One-step fabrication of optically transparent polydimethylsiloxane artificial lotus leaf film using under-exposed under-baked photoresist mold

We report an extremely simple one-step fabrication method of flexible, optically transparent super-hydrophobic polydimethylsiloxane (PDMS) thin film using under-exposed under-baked photoresist (PR) mold. Significant under soft bake condition makes photoresist retains good amount of solvents which greatly increase the dissolution rate. Once this condition is combined with the under-exposure condition, it would create a mushroom-like structure on the PR mold. The replicated PDMS using this PR mold showed hierarchical micro/nano scale features on the high aspect ratio pillar array structure. Contact angles and optical transmittance of various surfaces were tested and results were compared. A static contact angle as high as 163° was achieved. These micro/nano patterned super-hydrophobic transparent PDMS films could be used in various water-repellent applications.

[1]  Bo Lu,et al.  Highly flexible, transparent and patternable parylene-C superhydrophobic films with high and low adhesion , 2011, 2011 IEEE 24th International Conference on Micro Electro Mechanical Systems.

[2]  Jun-Bo Yoon,et al.  A robust superhydrophobic and superoleophobic surface with inverse-trapezoidal microstructures on a large transparent flexible substrate , 2010 .

[3]  Tingrui Pan,et al.  Photopatternable Superhydrophobic Nanocomposites for Microfabrication , 2010, Journal of Microelectromechanical Systems.

[4]  Ho-Young Kim,et al.  Nanoscale patterning of microtextured surfaces to control superhydrophobic robustness. , 2010, Langmuir : the ACS journal of surfaces and colloids.

[5]  W. King,et al.  Hydrophobicity of curved microstructured surfaces , 2010 .

[6]  J. Cooper,et al.  Creation of super-hydrophobic siloxane-modified SU-8 microstuctures , 2009 .

[7]  Neelesh Patankar,et al.  Design of surface hierarchy for extreme hydrophobicity. , 2009, Langmuir : the ACS journal of surfaces and colloids.

[8]  M. Im,et al.  "Lock-and-key" geometry effect of patterned surfaces: wettability and switching of adhesive force. , 2009, Small.

[9]  Bharat Bhushan,et al.  Contact angle, adhesion and friction properties of micro-and nanopatterned polymers for superhydrophobicity , 2006 .

[10]  Guozhong Cao,et al.  Optically transparent superhydrophobic silica-based films , 2005 .

[11]  John A. Rogers,et al.  Nanotransfer printing by use of noncovalent surface forces: Applications to thin-film transistors that use single-walled carbon nanotube networks and semiconducting polymers , 2004 .

[12]  S. Basu,et al.  Mechanisms for contact angle hysteresis and advancing contact angles , 1999 .

[13]  O. Takai,et al.  Preparation of ultra water-repellent films by microwave plasma-enhanced CVD , 1997 .

[14]  Wilhelm Barthlott,et al.  Characterization and Distribution of Water-repellent, Self-cleaning Plant Surfaces , 1997 .

[15]  Kazufumi Ogawa,et al.  Development of a Transparent and Ultrahydrophobic Glass Plate , 1993 .