Effect of cold‐work on the mechanism controlling the high‐temperature creep in Al−2 wt% Mg

The role of alloying and the associated mutual interaction of solute atoms with dislocations on the stress and temperature dependences of the steady-state creep rate is investigated for Al−2 wt% Mg. The high temperature steady state creep rate is measured for the annealed and pre-coldworked alloy under stresses up to 17 kg mm−2. The stress sensitivity paremeter, m′, is calculated and amounted to about three for both cold-worked and annealed samples. It is found, for temperatures less than 300 °C, that m′ is independent of the applied stress. The dependence of the apparent activation energy on stress shows that at relatively low stresses creep is controlled by selfdiffusion of Mg and at applied stresses higher than 15 kg mm2 most probably by cross slipping. Pre-cold-working the sample seemed to be ineffective on the mechanism controlling creep rate. Fur Al−2Gew% Mg wird der Einflus der Legierung und der damit verknupften gegenseitigen Wechselwirkung der gelosten Atome mit Versetzungen auf die Spannungs- und Temperaturabhangigkeiten der stationaren Kriechrate untersucht. Die stationare Hochtemperaturkriechrate wird fur getemperte und kalt vorbehandelte Legierungen unter Spannungen bis zu 17 kg mm−2 gemessen. Der Spannungsempfindlichkeitsparameter m′ wird berechnet und betragt etwa drei sowohl fur kaltbehandelte als auch fur getemperte Proben. Es wird fur Temperaturen unterhalb 300 °C gefunden, das m′ unabhangig von der angelegten Spannung ist. Die Abhangigkeit der auftretenden Aktivierungsenergie von der Spannung zeigt, das bei relativ niedriger Spannung das Kriechen durch Selbstdiffusion von Mg und bei hoheren Spannungen als 15 kg mm2, hochstwahrscheinlich durch Kreuzgleitung gesteuert wird. Eine Kaltvorbehandlung der Proben scheint nicht auf den Steuerungsmechanismus der Kriechrate wirksam zu sein.