Urchin-like CoP Nanocrystals as Hydrogen Evolution Reaction and Oxygen Reduction Reaction Dual-Electrocatalyst with Superior Stability.

High-performance electrocatalysts with superior stability are critically important for their practical applications in hydrogen evolution reaction (HER) and oxygen reduction reaction (ORR). Herein, we report a facile method to fabricate urchin-like CoP nanocrystals (NCs) as catalyst for both HER and ORR with desirable electrocatalytic activities and long-term stability. The urchin-like CoP NCs with a diameter of 5 μm were successfully prepared by a hydrothermal reaction following a phosphidation treatment in N2 atmosphere and present excellent HER catalytic performance with a low onset overpotential of 50 mV, a small Tafel slope of 46 mV/decade, and an exceptional low overpotential of ~180 mV at a current density of 100 mA cm(-2) with a mass loading density of 0.28 mg/cm(2). Meanwhile, a remarkable ORR catalytic activity was observed with a half-potential of 0.7 V and an onset potential of 0.8 V at 1600 rpm and a scan rate of 5 mV s(-1). More importantly, the urchin-like CoP NCs present superior stability and keep their catalytic activity for at least 10 000 CV cycles for HER in 0.5 M H2SO4 and over 30 000 s for ORR in 0.1 M KOH, which is ascribed to their robust three-dimensional structure. This urchin-like CoP NCs might be a promising replacement to the Pt-based electrocatalysts in water splitting and fuel cells.

[1]  Xun Wang,et al.  Noble metal alloy complex nanostructures: controllable synthesis and their electrochemical property. , 2015, Chemical Society reviews.

[2]  Wenzhong Wang,et al.  Shape-controlled synthesis of nickel phosphide nanocrystals and their application as hydrogen evolution reaction catalyst , 2015 .

[3]  Xuping Sun,et al.  Cobalt phosphide nanowires: efficient nanostructures for fluorescence sensing of biomolecules and photocatalytic evolution of dihydrogen from water under visible light. , 2015, Angewandte Chemie.

[4]  X. Lou,et al.  Porous molybdenum carbide nano-octahedrons synthesized via confined carburization in metal-organic frameworks for efficient hydrogen production , 2015, Nature Communications.

[5]  N. Lewis,et al.  Highly branched cobalt phosphide nanostructures for hydrogen-evolution electrocatalysis , 2015 .

[6]  Qiangbin Wang,et al.  MoSe2 porous microspheres comprising monolayer flakes with high electrocatalytic activity , 2015, Nano Research.

[7]  Jakob Kibsgaard,et al.  Molybdenum phosphosulfide: an active, acid-stable, earth-abundant catalyst for the hydrogen evolution reaction. , 2014, Angewandte Chemie.

[8]  Ping Jiang,et al.  A cost-effective 3D hydrogen evolution cathode with high catalytic activity: FeP nanowire array as the active phase. , 2014, Angewandte Chemie.

[9]  Abdullah M. Asiri,et al.  Self-Supported FeP Nanorod Arrays: A Cost-Effective 3D Hydrogen Evolution Cathode with High Catalytic Activity , 2014 .

[10]  N. Lewis,et al.  Electrocatalytic hydrogen evolution using amorphous tungsten phosphide nanoparticles. , 2014, Chemical communications.

[11]  N. Lewis,et al.  Amorphous Molybdenum Phosphide Nanoparticles for Electrocatalytic Hydrogen Evolution , 2014 .

[12]  Cuncai Lv,et al.  Ni12P5 nanoparticles as an efficient catalyst for hydrogen generation via electrolysis and photoelectrolysis. , 2014, ACS nano.

[13]  Yanguang Li,et al.  Ultrathin WS2 nanoflakes as a high-performance electrocatalyst for the hydrogen evolution reaction. , 2014, Angewandte Chemie.

[14]  Abdullah M. Asiri,et al.  Carbon nanotubes decorated with CoP nanocrystals: a highly active non-noble-metal nanohybrid electrocatalyst for hydrogen evolution. , 2014, Angewandte Chemie.

[15]  Song Jin,et al.  High-performance electrocatalysis using metallic cobalt pyrite (CoS₂) micro- and nanostructures. , 2014, Journal of the American Chemical Society.

[16]  Nathan S Lewis,et al.  Highly active electrocatalysis of the hydrogen evolution reaction by cobalt phosphide nanoparticles. , 2014, Angewandte Chemie.

[17]  Abdullah M. Asiri,et al.  Self-supported nanoporous cobalt phosphide nanowire arrays: an efficient 3D hydrogen-evolving cathode over the wide range of pH 0-14. , 2014, Journal of the American Chemical Society.

[18]  Xiaodong Li,et al.  Needle-like Co3O4 anchored on the graphene with enhanced electrochemical performance for aqueous supercapacitors. , 2014, ACS applied materials & interfaces.

[19]  Karren L. More,et al.  Highly Crystalline Multimetallic Nanoframes with Three-Dimensional Electrocatalytic Surfaces , 2014, Science.

[20]  T. Jaramillo,et al.  Building an appropriate active-site motif into a hydrogen-evolution catalyst with thiomolybdate [Mo3S13]2- clusters. , 2014, Nature chemistry.

[21]  Micheál D. Scanlon,et al.  A nanoporous molybdenum carbide nanowire as an electrocatalyst for hydrogen evolution reaction , 2014 .

[22]  B. Pan,et al.  Controllable disorder engineering in oxygen-incorporated MoS2 ultrathin nanosheets for efficient hydrogen evolution. , 2013, Journal of the American Chemical Society.

[23]  H. Dai,et al.  WS2 nanoflakes from nanotubes for electrocatalysis , 2013, Nano Research.

[24]  X. Lou,et al.  Defect‐Rich MoS2 Ultrathin Nanosheets with Additional Active Edge Sites for Enhanced Electrocatalytic Hydrogen Evolution , 2013, Advanced materials.

[25]  James R. McKone,et al.  Nanostructured nickel phosphide as an electrocatalyst for the hydrogen evolution reaction. , 2013, Journal of the American Chemical Society.

[26]  Zaiping Guo,et al.  Self-assembly of hierarchical star-like Co3O4 micro/nanostructures and their application in lithium ion batteries. , 2013, Nanoscale.

[27]  Desheng Kong,et al.  Synthesis of MoS2 and MoSe2 films with vertically aligned layers. , 2013, Nano letters.

[28]  Francisco del Monte,et al.  Three dimensional macroporous architectures and aerogels built of carbon nanotubes and/or graphene: synthesis and applications. , 2013, Chemical Society reviews.

[29]  H. Vrubel,et al.  Molybdenum boride and carbide catalyze hydrogen evolution in both acidic and basic solutions. , 2012, Angewandte Chemie.

[30]  Jakob Kibsgaard,et al.  Engineering the surface structure of MoS2 to preferentially expose active edge sites for electrocatalysis. , 2012, Nature materials.

[31]  A. Frenkel,et al.  Hydrogen-evolution catalysts based on non-noble metal nickel-molybdenum nitride nanosheets. , 2012, Angewandte Chemie.

[32]  X. Lou,et al.  Porous Co3O4 nanowires derived from long Co(CO3)(0.5)(OH)·0.11H2O nanowires with improved supercapacitive properties. , 2012, Nanoscale.

[33]  T. Jaramillo,et al.  Core-shell MoO3-MoS2 nanowires for hydrogen evolution: a functional design for electrocatalytic materials. , 2011, Nano letters.

[34]  Zhongwei Chen,et al.  A review on non-precious metal electrocatalysts for PEM fuel cells , 2011 .

[35]  H. Dai,et al.  Co₃O₄ nanocrystals on graphene as a synergistic catalyst for oxygen reduction reaction. , 2011, Nature materials.

[36]  Guosong Hong,et al.  MoS2 nanoparticles grown on graphene: an advanced catalyst for the hydrogen evolution reaction. , 2011, Journal of the American Chemical Society.

[37]  Y. Liu,et al.  Nitrogen-doped graphene as efficient metal-free electrocatalyst for oxygen reduction in fuel cells. , 2010, ACS nano.

[38]  Wei Xing,et al.  Development of durable carbon black/titanium dioxide supported macrocycle catalysts for oxygen reduction reaction , 2009 .

[39]  Piotr Zelenay,et al.  A class of non-precious metal composite catalysts for fuel cells , 2006, Nature.

[40]  M. A. Malik,et al.  Synthesis of single-crystalline CoP nanowires by a one-pot metal-organic route. , 2005, Journal of the American Chemical Society.

[41]  Martin Winter,et al.  What Are Batteries, Fuel Cells, and Supercapacitors? (Chem. Rev. 2003, 104, 4245−4269. Published on the Web 09/28/2004.) , 2005 .

[42]  B. V. Tilak,et al.  Interfacial processes involving electrocatalytic evolution and oxidation of H2, and the role of chemisorbed H , 2002 .

[43]  B. Conway,et al.  ac Impedance of Faradaic reactions involving electrosorbed intermediates—I. Kinetic theory , 1987 .