al.  Stability of Pt-Catalyzed Highly Oriented Pyrolytic Graphite Against Hydrogen Peroxide in Acid Solution , 2006 .

[12]  Belabbes Merzougui,et al.  Rotating Disk Electrode Investigations of Fuel Cell Catalyst Degradation Due to Potential Cycling in Acid Electrolyte , 2006 .

[13]  J.A.S. Bett,et al.  Electrochemical oxidation of carbon black in concentrated phosphoric acid at 135°C , 1973 .

[14]  M. R. Tarasevich,et al.  Redox reactions of quinones on carbon materials , 1987 .

[15]  T. Jarvi,et al.  Characterization of Vulcan Electrochemically Oxidized under Simulated PEM Fuel Cell Conditions , 2004 .

[16]  H. Boehm.,et al.  Some aspects of the surface chemistry of carbon blacks and other carbons , 1994 .

[17]  T. Jarvi,et al.  Electrocatalytic corrosion of carbon support in PEMFC cathodes , 2004 .

[18]  G. W. Graham,et al.  Influence of Cyclic Operation on PEM Fuel Cell Catalyst Stability , 2007 .

[19]  David L. Wood,et al.  PEM fuel cell electrocatalyst durability measurements , 2006 .

[20]  Michael P. Balogh,et al.  Investigation of thermal and electrochemical degradation of fuel cell catalysts , 2006 .