A geometric approach to modeling microstructurally small fatigue crack formation: I. Probabilistic simulation of constituent particle cracking in AA 7075-T651

Microstructurally small fatigue crack (MSFC) formation includes stages of incubation, nucleation and microstructurally small propagation. In AA 7075-T651, the fracture of Al7Cu2Fe constituent particles is the major incubation source. In experiments, it has been observed that only a small percentage of these Fe-bearing particles crack in a highly stressed volume. The work presented here addresses the identification of the particles prone to cracking and the prediction of particle cracking frequency, given a distribution of particles and crystallographic texture in such a volume. Three-dimensional elasto-viscoplastic finite element analyses are performed to develop a response surface for the tensile stress in the particle as a function of the strain level surrounding the particle, parent grain orientation and particle aspect ratio. A technique for estimating particle strength from fracture toughness, particle size and intrinsic flaw size is developed. Particle cracking is then determined by comparing particle stress and strength. The frequency of particle cracking is then predicted from sampling measured distributions of grain orientation, particle aspect ratio and size. Good agreement is found between the predicted frequency of particle cracking and two preliminary validation experiments. An estimate of particle cracking frequency is important for simulating the next stages of MSFC formation: inserting all particles into a microstructural model for these stages is computationally intractable and physically unnecessary.

[1]  Peter S. Pacheco.  Parallel programming with MPI , 1996 .

[2]  P. Dawson,et al.  Modeling crystallographic texture evolution with finite elements over neo-Eulerian orientation spaces , 1998 .

[3]  W. Morris.  The effect of intermetallics composition and microstructure on fatigue crack initiation in AI 2219-T851 , 1978 .

[4]  Y. Murakami,et al.  Effects of defects, inclusions and inhomogeneities on fatigue strength , 1994 .

[5]  M. Sutcu.  Statistical fibre failure and single crack behaviour in uniaxially reinforced ceramic composites , 1988 .

[6]  Toshio Mura,et al.  Micromechanics of defects in solids , 1982 .

[7]  U. F. Kocks,et al.  Latent hardening in aluminum , 1966 .

[8]  Otto Buck,et al.  Fatigue crack initiation and early propagation in Al 2219-T851 , 1976 .

[9]  T. C. Lindley,et al.  The effect of porosity on the fatigue life of cast aluminium-silicon alloys , 2004 .

[10]  Y. Murakami.  Stress Intensity Factors Handbook , 2006 .

[11]  E. W. Hart.  Theory of dispersion hardening in metals , 1972 .

[12]  M. Horstemeyer,et al.  Micromechanisms of multistage fatigue crack growth in a high-strength aluminum alloy , 2007 .

[13]  Karel Matouš,et al.  Finite element formulation for modelling large deformations in elasto‐viscoplastic polycrystals , 2004 .

[14]  The Institute of Metals , 1915, Nature.

[15]  David L. McDowell,et al.  Microstructure-based fatigue modeling of cast A356-T6 alloy , 2003 .

[16]  B. Lawn.  Fracture of Brittle Solids by Brian Lawn , 1993 .

[17]  A. Rollett,et al.  Three Dimensional Microstructures: Statistical Analysis of Second Phase Particles in AA7075-T651 , 2006 .

[18]  W. Curtin.  In Situ Fiber Strengths in Ceramic‐Matrix Composites from Fracture Mirrors , 1994 .

[19]  Bruce A. Craig,et al.  Probabilistic method for predicting the variability in fatigue behavior of 7075-T6 aluminum , 1999 .

[20]  David R. Clarke,et al.  The influence of particle size and particle fracture on the elastic/plastic deformation of metal matrix composites , 1996 .

[21]  Paul Lipinski,et al.  Micromechanical modelling of the elastoplastic behavior of polycrystals containing precipitates— Application to hypo- and hyper-eutectoid steels , 1997 .

[22]  Bernard D. Coleman,et al.  On the strength of classical fibres and fibre bundles , 1958 .

[23]  Ming Gao,et al.  An analytical electron microscopy study of constituent particles in commercial 7075-T6 and 2024-T3 alloys , 1998 .

[24]  J. Schijve,et al.  The role of inclusions in fatigue crack initiation in an aluminum alloy , 1973 .

[25]  Y. Matsuo,et al.  A Probabilistic Treatise of Rupture of Brittle Rotating Disks , 1979 .

[26]  P. Neumann,et al.  Representation of orientation and disorientation data for cubic, hexagonal, tetragonal and orthorhombic crystals , 1991 .

[27]  X. Z. Li,et al.  HREM study and structure modeling of the η′ phase, the hardening precipitates in commercial Al–Zn–Mg alloys , 1999 .

[28]  Morris E. Fine,et al.  Fatigue Crack initiation and microcrack growth in 2024-T4 and 2124-T4 aluminum alloys , 1979 .

[29]  Lyndon Edwards,et al.  Effect of surface texture on fatigue life in a squeeze-cast 6082 aluminium alloy , 1993 .

[30]  David L. McDowell,et al.  Computational micromechanics analysis of cyclic crack-tip behavior for microstructurally small cracks in dual-phase Al–Si alloys , 2001 .

[31]  U. F. Kocks.  The relation between polycrystal deformation and single-crystal deformation , 1970 .

[32]  K. Tanaka,et al.  A theory of fatigue crack initiation at inclusions , 1982 .

[33]  Owen Richmond,et al.  Three dimensional characterization and modeling of particle reinforced metal matrix composites: part I Quantitative description of microstructural morphology , 1999 .

[34]  Leo Christodoulou,et al.  Using materials prognosis to maximize the utilization potential of complex mechanical systems , 2004 .

[35]  M. Li,et al.  Three dimensional characterization and modeling of particle reinforced metal matrix composites part II: damage characterization , 1999 .

[36]  Kazuaki Shiozawa,et al.  CRACK INITIATION AND SMALL FATIGUE CRACK GROWTH BEHAVIOUR OF SQUEEZE‐CAST Al‐Si ALUMINIUM ALLOYS , 1997 .

[37]  P. Jackson,et al.  Latent Hardening and the Flow Stress in Copper Single Crystals , 1967 .

[38]  L. Riester,et al.  Characterization of Vickers, Berkovich, Spherical and Cube Cornered Diamond Indenters by Nanoindentation and SFM , 1998 .

[39]  James C. Newman,et al.  Stress-intensity factors for a wide range of semi-elliptical surface cracks in finite-thickness plates , 1979 .

[40]  Paul E. Magnusen,et al.  Microstructurally based model of fatigue initiation and growth , 1994 .

[41]  Mark F. Horstemeyer,et al.  Damage and stress state influence on the Bauschinger effect in aluminum alloys , 2007 .

[42]  K. Trustrum,et al.  On estimating the Weibull modulus for a brittle material , 1979 .

[43]  P. Stanley,et al.  Failure probability analysis of an elastic orthotropic brittle cylinder subjected to axisymmetric thermal and pressure loading , 1977 .

[44]  Somnath Ghosh,et al.  Particle fracture simulation in non-uniform microstructures of metal-matrix composites , 1998 .

[45]  P. M. Naghdi,et al.  SOME REMARKS ON ELASTIC-PLASTIC DEFORMATION AT FINITE STRAIN , 1971 .

[46]  David L. McDowell,et al.  On the driving force for fatigue crack formation from inclusions and voids in a cast A356 aluminum alloy , 2001 .

[47]  Robert P. Wei,et al.  Statistical analysis of constituent particles in 7075-T6 aluminum alloy , 2006 .

[48]  R. H. Wagoner,et al.  On precipitate induced hardening in crystal plasticity: theory , 2004 .

[49]  D. Hoitsma,et al.  SIPS, A Structural Integrity Prognosis System , 2007, 2007 IEEE Aerospace Conference.

[50]  Stress concentration due to a hemispherical surface inclusion , 1993 .

[51]  K. Tanaka,et al.  Average stress in matrix and average elastic energy of materials with misfitting inclusions , 1973 .

[52]  En-Jui Lee.  Elastic-Plastic Deformation at Finite Strains , 1969 .