Discussion on "Can water cause brittle fracture failures of non-ceramic insulators in the absence of electric field" [and reply]
暂无分享,去创建一个
Barzin Mobasher | Maciej Kumosa | R. S. Gorur | L. Kumosa | D. Armentrout | R. Gorur | B. Mobasher | M. Kumosa | L. Kumosa | D. Armentrout
[1] M. Kumosa,et al. Causes and potential remedies of brittle fracture failure of composite (nonceramic) insulators , 2004, IEEE Transactions on Dielectrics and Electrical Insulation.
[2] Maciej Kumosa,et al. Acoustic emission from stress corrosion cracks in aligned GRP , 1987 .
[3] Maciej Kumosa,et al. Boron-free fibers for prevention of acid induced brittle fracture of composite insulator GRP rods , 2003 .
[4] Maciej Kumosa,et al. The Stress Corrosion Experiments on an E-Glass/Epoxy Unidirectional Composite , 2000 .
[5] P. Spitéri,et al. Durability of Closed-End Pressurized GRP Pipes under Hygrothermal Conditions. Part I: Monotonic Tests , 1996 .
[6] H. Herman. A Structural Materials: Properties, Microstructure and Processing. , 1995 .
[7] Barzin Mobasher,et al. Mechanism of brittle fracture in nonceramic insulators , 2002 .
[8] M. Kumosa,et al. Can water cause brittle fracture failures of composite non-ceramic insulators in the absence of electric fields? , 2004, IEEE Transactions on Dielectrics and Electrical Insulation.
[9] A. Akhtar,et al. Failure analysis of brittle fracture in nonceramic insulators , 1987 .
[10] L. Pargamin,et al. "Brittle fracture" of composite insulators: why and how they occur , 2000, 2000 Power Engineering Society Summer Meeting (Cat. No.00CH37134).
[11] M. Kumosa,et al. FTIR analysis of non-ceramic composite insulators , 2004, IEEE Transactions on Dielectrics and Electrical Insulation.
[12] J. T. Burnham,et al. Gunshot damage to ceramic and nonceramic insulators , 1997 .
[13] R. Gorur,et al. Brittle fracture in nonceramic insulators: electrical aspects of microscopic flaws in glass reinforced plastic (GRP) rods , 2002 .
[14] P. Davies,et al. Influence of mechanical stresses on the hydrolytic aging of standard and low styrene unsaturated polyester composites , 2002 .
[15] Maciej Kumosa,et al. An investigation of brittle fracture of composite insulator rods in an acid environment with either static or cyclic loading , 2000 .
[16] David W. Lischer,et al. The Durability of E-Glass/Vinyl Ester Composite Materials Subjected to Environmental Conditioning and Sustained Loading , 1998 .
[17] Qiong Qiu. Brittle fracture mechanisms of glass-fiber reinforced polymer insulators , 1995 .
[18] Maciej Kumosa,et al. Stress corrosion cracking in a unidirectional E-glass/polyester composite subjected to static and cyclic loading conditions , 2003 .
[19] R. Gupta,et al. Effect of Aging Environment on Degradation of Glass-Reinforced Epoxy , 2002 .
[20] Maciej Kumosa,et al. Chemical analysis of a field-failed composite suspension insulator , 1998 .
[21] Y. Mai,et al. Evaluation of Property Retention in E-Glass/Vinylester Composites after Exposure to Salt Solution and Natural Weathering , 2000 .
[22] Maciej Kumosa,et al. Brittle Fracture of Non-Ceramic Suspension Insulators with Epoxy Cone End-Fittings , 1997 .
[23] Maciej Kumosa,et al. Resistance to stress corrosion cracking of unidirectional ECR-glass/polymer composites for high voltage composite insulator applications , 2003 .
[24] H. M. Schneider,et al. Aging of non-ceramic insulators due to corona from water drops. Discussion , 1999 .
[25] Maciej Kumosa,et al. The Effect of Sandblasting on the Initiation of Stress Corrosion Cracking in Unidirectional E-Glass/Polymer Composites Used in High Voltage Composite (Non-Ceramic) Insulators , 2002 .
[26] Maciej Kumosa,et al. Stress corrosion of aligned glass fibre-polyester composite material , 1985 .
[27] Maciej Kumosa,et al. Initiation of Stress Corrosion Cracking in Unidirectional Glass/Polymer Composite Materials , 2001 .
[28] Maciej Kumosa,et al. ANALYSES OF COMPOSITE INSULATORS WITH CRIMPED END- FITTINGS: PART II - SUITABLE CRIMPING CONDITIONS , 2002 .
[29] Maciej Kumosa,et al. Evaluation of Stress Corrosion Properties of Pultruded Glass Fiber/Polymer Composite Materials , 2001 .
[30] D. Dornfeld. Book reviewAcoustic emission, vol. 2: edited by J. R. Matthews; published by Gordon and Breach, New York, 1983; 168 pp.; price, U.S. $39.50 , 1985 .
[31] M. Kumosa,et al. Resistance to brittle fracture of glass reinforced polymer composites used in composite (nonceramic) insulators , 2005, IEEE Transactions on Power Delivery.
[32] Maciej Kumosa,et al. Corrosion of E-glass fibers in acidic environments , 1997 .
[33] Maciej Kumosa,et al. Moisture absorption properties of unidirectional glass/polymer composites used in composite (non-ceramic) insulators , 2004 .
[34] S. J. Harris,et al. Failure of high voltage electrical insulators with pultruded glass fibre-reinforced plastic cores , 1986 .
[35] S. J. Harris,et al. Metallographic investigation of the damage caused to GRP by the combined action of electrical, mechanical and chemical environments , 1984 .
[36] M. Kuhl. FRP rods for brittle fracture resistant composite insulators , 2001 .
[37] T. M. Damiani,et al. Phenomenological Prediction of Tensile Strength of E-Glass Composites from Available Aging and Stress Corrosion Data , 2003 .
[38] R. Gorur,et al. Effect of long-term corona on non-ceramic outdoor insulator housing materials , 2001 .
[39] M. Kumosa,et al. Water diffusion into and electrical testing of composite insulator GRP rods , 2004, IEEE Transactions on Dielectrics and Electrical Insulation.
[40] Maciej Kumosa,et al. An investigation of brittle fracture in composite materials used for high voltage insulators , 1998 .
[41] Maciej Kumosa,et al. Analyses of composite insulators with crimped end-fittings: Part I—non linear finite element computations , 2002 .
[42] Maciej Kumosa,et al. Mechanical Evaluation of Axially Loaded Composite Insulators with Crimped End-Fittings , 1997 .
[43] David W. Lischer,et al. Mechanical and microstructural properties of notched E-glass/vinyl ester composite materials subjected to the environment and a sustained load , 2001 .
[44] Maciej Kumosa,et al. Finite element analysis of substation composite insulators , 1995 .
[45] Barzin Mobasher,et al. Mechanical aspects of crimped glass reinforced plastic (GRP) rods , 2003 .
[46] Maciej Kumosa,et al. Acoustic emission monitoring of stress corrosion cracks in aligned GRP , 1987 .
[47] Maciej Kumosa,et al. An evaluation of the critical conditions for the initiation of stress corrosion cracking in unidirectional E-glass/polymer composites , 2001 .
[48] H. W. King,et al. The aging of silicate glass surfaces in humid air , 1997 .
[49] R. Gorur,et al. Impact of corona on the long-term performance of nonceramic insulators , 2003, IEEE Transactions on Dielectrics and Electrical Insulation.
[50] K. Liao,et al. Influence of moisture-induced stress on in situ fiber strength degradation of unidirectional polymer composite , 2001 .
[51] M. Shioya,et al. The use of a single-fibre fragmentation test to study environmental durability of interfaces/interphases between DGEBA/mPDA epoxy and glass fibre: the effect of moisture , 1994 .
[52] Maciej Kumosa,et al. Resistance to Stress Corrosion Cracking of Unidirectional Glass/Polymer Composites Based on Low and High Seed ECR- glass Fibers for High Voltage Composite Insulator Applications , 2003 .
[53] V. Karbhari,et al. Low‐temperature hygrothermal degradation of ambient cured E‐glass/vinylester composites , 2002 .
[54] S. J. Harris,et al. Stress corrosion cracking of GRP pultruded rods in acid environments , 1983 .
[55] J. T. Burnham,et al. IEEE Task Force Report: brittle fracture in nonceramic insulators , 2002 .