Variable amplitude fatigue crack growth in a mild steel for railway axles: Experiments and predictive models

Abstract Railway axles, though designed for infinite life, are subject to failure due to various types of surface damage (ballast hits, corrosion) that might occur during their very long service life (30 years or 10 7  km). This problem is dealt with by regular axle examinations in the form of nondestructive testing inspections, whose periodicity is calculated on the basis of the propagation lifetime of a given initial defect. The key point is therefore a reliable estimation of propagation lifetime under service loads. This paper discusses the application of predictive crack growth algorithms to the propagations of cracks in A1N steel axles. In particular, constant amplitude crack propagation tests on small-scale and “companion specimens” were carried out together with experiments on full-scale axles. Variable amplitude tests on companion specimens were performed and the results were then analysed using a simple “no-interaction” algorithm. Then, variable amplitude tests on companion specimens and the analysis of results with a simple “no-interaction” algorithm and the Strip-Yield model were dealt with. The results showed a negligible load-interaction effect on “companion specimens” and a significant retardation on full-scale axles. The consequences resulting from the application of predictive models to a full-scale axle under service spectrum were then analysed.

[1]  M. Skorupa,et al.  Load interaction effects during fatigue crack growth under variable amplitude loading—a literature review. Part II: qualitative interpretation , 1999 .

[2]  J. B. Chang,et al.  Methods and models for predicting fatigue crack growth under random loading , 1981 .

[3]  I. Varfolomeev,et al.  Fracture mechanics assessment of railway axles: Experimental characterization and computation , 2010 .

[4]  Stefano Beretta,et al.  An algorithm for evaluating crack closure from local compliance measurements , 2002 .

[5]  K. M. Golos,et al.  A comparison of different methods to determine the threshold of fatigue crack propagation , 1994 .

[6]  S. Beretta,et al.  Simulation of Fatigue Crack Propagation in Railway Axles , 2005 .

[7]  Jaap Schijve,et al.  Four lectures on fatigue crack growth , 1977 .

[8]  S. Beretta,et al.  Analysis of Crack Growth at R =−1 under Variable Amplitude Loading on a Steel for Railway Axles , 2008 .

[9]  James C. Newman,et al.  On Generating Fatigue Crack Growth Thresholds , 2003 .

[10]  S. Beretta,et al.  An investigation of the effects of corrosion on the fatigue strength of AlN axle steel , 2008 .

[11]  J. Newman,et al.  Compression pre-cracking to generate near threshold fatigue-crack-growth rates in two aluminum alloys , 2005 .

[12]  M. Carboni,et al.  Variable amplitude crack growth in railway axles: influence on inspection intervals , 2009 .

[13]  Mauro Madia,et al.  Estimation of Constraint under Cyclic Loading on Cracked Components , 2009 .

[14]  M. Dankert,et al.  AN ANALYTICAL PROCEDURE FOR PREDICTING OPENING LOADS OF CRACKS AT NOTCHES , 1995 .

[15]  Jaap Schijve,et al.  Fatigue of structures and materials , 2001 .

[16]  Uwe Zerbst,et al.  The development of a damage tolerance concept for railway components and its demonstration for a railway axle , 2005 .

[17]  James C. Newman,et al.  Fatigue-Crack-Growth Computer Program , 1991 .

[18]  Michele Carboni,et al.  Application of fatigue crack growth algorithms to railway axles and comparison of two steel grades , 2004 .

[19]  E. Gassner,et al.  ASSESSMENT OF THE ALLOWABLE DESIGN STRESSES AND THE CORRESPONDING FATIGUE LIFE , 1969 .

[20]  Uwe Zerbst,et al.  Damage tolerance of railway axles , 2011 .

[21]  M. Skorupa.  Load interaction effects during fatigue crack growth under variable amplitude loading : A literature review. Part I : Empirical trends , 1998 .

[22]  Atsushi Sugeta,et al.  CRACK CLOSURE AND EFFECT OF LOAD VARIATION ON SMALL FATIGUE CRACK GROWTH BEHAVIOUR , 1996 .

[23]  Michele Carboni,et al.  Experiments and stochastic model for propagation lifetime of railway axles , 2006 .

[24]  Ji-Ho Song,et al.  Crack closure and growth behavior of physically short fatigue cracks under random loading , 2000 .

[25]  Arthur T. Motta,et al.  Microstructure and Growth Mechanism of Oxide Layers Formed on Zr Alloys Studied with Micro-Beam Synchrotron Radiation , 2005 .

[26]  L. Rose,et al.  The influence of cross‐sectional thickness on fatigue crack growth , 1999 .

[27]  M. Carboni,et al.  Determination of Δ K th by Compression Pre-Cracking in a Structural Steel , 2009 .

[28]  Fred Nilsson,et al.  Closure effects on fatigue crack growth rates at constant and variable amplitude loading , 2004 .

[29]  J. Schijve,et al.  Application of the strip-yield model from the NASGRO software to predict fatigue crack growth in aluminium alloys under constant and variable amplitude loading , 2007 .

[30]  J. Newman.  A crack-closure model for predicting fatigue crack growth under aircraft spectrum loading , 1981 .

[31]  Alain Leluan,et al.  Prédiction de la durée de vie des essieux-axes ferroviaires , 1999 .

[32]  D S Hoddinott,et al.  Railway axle failure investigations and fatigue crack growth monitoring of an axle , 2004 .

[33]  Stefano Beretta,et al.  Effect of probability of detection upon the definition of inspection intervals for railway axles , 2007 .