Material characterization and residual stresses simulation during the manufacturing process of epoxy matrix composites

A thermal, rheological and mechanical material characterization of an aeronautic epoxy resin from commercial prepreg is reported in this article. The kinetic of the crosslinking reaction of the resin is characterized and modeled. The specific heat, the glass transition temperature, the thermal expansion coefficients, the chemical shrinkage coefficients and the thermo-mechanical properties have been investigated as a function of temperature and degree of cure. Dynamic mechanical measurements are used to determine the gel point. Finally, the residual stresses developed during the curing process are calculated using a finite element simulation, taking into account the material properties evolutions according to proposed models. The results highlight the importance of the characterization accuracy and the associated models.

[1]  John W. Gillespie,et al.  Process-Induced Stress and Deformation in Thick-Section Thermoset Composite Laminates , 1992 .

[2]  D. Kim,et al.  Rubber modified epoxy resin. I: Cure kinetics and chemorheology , 1994 .

[3]  Scott R. White,et al.  PROCESS-INDUCED RESIDUAL STRESS ANALYSIS OF AS4/3501-6 COMPOSITE MATERIAL , 1998 .

[4]  M. S. Kiasat,et al.  The effect of the addition of a low profile additive on the curing shrinkage of an unsaturated polyester resin , 1999 .

[5]  François Trochu,et al.  Numerical analysis of cure temperature and internal stresses in thin and thick RTM parts , 2005 .

[6]  J. Gillespie,et al.  Process induced stress for woven fabric thick section composite structures , 2000 .

[7]  S. Redner,et al.  Introduction To Percolation Theory , 2018 .

[8]  D. N. Fenner,et al.  Matrix crack propagation criteria for model short-carbon fibre/epoxy composites , 2000 .

[9]  A. Gawdzik,et al.  Basic kinetic model for the reaction yielding linear polyurethanes. II , 1995 .

[10]  Gary W. Poehlein,et al.  A kinetic model for curing reactions of epoxides with amines , 1987 .

[11]  L. J. Lee,et al.  Development of a dilatometer and its application to low-shrink unsaturated polyester resins , 1992 .

[12]  Reza Vaziri,et al.  Finite element based prediction of process-induced deformation of autoclaved composite structures using 2D process analysis and 3D structural analysis , 2003 .

[13]  J. Holmberg,et al.  Prediction of shape distortions Part I. FE-implementation of a path dependent constitutive model , 2004 .

[14]  R. R. Hill,et al.  Numerical simulation of non‐isothermal SMC (sheet molding compound) molding , 1993 .

[15]  H. Winter.  Can the gel point of a cross-linking polymer be detected by the G′ – G″ crossover? , 1987 .

[16]  D. Delaunay,et al.  Behaviour of a moulded composite part: Modelling of dilatometric curve (constant pressure) or pressure (constant volume) with temperature and conversion degree gradients , 2007 .

[17]  J. M. Salla,et al.  Effect of the initiator content and temperature on the curing of an unsaturated polyester resin , 1999 .

[18]  R. Bruce Prime,et al.  Differential scanning calorimetry of the epoxy cure reaction , 1973 .

[19]  Yan-Jyi Huang,et al.  Volume shrinkage characteristics in the cure of low-shrink unsaturated polyester resins , 1996 .

[20]  H. Thomas Hahn,et al.  Residual Stresses in Polymer Matrix Composite Laminates , 1976 .

[21]  A thermodynamically consistent, nonlinear viscoelastic approach for modeling thermosets during cure , 2007 .

[22]  Nuri Ersoy,et al.  Mechanisms generating residual stresses and distortion during manufacture of polymer-matrix composite structures , 2006 .

[23]  Musa R. Kamal,et al.  Kinetics and thermal characterization of thermoset cure , 1973 .

[24]  Three-Dimensional Curing Stresses in Symmetric Cross-Ply Laminates with Temperature-Dependent Properties , 1983 .

[25]  M. Vayer,et al.  Analysis and modeling of PVTX diagram of an unsaturated polyester resin, thermoplastic additive, and mineral fillers blend , 2003 .