EFFECT OF VOLTAGE ON THE CONSOLIDATION OF TiC PARTICULATES ON STEEL SUBSTRATE FUSED BY TIG WELDING ARC

Surface alloying with ceramic powder uses a high energy input to create composite coating that provides protection against wear and corrosion. In this work TiC incorporated composite coating was created by melting single tracks in 1.0 mg/mm2 TiC powder preplaced on alloy steel surfaces using a conventional TIG welding torch produced at 80 ampere current with a voltage between 30 to 55V and a constant traversing speed of 1.0 mm/s. The effect of voltage, used to generate TIG torch for melting, was investigated in terms of geometry, microstructure and hardness of the processed track. The TIG torch produced with different voltages created melt pool of hemispherical shape with varying track dimensions. The melt dimensions increased with increasing voltage. Glazing with 30 V created a melt pool of 3.10mm wide and 0.80 mm deep; the maximum width of 3.96mm and depth of 0.97 mm was produced at 55 V and 45 V, respectively. Tracks produced under different conditions were free from cracks but pores were seen in places. The melt microstructures consisted of partially dissolved and unmelted TiC particulates along with dendrites of a variety of TiC precipitates. Agglomeration of TiC was apparent at the edges. The population of TiC precipitates and partially dissolved TiC particulates increased when glazed at high voltage torch. Hardness development was lowest when glazed at 30 V and it increased by glazing at 35 and 45 V. The population of TiC particulates and their sizes were seen to influence the hardness and this phenomenon is also similar for the precipitated particlesHardness development was lowest when glazed at 30 V and it increased by glazing at 35 and 45 V. The population of TiC particulates and their sizes were seen to influence the hardness and this phenomenon is also similar for the precipitated particles.

[1]  T. N. Baker,et al.  Incorporation of TiC Particulates on AISI 4340 Low Alloy Steel Surfaces via Tungsten Inert Gas Arc Melting , 2012 .

[2]  S. K. Shaha,et al.  Wear Behavior of Modified Surface Layer Produced by TIG Melting of Preplaced Ti Powder in Nitrogen Environment , 2011 .

[3]  Li Mei Wang,et al.  Fe-Cr-C-TiC High-Chromium Fe-Based Ceramic Composite Coating Prepared by PTA Weld-Surfacing Process , 2011 .

[4]  M. Zhang,et al.  Microstructure and wear properties of TiC/FeCrBSi surface composite coating prepared by laser cladding , 2008 .

[5]  E. Liang,et al.  Microstructure and wear resistance of TaC reinforced Ni-based coating by laser cladding , 2008 .

[6]  T. N. Baker,et al.  Incorporation of 3 μm SiCp into Titanium surfaces using a 2.8 kW laser beam of 186 and 373 MJ m-2 energy densities in a nitrogen environment , 2007 .

[7]  Z. Zou,et al.  Characterization of in situ synthesized TiC particle reinforced Fe-based composite coatings produced by multi-pass overlapping GTAW melting process , 2007 .

[8]  J. Haiyan,et al.  Microstructure and mechanical properties of GTA surface modified composite layer on magnesium alloy AZ31 with SiCP , 2007 .

[9]  Z. Zou,et al.  Fabricating TiC particles reinforced Fe-based composite coatings produced by GTAW multi-layers melting process , 2006 .

[10]  Wang Xinhong,et al.  Microstructure and wear properties of in situ TiC/FeCrBSi composite coating prepared by gas tungsten arc welding , 2006 .

[11]  S. Buytoz,et al.  Dry sliding wear behavior of TIG welding clad WC composite coatings , 2005 .

[12]  S. Mridha Titanium nitride layer formation by TIG surface melting in a reactive environment , 2005 .

[13]  K. Das,et al.  A Review on the various synthesis routes of TiC reinforced ferrous based composites , 2002 .

[14]  P. Cheang,et al.  Intermetallic coatings produced by TIG surface melting , 2001 .

[15]  Yue Sun,et al.  Tribological performance of Ti-6Al-4V plasma-based ion implanted with nitrogen , 2000 .

[16]  K. Rie,et al.  Wear-resistant PACVD coatings of the system Ti-B-N , 1999 .

[17]  S. Mridha,et al.  Addition of ceramic particles to TIG melted titanium surfaces , 1999 .

[18]  Marcel Schneider Laser cladding with powder, effect of some machining parameters on clad properties , 1998 .

[19]  T. N. Baker,et al.  Design of surface in situ metal–ceramic composite formation via laser treatment , 1994 .

[20]  J. Abboud,et al.  Microstructure of titanium injected with SiC particles by laser processing , 1991 .

[21]  J. R. Stephens Intermetallic and ceramic matrix composites for 815 to 1370 C (1500 to 2500 F) gas turbine engine applications , 1990 .

[22]  K. Easterling Introduction to the physical metallurgy of welding , 1983 .

[23]  S. Avner Introduction to Physical Metallurgy , 1964 .

[24]  C. J. Smithells,et al.  Metals reference book , 1949 .