Effect of pressure on the deposition of hydrogenated amorphous carbon films using the electron cyclotron resonance chemical vapor deposition

Hydrogenated amorphous carbon (a-C:H) thin films have been deposited from a mixture of methane and hydrogen using the electron cyclotron resonance chemical vapour deposition (ECR-CVD) technique. The films were prepared over a wide range of deposition pressure under a constant microwave power of 200 W, and the rf induced dc bias voltage was maintained constant at −100 V by varying the applied rf power. It was found that changing the deposition pressure in the ECR-CVD process has a profound effect on the properties of the films deposited, as evidenced from their Raman scattering and optical absorption results. The hardness of the films was found to increase remarkably with pressure, whereas the number of bonded hydrogen as deduced from the IR absorption showed only a weak dependence. A hardness of up to 18 GPa was measured for films deposited at 36 mTorr. The sp3 content in the films was also observed to increase with the deposition pressure as deduced from their Raman spectra. The results can be attributed...

[1]  S. Aisenberg,et al.  Ion‐Beam Deposition of Thin Films of Diamondlike Carbon , 1971 .

[2]  Seitaro Matsuo,et al.  Low Temperature Chemical Vapor Deposition Method Utilizing an Electron Cyclotron Resonance Plasma , 1983 .

[3]  A. Bubenzer,et al.  rf‐plasma deposited amorphous hydrogenated hard carbon thin films: Preparation, properties, and applications , 1983 .

[4]  Nick Savvides,et al.  Deposition parameters and film properties of hydrogenated amorphous silicon prepared by high rate dc planar magnetron reactive sputtering , 1984 .

[5]  Robertson,et al.  Electronic and atomic structure of amorphous carbon. , 1987, Physical review. B, Condensed matter.

[6]  A. Ishitani,et al.  Raman spectra of diamondlike amorphous carbon films , 1988 .

[7]  T. Takahagi,et al.  Epitaxial growth of silicon at low temperature by ultrahigh vacuum electron cyclotron resonance plasma chemical vapor deposition , 1988 .

[8]  Tohru Inoue,et al.  Additional Bias Effects on the Formation of Amorphous Hydrogenated Carbon Films by ECR , 1990 .

[9]  F. Pool,et al.  Deposition of diamondlike films by electron cyclotron resonance microwave plasmas , 1990 .

[10]  A. Buuron,et al.  Carbon deposition using an expanding cascaded arc d.c. plasma , 1991 .

[11]  J. Robertson.  Hard amorphous (diamond-like) carbons , 1991 .

[12]  E. Kunhardt,et al.  Deposition of diamond‐like carbon film using electron cyclotron resonance plasma , 1991 .

[13]  J. Chang,et al.  Low temperature and low pressure diamond synthesis in a microwave electron cyclotron resonance discharge , 1991 .

[14]  D. Poitras,et al.  Diamond-like carbon films deposited in a dual microwave-radio-frequency plasma , 1992 .

[15]  M. Tamor,et al.  Raman ``fingerprinting'' of amorphous carbon films , 1994 .

[16]  J. Piqueras,et al.  Silicon dioxide deposition by electron cyclotron resonance plasma: Kinetic and ellipsometric studies , 1994 .

[17]  Rusli,et al.  Photoluminescence in amorphous carbon thin films and its relation to the microscopic properties , 1995 .

[18]  Robertson.  Recombination and photoluminescence mechanism in hydrogenated amorphous carbon. , 1996, Physical review. B, Condensed matter.

[19]  Gehan A. J. Amaratunga,et al.  Nitrogen containing hydrogenated amorphous carbon for thin‐film field emission cathodes , 1996 .

[20]  Rusli,et al.  Photoluminescence behavior of hydrogenated amorphous carbon , 1996 .