Thermal, Mechanical, Viscoelastic and Morphological Properties of Poly(lactic acid) based Biocomposites with Potato Pulp Powder Treated with Waxes

The thermal, mechanical and viscoelastic properties of biocomposites of poly(lactic acid) (PLA) with 20 wt.% of potato pulp powder were investigated. The potato pulp powder utilized is a byproduct from the production and extraction of starch. The results showed that the potato pulp powder does not act as reinforcement, but as filler for PLA, due to an unfavorable aspect ratio and the irregular shape of the particles. In order to improve the mechanical response of the PLA/potato pulp powder biocomposites, surface treatment of the potato pulp particles with bio-based and petroleum-based waxes was investigated. This treatment was found to improve the properties of the biocomposites, enhancing the adhesion between the PLA based polymeric matrix and the potato pulp fibers. The best result is obtained with a petroleum-based wax, but also the bio-based waxes lead to good mechanical properties of the biocomposite. Thus, the addition to PLA of potato pulp powder, treated with waxes, appears a method able to (i) utilize and valorize an abundant agro-food biomass such as potato pulp, according to the principles of circular economy, (ii) favor the production of articles with properties valuable for practical applications, and (iii) reduce the cost of the final products, considering the relatively high cost of PLA.

[1]  Qinglin Wu,et al.  Thermal decomposition kinetics of natural fibers: Activation energy with dynamic thermogravimetric analysis , 2008 .

[2]  Andrea Lazzeri,et al.  Effect of nucleating agents on crystallinity and properties of poly (lactic acid) (PLA) , 2017 .

[3]  A. Błędzki,et al.  Composites reinforced with cellulose based fibres , 1999 .

[4]  M. Sain,et al.  Thermorheological and mechanical properties of cellulose reinforced PLA bio-composites , 2015 .

[5]  Bikash Mohanty,et al.  Melt–solid polycondensation of lactic acid and its biodegradability , 2009 .

[6]  Rui Huang,et al.  On transcrystallinity in semi-crystalline polymer composites , 2005 .

[7]  K. P. Sandeep,et al.  Preparation and characterization of bio-nanocomposite films based on soy protein isolate and montmorillonite using melt extrusion , 2010 .

[8]  Long Yu,et al.  Polymer blends and composites from renewable resources , 2006 .

[9]  G. Wegner,et al.  Investigation of the structure of solution grown crystals of lactide copolymers by means of chemical reactions , 1973 .

[10]  Manjusri Misra,et al.  Composites from renewable and sustainable resources: Challenges and innovations , 2018, Science.

[11]  F. L. Matthews,et al.  A study of transcrystallinity and its effect on the interface in flax fibre reinforced composite materials , 2001 .

[12]  P. Pimienta,et al.  Mechanical Properties , 2018, Bainite in Steels.

[13]  M. Narkis,et al.  A deformational mechanism in particulate‐filled glassy polymers , 1973 .

[14]  Andrea Lazzeri,et al.  Evaluation of Mechanical and Interfacial Properties of Bio-Composites Based on Poly(Lactic Acid) with Natural Cellulose Fibers , 2019, International journal of molecular sciences.

[15]  A. Södergård,et al.  Properties of lactic acid based polymers and their correlation with composition , 2002 .

[16]  K. Pickering,et al.  A review of recent developments in natural fibre composites and their mechanical performance , 2016 .

[17]  A. Chiralt,et al.  Combination of Poly(lactic) Acid and Starch for Biodegradable Food Packaging , 2017, Materials.

[18]  R. Lappalainen,et al.  Utilization of agricultural and forest industry waste and residues in natural fiber-polymer composites: A review. , 2016, Waste management.

[19]  A. P. Tulloch.  The composition of beeswax and other waxes secreted by insects , 1970, Lipids.

[20]  S. Mohanty,et al.  Influence of Different Treated Cellulose Fibers on the Mechanical and Thermal Properties of Poly(lactic acid) , 2016 .

[21]  B. Pukánszky.  Influence of interface interaction on the ultimate tensile properties of polymer composites , 1990 .

[22]  W. B. Pedersen,et al.  Biodegradable composites based on l-polylactide and jute fibres , 2003 .

[23]  M. Laus,et al.  Temperature dependence of the rigid amorphous fraction in poly(ethylene terephthalate) , 2014 .

[24]  Chul B. Park,et al.  Poly(lactic acid) crystallization , 2012 .

[25]  I. C. Mcneill,et al.  Degradation studies of some polyesters and polycarbonates—1. Polylactide: General features of the degradation under programmed heating conditions , 1985 .

[26]  Haiping Yang,et al.  Characteristics of hemicellulose, cellulose and lignin pyrolysis , 2007 .

[27]  Sung-Hoon Ahn,et al.  Recent Advances in the Application of Natural Fiber Based Composites , 2010 .

[28]  Angela Montanari,et al.  Processing, Valorization and Application of Bio-Waste Derived Compounds from Potato, Tomato, Olive and Cereals: A Review , 2017 .

[29]  D. Piotrowski,et al.  [Introduction to rheology]. , 1982, Acta haematologica Polonica.

[30]  T. Mekonnen,et al.  Progress in bio-based plastics and plasticizing modifications , 2013 .

[31]  Y. Inoue,et al.  Polymorphism and isomorphism in biodegradable polyesters , 2009 .

[32]  J. Jog,et al.  Natural fiber polymer composites: A review , 1999 .

[33]  D. Dollimore,et al.  Comparative thermal analysis study of two biopolymers, starch and cellulose , 1997 .

[34]  R. Pantani,et al.  Thermal and hydrolytic degradation kinetics of PLA in the molten state , 2014 .

[35]  P. Pagès,et al.  Processing of poly(lactic acid): characterization of chemical structure, thermal stability and mechanical properties , 2010 .

[36]  P. Cinelli,et al.  Thermal, Mechanical, and Rheological Properties of Biocomposites Made of Poly(lactic acid) and Potato Pulp Powder , 2019, International journal of molecular sciences.

[37]  E. Piorkowska,et al.  Composites of poly(L‐lactide) with hemp fibers: Morphology and thermal and mechanical properties , 2007 .

[38]  C. Schick,et al.  Melting of Conformationally Disordered Crystals (α′-Phase) of Poly(l-lactic acid) , 2014 .

[39]  G. Höhne,et al.  Metrologically based procedures for the temperature, heat and heat flow rate calibration of DSC , 1997 .

[40]  Maya Jacob John,et al.  Biofibres and Biocomposites , 2008 .

[41]  Rahul Bhardwaj,et al.  Renewable resource-based green composites from recycled cellulose fiber and poly(3-hydroxybutyrate-co-3-hydroxyvalerate) bioplastic. , 2006, Biomacromolecules.

[42]  A. N. Nakagaito,et al.  Polylactic acid (PLA) biocomposites reinforced with coir fibres: Evaluation of mechanical performance and multifunctional properties , 2014 .

[43]  J. Furukawa,et al.  A Molecular Theory of Filler Reinforcement Based upon the Conception of Internal Deformation (A Rough Approximation of the Internal Deformation) , 1962 .

[44]  K. Satyanarayana,et al.  Biodegradable composites based on lignocellulosic fibers—An overview , 2009 .

[45]  M. Skrifvars,et al.  Natural fibres as reinforcement in polylactic acid (PLA) composites , 2003 .

[46]  C. Schick,et al.  Melting and reorganization of poly(ethylene terephthalate) on fast heating (1000 K/s) , 2004 .

[47]  F. Signori,et al.  Amorphous/crystal and polymer/filler interphases in biocomposites from poly(butylene succinate) , 2012 .

[48]  A. Błędzki,et al.  Biocomposites reinforced with natural fibers: 2000–2010 , 2012 .

[49]  L. E. Vandenburg,et al.  The structural constituents of carnauba wax , 1970 .

[50]  A. Amash,et al.  Morphology and properties of isotropic and oriented samples of cellulose fibre–polypropylene composites , 2000 .

[51]  B. Wunderlich,et al.  Heat capacity of poly(lactic acid) , 2002 .

[52]  L. Palade,et al.  Melt Rheology of High l-Content Poly(lactic acid) , 2001 .

[53]  Andrea Lazzeri,et al.  Effect of Potato Pulp Filler on the Mechanical Properties and Water Vapor Transmission Rate of Thermoplastic WPI/PBS Blends , 2016 .

[54]  Elisa Zini,et al.  Green composites: An overview , 2011 .

[55]  I. Ferguson,et al.  Effect of surface treatment on thermal stability of the hemp-PLA composites: Correlation of activation energy with thermal degradation , 2014 .

[56]  M. Gazzano,et al.  Enthalpy of melting of α′- and α-crystals of poly(l-lactic acid) , 2015 .

[57]  M. Laus,et al.  Rigid amorphous fraction and melting behavior of poly(ethylene terephthalate) , 2014, Colloid and Polymer Science.