Application of X-ray microtomography to study the influence of the casting microstructure upon the tensile behaviour of an Al-Si alloy

In cast aluminium alloys used in the automotive industry the microstructure inherited from the foundry process has a strong influence on the mechanical properties. In the cylinder heads produced by the Lost Foam Casting process, the microstructure consists of hard intermetallic phases and large gas and microshrinkage pores. To study its influence, full field measurements at the microstructure scale were performed during a tensile test performed in situ under X-ray microtomography. Intermetallics were used as a natural speckle pattern. Feasibility of Digital Volume Correlation on this alloy was proved and the accuracy of the measurement was assessed and discussed in light of the small volume fraction of intermetallics and in comparison with the accuracy of Digital Image Correlation performed on optical images at a finer spatial resolution.

[1]  Johann Kastner,et al.  A comparative study of high resolution cone beam X-ray tomography and synchrotron tomography applied to Fe- and Al-alloys , 2010, NDT & E international : independent nondestructive testing and evaluation.

[2]  E. Maire,et al.  In Situ Experiments with X ray Tomography: an Attractive Tool for Experimental Mechanics , 2010 .

[3]  Stéphane Roux,et al.  Three dimensional image correlation from X-Ray computed tomography of solid foam , 2008 .

[4]  C. Davidson,et al.  Oxide films, pores and the fatigue lives of cast aluminum alloys , 2006 .

[5]  A. Chabod,et al.  Microtomographic study and finite element analysis of the porosity harmfulness in a cast aluminium alloy , 2011 .

[6]  E. Maire,et al.  3D Characterization of the Influence of Porosity on Fatigue Properties of a Cast Al Alloy , 2011 .

[7]  Stéphane Roux,et al.  Influence of closure on the 3D propagation of fatigue cracks in a nodular cast iron investigated by X-ray tomography and 3D volume correlation , 2010 .

[8]  Yuh J. Chao,et al.  Advances in Two-Dimensional and Three-Dimensional Computer Vision , 2000 .

[9]  D. Tolnai,et al.  Characterization of phases in an Al casting alloy by synchrotron tomography , 2009 .

[10]  Dominique Houzet,et al.  Investigating performance variations of an optimized GPU-ported granulometry algorithm , 2012, Proceedings of the 2012 Conference on Design and Architectures for Signal and Image Processing.

[11]  J. Réthoré,et al.  Analysis and Artifact Correction for Volume Correlation Measurements Using Tomographic Images from a Laboratory X-ray Source , 2011 .

[12]  E. Maire,et al.  Experimental study of porosity and its relation to fatigue mechanisms of model Al–Si7–Mg0.3 cast Al alloys , 2001 .

[13]  Fabien Szmytka,et al.  Behavior, damage and fatigue life assessment of lost foam casting aluminum alloys under thermo-mechanical fatigue conditions , 2010 .

[14]  Thomas Zwieg.  Specimen preparation for high edge retention of aluminum alloys , 2003 .

[15]  S. Degallaix,et al.  Surface observation and measurement techniques to study the fatigue damage micromechanisms in a duplex stainless steel , 2009 .