Lifetime assessment of Bisphenol-A Polycarbonate (BPA-PC) plastic lens, used in LED-based products

Abstract In this investigation, the accelerated optical degradation of two different commercial Bisphenol-A Polycarbonate (BPA-PC) grades under elevated temperature stress is studied. The BPA-PC plates are used both in light conversion carriers in LED modules and encapsulants in LED packages. BPA-PC plates are exposed to temperatures in the range of 100–140 °C. Optical properties of the thermally-aged plates were studied using an integrated sphere. The results show that increasing the exposure time leads to degradation of BPA-PC optical properties, i.e. decrease of light transmission and increase in the yellowing index (YI). An exponential luminous decay model and Arrhenius equation are used to predict the lumen depreciation over different time and temperatures. Accelerated thermal stress tests together with the applied reliability model are used to predict the lifetime of plastic lens in LED lamps in real life conditions.

[1]  S. Girois,et al.  Polym. Degrad. Stab. , 1996 .

[2]  W. D. Driel,et al.  Photodegradation of bisphenol A polycarbonate under blue light radiation and its effect on optical properties , 2013 .

[3]  J. Carnahan,et al.  The chemistry of γ-irradiated bisphenol-A polycarbonate , 1994 .

[4]  Gaudenzio Meneghesso,et al.  Phosphors for LED-based light sources: Thermal properties and reliability issues , 2012, Microelectron. Reliab..

[5]  Uwe Strauss,et al.  Industrial production of GaN and InGaN-light emitting diodes on SiC-substrates , 2001 .

[6]  S. Esterby.  American Society for Testing and Materials , 2006 .

[7]  Gaudenzio Meneghesso,et al.  High temperature electro-optical degradation of InGaN/GaN HBLEDs , 2007, Microelectron. Reliab..

[8]  M. Vanzi,et al.  Accelerated Life Test of High Brightness Light Emitting Diodes , 2008, IEEE Transactions on Device and Materials Reliability.

[9]  P. V. Varde,et al.  Light emitting diodes reliability review , 2012, Microelectron. Reliab..

[10]  Michael R. Krames,et al.  Green phosphor-converted LED , 2002, SPIE Optics + Photonics.

[11]  Regina Mueller-Mach,et al.  Illumination-grade white LEDs , 2002, SPIE Optics + Photonics.

[12]  Jean Paul Freyssinier,et al.  Solid-state lighting: failure analysis of white LEDs , 2004 .

[13]  Jao-Hwa Kuang,et al.  Failure Mechanisms Associated With Lens Shape of High-Power LED Modules in Aging Test , 2008, IEEE Transactions on Electron Devices.

[14]  Bo Sun,et al.  Product level accelerated lifetime test for indoor LED luminaires , 2013, 2013 14th International Conference on Thermal, Mechanical and Multi-Physics Simulation and Experiments in Microelectronics and Microsystems (EuroSimE).

[15]  Chang-Hee Hong,et al.  Optical Degradation of Phosphor-Converted White GaN-Based Light-Emitting Diodes under Electro-Thermal Stress , 2011 .

[16]  Lianqiao Yang,et al.  Electrical, optical and thermal degradation of high power GaN/InGaN light-emitting diodes , 2008 .

[17]  Gaudenzio Meneghesso,et al.  Stability and performance evaluation of high-brightness light-emitting diodes under DC and pulsed bias conditions , 2006, SPIE Optics + Photonics.

[18]  A. Steckl,et al.  A nearly ideal phosphor-converted white light-emitting diode , 2008 .

[19]  Shuji Nakamura,et al.  Present performance of InGaN-based blue/green/yellow LEDs , 1997, Photonics West.

[20]  N. Narendran,et al.  Extracting phosphor‐scattered photons to improve white LED efficiency , 2005 .