Fiber breakage in polymer-matrix composite during static and fatigue loading, observed by electrical resistance measurement

By measuring the electrical resistance of a continuous unidirectional carbon fiber epoxy-matrix composite along the fiber direction during loading in this direction, fiber breakage was progressively monitored in real time. Fiber breakage occurred in spurts involving 1000 or more fibers. It started at about half of the failure strain during static tensile loading and at about half of the fatigue life during tension–tension fatigue testing. Immediately before static failure, at least 35% of the fibers were broken. Immediately before fatigue failure, at least 18% of the fibers were broken. The fiber breakage was accompanied by decrease in modulus.

[1]  D.D.L. Chung,et al.  Electromechanical behavior of carbon fiber , 1998, Smart Structures.

[2]  D.D.L. Chung,et al.  Continuous carbon fibre epoxy-matrix composite as a sensor of its own strain , 1996 .

[3]  L. Vincent,et al.  Damage mechanisms characterisation of carbon fibre/epoxy composite laminates by both electrical resistance measurements and acoustic emission analysis , 1996 .

[4]  Gerard Franklyn Fernando,et al.  An intensity-based optical fibre sensor for fatigue damage detection in advanced fibre-reinforced composites , 1995 .

[5]  Hiroaki Yanagida,et al.  Materials design of CFGFRP-reinforced concretes with diagnosing function for preventing fatal fracture , 1995 .

[6]  M. Miyayama,et al.  Foreseeing of Fracture in CFGFRP Composites by the Measurement of Residual Change in Electrical Resistance , 1992 .

[7]  R. Prabhakaran,et al.  Damage assessment through electrical resistance measurement in graphite fiber-reinforced composites , 1990 .

[8]  Karl Schulte,et al.  Load and failure analyses of CFRP laminates by means of electrical resistivity measurements , 1989 .

[9]  R. Jamison.  The role of microdamage in tensile failure of graphite/epoxy laminates☆ , 1985 .

[10]  Paul S. Steif,et al.  Stiffness Reduction Due to Fiber Breakage , 1984 .

[11]  Tk O'Brien,et al.  Fatigue Damage: Stiffness/Strength Comparisons for Composite Materials , 1977 .

[12]  B. Harris,et al.  Acoustic emission studies of filament-wound carbon fibre reinforced rings and pressure vessels , 1976 .

[13]  B. Harris,et al.  An evaluation of acoustic emission techniques applied to carbon-fibre composites , 1976 .

[14]  B. Harris,et al.  Tensile failure mechanisms in carbon fibre reinforced plastics , 1975 .

[15]  A. R. Bunsell,et al.  Acoustic emission during cyclic loading of carbon-fibre-reinforced plastics , 1975 .