Bendable thin-film transistors based on sol–gel derived amorphous Ga-doped In2O3 semiconductors

Abstract Bendable thin-film transistors (TFTs) are demonstrated based on sol–gel-derived amorphous Ga-doped In2O3 (GIO) that can be thermally converted into a device-quality semiconducting layer at 300 °C, which is compatible with a plastic polyimide (PI) substrate. The device performance of the GIO TFTs is studied through the investigation on the electrical parameters (including mobility, threshold voltage, off-current, and subthreshold swing) of the devices as a function of Ga composition. With increasing Ga composition up to 36 mol%, the mobility decreases from 1.4 to 0.08 cm2 V s−1 with sluggish reduction in the Ga compositional range between 0 and 12 mol%, and the threshold voltage shifts from −21.6 to 13.5 V. Both the off-current and subthreshold swing decreases with a dramatic variation at Ga composition of 12 mol%. From the overall analysis, it is concluded that the incorporation of 12 mol% Ga enables for the GIO semiconducting layer with the best electrical performance. In addition, the bending characteristics of GIO TFTs, prepared on a SiO2/ITO/PI substrate, are analyzed with device performance variations depending on the bending radius. It is demonstrated that the device performance is maintained with acceptable electrical characteristics under a bending radius of 10 mm.

[1]  Sunho Jeong,et al.  Organic-inorganic hybrid dielectrics with low leakage current for organic thin-film transistors , 2006 .

[2]  Jooho Moon,et al.  Fully Flexible Solution‐Deposited ZnO Thin‐Film Transistors , 2010, Advanced materials.

[3]  P. K. Nayak,et al.  Effects of Li doping on the performance and environmental stability of solution processed ZnO thin film transistors , 2009 .

[4]  Doo-Hyoung Lee,et al.  Inkjet printed high-mobility indium zinc tin oxide thin film transistors , 2009 .

[5]  Richard H. Friend,et al.  General observation of n-type field-effect behaviour in organic semiconductors , 2005, Nature.

[6]  D. Keszler,et al.  Aqueous inorganic inks for low-temperature fabrication of ZnO TFTs. , 2008, Journal of the American Chemical Society.

[7]  J. Wager,et al.  Transparent Electronics , 2003, Science.

[8]  M. Kanatzidis,et al.  High-performance solution-processed amorphous zinc-indium-tin oxide thin-film transistors. , 2010, Journal of the American Chemical Society.

[9]  A. Facchetti,et al.  Role of Gallium Doping in Dramatically Lowering Amorphous‐Oxide Processing Temperatures for Solution‐Derived Indium Zinc Oxide Thin‐Film Transistors , 2010, Advances in Materials.

[10]  Sunho Jeong,et al.  Solution-Processed Zinc Tin Oxide Semiconductor for Thin-Film Transistors , 2008 .

[11]  Young-Min Choi,et al.  Chemically improved high performance printed indium gallium zinc oxide thin-film transistors , 2011 .

[12]  M. Kanatzidis,et al.  Low-temperature fabrication of high-performance metal oxide thin-film electronics via combustion processing. , 2011, Nature materials.

[13]  Sunho Jeong,et al.  Low-temperature, solution-processed metal oxide thin film transistors , 2012 .

[14]  Chih-hung Chang,et al.  Low-temperature, high-performance, solution-processed indium oxide thin-film transistors. , 2011, Journal of the American Chemical Society.

[15]  Sunho Jeong,et al.  Bias stress stable aqueous solution derived Y-doped ZnO thin film transistors , 2011 .

[16]  Young-Min Choi,et al.  Impact of Metal Salt Precursor on Low-Temperature Annealed Solution-Derived Ga-doped In2O3 Semiconductor for Thin-Film Transistors , 2011 .