Development of a thermosensitive HAMA-containing bio-ink for the fabrication of composite cartilage repair constructs

Fine-tuning of bio-ink composition and material processing parameters is crucial for the development of biomechanically relevant cartilage constructs. This study aims to design and develop cartilage constructs with tunable internal architectures and relevant mechanical properties. More specifically, the potential of methacrylated hyaluronic acid (HAMA) added to thermosensitive hydrogels composed of methacrylated poly[N-(2-hydroxypropyl)methacrylamide mono/dilactate] (pHPMA-lac)/polyethylene glycol (PEG) triblock copolymers, to optimize cartilage-like tissue formation by embedded chondrocytes, and enhance printability was explored. Additionally, co-printing with polycaprolactone (PCL) was performed for mechanical reinforcement. Chondrocyte-laden hydrogels composed of pHPMA-lac-PEG and different concentrations of HAMA (0%-1% w/w) were cultured for 28 d in vitro and subsequently evaluated for the presence of cartilage-like matrix. Young's moduli were determined for hydrogels with the different HAMA concentrations. Additionally, hydrogel/PCL constructs with different internal architectures were co-printed and analyzed for their mechanical properties. The results of this study demonstrated a dose-dependent effect of HAMA concentration on cartilage matrix synthesis by chondrocytes. Glycosaminoglycan (GAG) and collagen type II content increased with intermediate HAMA concentrations (0.25%-0.5%) compared to HAMA-free controls, while a relatively high HAMA concentration (1%) resulted in increased fibrocartilage formation. Young's moduli of generated hydrogel constructs ranged from 14 to 31 kPa and increased with increasing HAMA concentration. The pHPMA-lac-PEG hydrogels with 0.5% HAMA were found to be optimal for cartilage-like tissue formation. Therefore, this hydrogel system was co-printed with PCL to generate porous or solid constructs with different mesh sizes. Young's moduli of these composite constructs were in the range of native cartilage (3.5-4.6 MPa). Interestingly, the co-printing procedure influenced the mechanical properties of the final constructs. These findings are relevant for future bio-ink development, as they demonstrate the importance of selecting proper HAMA concentrations, as well as appropriate print settings and construct designs for optimal cartilage matrix deposition and final mechanical properties of constructs, respectively.

[1]  J. Glowacki,et al.  Effects of hyaluronan on engineered articular cartilage extracellular matrix gene expression in 3-dimensional collagen scaffolds. , 2001, Journal of biomedical materials research.

[2]  S. Bryant,et al.  Hydrogel properties influence ECM production by chondrocytes photoencapsulated in poly(ethylene glycol) hydrogels. , 2002, Journal of biomedical materials research.

[3]  C. V. van Blitterswijk,et al.  Design of porous scaffolds for cartilage tissue engineering using a three-dimensional fiber-deposition technique. , 2004, Biomaterials.

[4]  N. Takahashi,et al.  Mechanisms involved in enhancement of the expression and function of aggrecanases by hyaluronan oligosaccharides. , 2012, Arthritis and rheumatism.

[5]  J. Malda,et al.  Yield stress determines bioprintability of hydrogels based on gelatin-methacryloyl and gellan gum for cartilage bioprinting , 2016, Biofabrication.

[6]  S. Nehrer,et al.  Investigation of Collagen Transplants Seeded with Human Autologous Chondrocytes at the Time of Transplantation , 2010, Cartilage.

[7]  Albert C. Chen,et al.  Depth- and strain-dependent mechanical and electromechanical properties of full-thickness bovine articular cartilage in confined compression. , 2001, Journal of biomechanics.

[8]  J. Malda,et al.  Biofabrication of multi-material anatomically shaped tissue constructs , 2013, Biofabrication.

[9]  T. Teramura,et al.  Hyaluronic acid regulates a key redox control factor Nrf2 via phosphorylation of Akt in bovine articular chondrocytes , 2015, FEBS open bio.

[10]  Dong-Woo Cho,et al.  An additive manufacturing‐based PCL–alginate–chondrocyte bioprinted scaffold for cartilage tissue engineering , 2015, Journal of tissue engineering and regenerative medicine.

[11]  C. V. van Blitterswijk,et al.  The effect of PEGT/PBT scaffold architecture on the composition of tissue engineered cartilage. , 2005, Biomaterials.

[12]  Wim E. Hennink,et al.  Thermoresponsive Polymeric Micelles with Controlled Instability Based on Hydrolytically Sensitive N-Isopropylacrylamide Copolymers , 2001 .

[13]  T. Yasuda.  Nuclear factor-κB activation by type II collagen peptide in articular chondrocytes: its inhibition by hyaluronan via the receptors , 2013, Modern rheumatology.

[14]  S. Hofmann,et al.  Chondrocyte redifferentiation in 3D: the effect of adhesion site density and substrate elasticity. , 2012, Journal of biomedical materials research. Part A.

[15]  Andrew A. Pitsillides,et al.  An Essential Role for the Interaction Between Hyaluronan and Hyaluronan Binding Proteins During Joint Development , 1998, The journal of histochemistry and cytochemistry : official journal of the Histochemistry Society.

[16]  Randall M. Erb,et al.  Designing bioinspired composite reinforcement architectures via 3D magnetic printing , 2015, Nature Communications.

[17]  Jos Malda,et al.  A Printable Photopolymerizable Thermosensitive p(HPMAm‐lactate)‐PEG Hydrogel for Tissue Engineering , 2011 .

[18]  Moumita Das,et al.  Structure-function relations and rigidity percolation in the shear properties of articular cartilage. , 2014, Biophysical journal.

[19]  P. Benya,et al.  Dedifferentiated chondrocytes reexpress the differentiated collagen phenotype when cultured in agarose gels , 1982, Cell.

[20]  P. Herrlich,et al.  CD44: From adhesion molecules to signalling regulators , 2003, Nature Reviews Molecular Cell Biology.

[21]  D. Hutmacher,et al.  Scaffolds in tissue engineering bone and cartilage. , 2000, Biomaterials.

[22]  T. Scheibel,et al.  Strategies and Molecular Design Criteria for 3D Printable Hydrogels. , 2016, Chemical reviews.

[23]  H. Deschout,et al.  Photopolymerized thermosensitive poly(HPMAlactate)-PEG-based hydrogels: effect of network design on mechanical properties, degradation, and release behavior. , 2010, Biomacromolecules.

[24]  Scott Hollister,et al.  Tissue-engineered cartilage constructs using composite hyaluronic acid/collagen I hydrogels and designed poly(propylene fumarate) scaffolds. , 2007, Tissue engineering.

[25]  Dietmar W. Hutmacher,et al.  Hyaluronic Acid Enhances the Mechanical Properties of Tissue-Engineered Cartilage Constructs , 2014, PloS one.

[26]  M. Morra,et al.  Novel bioceramic-reinforced hydrogel for alveolar bone regeneration. , 2016, Acta biomaterialia.

[27]  Zohreh Izadifar,et al.  Modulating mechanical behaviour of 3D-printed cartilage-mimetic PCL scaffolds: influence of molecular weight and pore geometry , 2016, Biofabrication.

[28]  E B Hunziker,et al.  Optical and mechanical determination of Poisson's ratio of adult bovine humeral articular cartilage. , 1997, Journal of biomechanics.

[29]  Hyejin Park,et al.  Injectable chitosan hyaluronic acid hydrogels for cartilage tissue engineering. , 2013, Acta biomaterialia.

[30]  W. Dhert,et al.  Hypoxia impedes hypertrophic chondrogenesis of human multipotent stromal cells. , 2012, Tissue engineering. Part A.

[31]  D. Hutmacher,et al.  The return of a forgotten polymer : Polycaprolactone in the 21st century , 2009 .

[32]  Robert L Sah,et al.  Tissue engineering of articular cartilage with biomimetic zones. , 2009, Tissue engineering. Part B, Reviews.

[33]  J. Steadman,et al.  Microfracture: surgical technique and rehabilitation to treat chondral defects. , 2001, Clinical orthopaedics and related research.

[34]  Jos Malda,et al.  A Synthetic Thermosensitive Hydrogel for Cartilage Bioprinting and Its Biofunctionalization with Polysaccharides. , 2016, Biomacromolecules.

[35]  Jos Malda,et al.  Reinforcement of hydrogels using three-dimensionally printed microfibres , 2015, Nature Communications.

[36]  J Malda,et al.  A thermo-responsive and photo-polymerizable chondroitin sulfate-based hydrogel for 3D printing applications. , 2016, Carbohydrate polymers.

[37]  D. Vigetti,et al.  Biology and biotechnology of hyaluronan , 2015, Glycoconjugate Journal.

[38]  R W Farndale,et al.  A direct spectrophotometric microassay for sulfated glycosaminoglycans in cartilage cultures. , 1982, Connective tissue research.

[39]  Scott J. Hollister,et al.  Erratum: Porous scaffold design for tissue engineering , 2006 .

[40]  J. Malda,et al.  Biofabrication of reinforced 3D-scaffolds using two-component hydrogels. , 2015, Journal of materials chemistry. B.

[41]  D. Cho,et al.  Improving mechanical properties of alginate hydrogel by reinforcement with ethanol treated polycaprolactone nanofibers , 2013 .

[42]  H. Deschout,et al.  Photopolymerized thermosensitive hydrogels for tailorable diffusion-controlled protein delivery. , 2009, Journal of controlled release : official journal of the Controlled Release Society.

[43]  Dietmar W. Hutmacher,et al.  A biomimetic extracellular matrix for cartilage tissue engineering centered on photocurable gelatin, hyaluronic acid and chondroitin sulfate. , 2014, Acta biomaterialia.

[44]  Z. Qian,et al.  Recent developments in scaffold-guided cartilage tissue regeneration. , 2014, Journal of biomedical nanotechnology.

[45]  A. Goodship,et al.  The effects of hyaluronic acid on articular chondrocytes. , 2005, Journal of Bone and Joint Surgery-british Volume.

[46]  J Malda,et al.  Hydrogel-based reinforcement of 3D bioprinted constructs , 2016, Biofabrication.

[47]  M. Tammi,et al.  Hyaluronan binding by cell surface CD44. , 2000, The Journal of biological chemistry.

[48]  W. Hennink,et al.  Degradation Mechanism and Kinetics of Thermosensitive Polyacrylamides Containing Lactic Acid Side Chains , 2003 .

[49]  D K MacCallum,et al.  Culture and growth characteristics of chondrocytes encapsulated in alginate beads. , 1989, Connective tissue research.

[50]  S. Hollister.  Porous scaffold design for tissue engineering , 2005, Nature materials.

[51]  Divya Prakash,et al.  Natural progression of osteo-chondral defect in the femoral condyle. , 2002, The Knee.

[52]  D. Cho,et al.  3D printing of composite tissue with complex shape applied to ear regeneration , 2014, Biofabrication.

[53]  F. Boey,et al.  Effect of cell-seeding density on the proliferation and gene expression profile of human umbilical vein endothelial cells within ex vivo culture. , 2011, Cytotherapy.

[54]  R. Auzély-Velty,et al.  Design of biomimetic cell-interactive substrates using hyaluronic acid hydrogels with tunable mechanical properties. , 2012, Biomacromolecules.

[55]  P. Janmey,et al.  Tissue Cells Feel and Respond to the Stiffness of Their Substrate , 2005, Science.

[56]  Wim E Hennink,et al.  25th Anniversary Article: Engineering Hydrogels for Biofabrication , 2013, Advanced materials.

[57]  T. Vermonden,et al.  Photopolymerized thermosensitive hydrogels: synthesis, degradation, and cytocompatibility. , 2008, Biomacromolecules.

[58]  N. Adachi,et al.  Hyaluronic acid enhances proliferation and chondroitin sulfate synthesis in cultured chondrocytes embedded in collagen gels , 1999, Journal of cellular physiology.

[59]  J. Malda,et al.  Development and characterisation of a new bioink for additive tissue manufacturing. , 2014, Journal of materials chemistry. B.

[60]  J Malda,et al.  Bioprinting of hybrid tissue constructs with tailorable mechanical properties , 2011, Biofabrication.

[61]  F. J. Dzida,et al.  Comparative study of the intrinsic mechanical properties of the human acetabular and femoral head cartilage , 1991, Journal of orthopaedic research : official publication of the Orthopaedic Research Society.

[62]  Differential behavior of auricular and articular chondrocytes in hyaluronic acid hydrogels. , 2008 .

[63]  Anthony Atala,et al.  3D bioprinting of tissues and organs , 2014, Nature Biotechnology.

[64]  C. V. van Donkelaar,et al.  Low agarose concentration and TGF-β3 distribute extracellular matrix in tissue-engineered cartilage. , 2013, Tissue engineering. Part A.

[65]  P. R. Weeren,et al.  Zonal Chondrocyte Subpopulations Reacquire Zone-Specific Characteristics during in Vitro Redifferentiation , 2009, The American journal of sports medicine.

[66]  T. Board,et al.  Chemical Basis for the Histological Use of Safranin O in the Study of Articular Cartilage , 2014 .

[67]  K. Athanasiou,et al.  Design Characteristics for the Tissue Engineering of Cartilaginous Tissues , 2004, Annals of Biomedical Engineering.

[68]  J Tramper,et al.  The effect of PEGT/PBT scaffold architecture on oxygen gradients in tissue engineered cartilaginous constructs. , 2004, Biomaterials.

[69]  ZhiYong Qian,et al.  Biodegradable CSMA/PECA/Graphene Porous Hybrid Scaffold for Cartilage Tissue Engineering , 2015, Scientific Reports.

[70]  Gaurav Jain,et al.  Cell migration on planar and three-dimensional matrices: a hydrogel-based perspective. , 2015, Tissue engineering. Part B, Reviews.

[71]  Itai Cohen,et al.  Mapping the depth dependence of shear properties in articular cartilage. , 2007, Journal of biomechanics.

[72]  Feng Xu,et al.  Engineering three-dimensional cell mechanical microenvironment with hydrogels , 2012, Biofabrication.