Utilizing acid pretreatment and electrospinning to improve biocompatibility of poly(glycolic acid) for tissue engineering.

Poly(glycolic acid) (PGA) has a long history as a bioresorbable polymer. Its biocompatibility is widely accepted, yet PGA is often rejected as a soft-tissue scaffold because of fibrous encapsulation. The goal of this study was to improve the soft-tissue biocompatibility of PGA by producing scaffolds composed of small-diameter fibers through electrospinning and subjecting these scaffolds to a concentrated hydrochloric acid (HCL) pretreatment. The theory is that small-diameter fibers will elicit a reduced immune response and HCl treatment will improve cellular interactions. Scaffolds were characterized in terms of fiber diameter and pore area via image-analysis software. Biocompatibility was assessed through a WST-1 cell-proliferation assay (in vitro) with the use of rat cardiac fibroblasts and rat intramuscular implantations (in vivo). Fibers produced ranged in diameter from 0.22 to 0.88 microm with pore areas from 1.84 to 13.22 microm(2). The untreated scaffold composed of 0.88-microm fibers was encapsulated in vivo and supported the lowest rates of cell proliferation. On the contrary, the acid pretreated scaffold with 0.22-microm fibers was incorporated into the surrounding tissue and exhibited proliferation rates that exceeded the control populations on tissue-culture plastic. In conclusion, this study has shown the ability to improve the biocompatibility of PGA through acid pretreatment of scaffolds comprised of submicron fiber diameters.

[1]  David J. Mooney,et al.  Synthesis and Properties of Biodegradable Polymers Used as Synthetic Matrices for Tissue Engineering , 1997 .

[2]  T. Groth,et al.  Studies on cell-biomaterial interaction: role of tyrosine phosphorylation during fibroblast spreading on surfaces varying in wettability. , 1996, Biomaterials.

[3]  Thomas J Webster,et al.  Polymers with nano-dimensional surface features enhance bladder smooth muscle cell adhesion. , 2003, Journal of biomedical materials research. Part A.

[4]  D J Mooney,et al.  Smooth muscle cell adhesion to tissue engineering scaffolds. , 2000, Biomaterials.

[5]  John Layman,et al.  Release of tetracycline hydrochloride from electrospun poly(ethylene-co-vinylacetate), poly(lactic acid), and a blend. , 2002, Journal of controlled release : official journal of the Controlled Release Society.

[6]  G. Wnek,et al.  Electrospinning of Collagen Type II: A Feasibility Study , 2003 .

[7]  Gary E. Wnek,et al.  Electrospinning of Nanofiber Fibrinogen Structures , 2003 .

[8]  Gary E. Wnek,et al.  TAILORING TISSUE ENGINEERING SCAFFOLDS USING ELECTROSTATIC PROCESSING TECHNIQUES: A STUDY OF POLY(GLYCOLIC ACID) ELECTROSPINNING , 2001 .

[9]  R. Langer,et al.  Engineering Biomaterials for Tissue Engineering: The 10‚Äì100 Micron Size Scale , 1999 .

[10]  C. E. Stiles,et al.  Tissue response to single-polymer fibers of varying diameters: evaluation of fibrous encapsulation and macrophage density. , 2000, Journal of biomedical materials research.

[11]  R Langer,et al.  Surface hydrolysis of poly(glycolic acid) meshes increases the seeding density of vascular smooth muscle cells. , 1998, Journal of biomedical materials research.

[12]  T K Borg,et al.  Expression of collagen binding integrins during cardiac development and hypertrophy. , 1991, Circulation research.

[13]  David G Simpson,et al.  Electrospinning of collagen nanofibers. , 2002, Biomacromolecules.

[14]  T. Webster,et al.  Mechanisms of enhanced osteoblast adhesion on nanophase alumina involve vitronectin. , 2001, Tissue engineering.

[15]  V. I. Samoilov,et al.  Morphogenetic response of cultured normal and transformed fibroblasts, and epitheliocytes, to a cylindrical substratum surface. Possible role for the actin filament bundle pattern. , 1994, Journal of cell science.

[16]  T. Decker,et al.  A quick and simple method for the quantitation of lactate dehydrogenase release in measurements of cellular cytotoxicity and tumor necrosis factor (TNF) activity. , 1988, Journal of immunological methods.

[17]  J D Stitzel,et al.  Arterial Smooth Muscle Cell Proliferation on a Novel Biomimicking, Biodegradable Vascular Graft Scaffold , 2001, Journal of biomaterials applications.