Effect of Reaction Parameters on γ‐AlON Formation from Al2O3 and AlN

The formation of γ-AlON from Al2O3 and AlN was investigated as a function of some of the reaction parameters, that is, temperature and time. The appearance of phases was followed in conjunction with the change in lattice parameter to reveal the reaction sequences of formation. An oxygen-rich γ-AlON phase formed first, which reacted further with AlN. Nitrogen diffusion through the γ-AlON lattice seemed to be rate controlling.

[1] Hong-Yang Lu,et al. Defect reactions and the controlling mechanism in the sintering of magnesium aluminate spinel , 1999 .

[2] Jie Zheng,et al. Carbothermal synthesis of Aluminium Oxynitride (ALON) powder: Influence of starting materials and synthesis parameters , 1995 .

[3] H. X. Willems,et al. Thermodynamics of Alon I: Stability at Lower Temperatures , 1992 .

[4] H. X. Willems,et al. Thermodynamics of Alon II : phase relations , 1992 .

[5] M. Ish-Shalom. Formation of aluminium oxynitride by carbothermal reduction of aluminium oxide in nitrogen , 1982 .

[6] I. Cutler,et al. Preparation of Sinterable Cubic Aluminum Oxynitride by the Carbothermal Nitridation of Aluminum Oxide , 1981 .

[7] J. Labbé,et al. Contribution a l'etude du systeme AL/O/N II: Retention d'azote dans les produits d'oxydation de l'oxynitrure d'aluminium γ , 1981 .

[8] J. Mccauley,et al. Phase Relations and Reaction Sintering of Transparent Cubic Aluminum Oxynitride Spinel (ALON) , 1979 .

[9] J. Mccauley,et al. A Simple Model for Aluminum Oxynitride Spinels , 1978 .

[10] P. Goursat,et al. Contribution a l'etude du systeme Al/O/N I — reactive de l'oxynitrure d'aluminium γ , 1976 .