Novel Method to Manufacture Porous Hydroxyapatite by Dual‐Phase Mixing

We have developed a novel method to construct porous hydroxyapatite (HA) by dual-phase mixing—in other words, generating a porous ceramic body and pore-forming template simultaneously. The technique is based on mixing two immiscible phases: HA slurry and polymethylmethacrylate (PMMA) resin. Naphthalene particles are necessary when greater porosity (>50%) is wanted. After shaping in a mold, the mixture is subjected to polymerization, drying, pyrolysis, and sintering. The porous HA has been thoroughly characterized with Fourier transformation infrared spectrometry, X-ray diffractometry, environmental scanning electron microscopy coupled with energy-dispersive X-ray analysis, and image analysis. The demanding specifications for bone ingrowth are met: (i) the size of pores and their fenestrations are adjustable, ∼80% within 300–800 μm; (ii) uniform and isotropic porous structure is observed in three directions; (iii) pores are fully interconnected throughout; (iv) the porosity is adjustable up to 60%; and (v) sufficient mechanical strength is present for cell culture and implantation handling. The porous HA can be applied as either implant material or scaffold for bone-tissue engineering.

[1]  P. Layrolle,et al.  Bioceramic Scaffold with Controlled Porous Structure for Bone Tissue Engineering , 2001 .

[2]  M. Descamps,et al.  Macroporous Calcium Phosphate Ceramics: Optimization of the Porous Structure and its Effect on the Bone Ingrowth in a Sheep Model , 2000 .

[3]  R. Martinetti,et al.  Porous Hydroxyapatite Cell Carrier for Tissue Engineering , 2000 .

[4]  J. Binner,et al.  Production of porous hydroxyapatite by the gel-casting of foams and cytotoxic evaluation. , 2000, Journal of biomedical materials research.

[5]  L. Vanasupa,et al.  A Review of Innovations in MSE Education: From Wulff to Web , 2000 .

[6]  W. Bonfield,et al.  Characterization of porous hydroxyapatite , 1999, Journal of materials science. Materials in medicine.

[7]  A. Carr,et al.  A synthetic bone implant macroscopically identical to cancellous bone. , 1998, Biomaterials.

[8]  John W. Halloran,et al.  Stereolithography of ceramic suspensions , 1997 .

[9]  V. M. Castano,et al.  Synthesis and processing of hydroxyapatite ceramic tapes with controlled porosity , 1995 .

[10]  K Ono,et al.  Ectopic bone induction on and in porous hydroxyapatite combined with collagen and bone morphogenetic protein. , 1988, Clinical orthopaedics and related research.

[11]  R M Pilliar,et al.  The optimum pore size for the fixation of porous-surfaced metal implants by the ingrowth of bone. , 1980, Clinical orthopaedics and related research.

[12]  A. Weinstein,et al.  An evaluation of bone growth into porous high density polyethylene. , 1976, Journal of biomedical materials research.

[13]  D. Roy,et al.  Hydroxyapatite formed from Coral Skeletal Carbonate by Hydrothermal Exchange , 1974, Nature.

[14]  E. White,et al.  Replamineform: A New Process for Preparing Porous Ceramic, Metal, and Polymer Prosthetic Materials , 1972, Science.

[15]  E. White,et al.  New Porous Biomaterials by Replication of Echinoderm Skeletal Microstructures , 1971, Nature.

[16]  Eugene Ryshkewitch,et al.  Compression Strength of Porous Sintered Alumina and Zirconia , 1953 .

[17]  C. Scott,et al.  Processing of porous ceramics , 1992 .

[18]  K. Groot.  Bioceramics consisting of calcium phosphate salts. , 1980 .

[19]  D. Roy,et al.  Hydrothermal synthesis of various carbonate containing calcium hydroxyapatites , 1974 .