Cobalt Ion-Doped TiO(2) Photocatalyst Response to Visible Light.

Photocatalytic activity under visible light irradiation was generated by doping a small amount of Co(2+) ions into TiO(2) particles. Nanometer-sized particles with the composition xCoO-(100-x) TiO(2) (xCo/TiO(2); 0</=x</=6.0) were prepared from TiOSO(4).4.5H(2)O and Co(CH(3)COO)(2).4H(2)O in an ethanol-water solution containing NaOH under reflux. The photoreactivity of xCo/TiO(2) was evaluated by the rate of CH(3)CHO degradation. The Co(2+) ion doping (0.01</=x</=0.27) not only enhanced the photocatalytic activity under ultraviolet-visible (lambda>300 nm) light irradiation but also induced the visible light (lambda>400 nm) response. The highest photocatalytic activities were obtained at x=0.03 for both irradiations. Copyright 2000 Academic Press.

[1] S. Ito,et al. Facile Synthesis of Nanocrystalline Anatase Particles from Titanyl Sulfate , 1998 .

[2] S. Ito,et al. New route to prepare ultrafine ZnO particles and its reaction mechanism , 1997 .

[3] H. Tada,et al. Dependence of TiO2 Photocatalytic Activity upon Its Film Thickness , 1997 .

[4] H. Tada,et al. Mechanism of Formation of Nanocrystalline ZnO Particles through the Reaction of [Zn(acac)2] with NaOH in EtOH , 1998 .

[5] R. Dunbar,et al. Time-resolved photodissociation rates and kinetic modeling for unimolecular dissociations of iodotoluene ions , 1994 .

[6] H. Onishi,et al. Structures and dynamic behavior of catalyst model surfaces characterized by modern physical techniques , 1998 .

[7] Hara,et al. Low-Temperature Synthesis of Nanometer-Sized Crystalline TiO2 Particles and Their Photoinduced Decomposition of Formic Acid. , 1999, Journal of colloid and interface science.

[8] H. Tada. Photoinduced Oxidation of Methylsiloxane Monolayers Chemisorbed on TiO2 , 1996 .

[9] M. Hoffmann,et al. Effects of metal-ion dopants on the photocatalytic reactivity of quantum-sized TiO2 particles , 1994 .

[10] S. Ito,et al. Synthesis of nanometer-sized hematite single crystals through NAC-FAS method , 2000 .