Local environment under simulated disbonded coating on steel pipelines in soil solution

Abstract Taking advantage of microelectrode technique, the local potential and pH in a crevice simulating disbonded coating on X70 pipeline steel were investigated as a function of cathodic protection (CP) in a near neutral pH soil bulk solution bubbled with 5% CO2/N2 gas. The experimental potential–pH (E–pH) diagrams were established for the steel in the crevice. Stress corrosion cracking (SCC) susceptibility of the steel in the local environment in the crevice was analyzed based on the experimental E–pH diagrams. The results showed that the local steel potential in the deep of the crevice was independent on CP potential applied at the opening. Due to the effect of the atmospheric CO2, a near-neutral pH local environment promoting near-neutral pH SCC (also known as transgranular SCC, TGSCC) might be harbored in the crevice even with normal CP at the opening. During CP interruption, the steel potential decay and CO2 absorption (pH decrease) might shift E–pH points into a susceptibility region of near-neutral pH SCC.

[1]  E. A. Charles,et al.  Generation of Stress Corrosion Cracking Environments at Pipeline Surfaces , 1995 .

[2]  J. Pikas.  Case Histories of External Microbiologically Influenced Corrosion Underneath Disbonded Coatings , 1996 .

[3]  Jingli Luo,et al.  Effect of Cathodic Potential on Hydrogen Content in a Pipeline Steel Exposed to NS4 Near-Neutral pH Soil Solution , 2004 .

[4]  R. N. Parkins,et al.  Stress Corrosion Cracking Characteristics of a Range of Pipeline Steels in Carbonate-Bicarbonate Solution ✫ , 1993 .

[5]  R. N. Parkins,et al.  Transgranular Stress Corrosion Cracking of High-Pressure Pipelines in Contact with Solutions of Near Neutral pH , 1994 .

[7]  D. Chin,et al.  Cathodic protection to mitigate external corrosion of underground steel pipe beneath disbonded coating , 1994 .

[8]  R. N. Parkins,et al.  Cathodic Protection Levels under Disbonded Coatings , 1983 .

[9]  R. N. Parkins,et al.  A Review of Stress Corrosion Cracking of High Pressure Gas Pipelines , 2000 .

[10]  G. Burstein,et al.  Reactions of pipeline steels in carbon dioxide solutions , 1999 .

[11]  E. Han,et al.  Electrochemical measurements using combination microelectrode in crevice simulating disbonded of pipeline coatings under cathodic protection , 2007 .

[12]  N. Sridhar,et al.  Application of a General Reactive Transport Model to Predict Environment Under Disbonded Coatings , 2001 .

[13]  P. Lichtner,et al.  Evolution of Environment Under Disbonded Coating on Cathodically Protected Pipeline - Preliminary Modeling and Experimental Studies , 1998 .

[14]  X. Mao,et al.  A study on cathodic protection against crevice corrosion in dilute NaCl solutions , 2002 .