Synthesis and Characterization of LPCVD Polysilicon and Silicon Nitride Thin Films for MEMS Applications

Inherent residual stresses during material deposition can have profound effects on the functionality and reliability of fabricated MEMS devices. Residual stress often causes device failure due to curling, buckling, or fracture. Typically, the material properties of thin films used in surface micromachining are not very well controlled during deposition. The residual stress, for example, tends to vary significantly for different deposition conditions; experiments were carried out to study the polysilicon and silicon nitride deposited by Low Pressure Chemical Vapor Deposition (LPCVD) method at wide range of process conditions. High temperature annealing effects on stress in case polysilicon are also reported. The reduced residual stress levels can significantly improve device performance, reliability, and yield as MEMS devices become smaller.

[1]  Tong-Yi Zhang,et al.  Measurements of residual stresses in thin films using micro-rotating-structures , 1998 .

[2]  G. Sessler,et al.  Charge storage in APCVD silicon nitride , 1997, IEEE 1997 Annual Report Conference on Electrical Insulation and Dielectric Phenomena.

[3]  S. Wolf,et al.  Silicon Processing for the VLSI Era , 1986 .

[4]  Impact of long, high temperature anneals on residual stress in polysilicon , 1997, Proceedings of International Solid State Sensors and Actuators Conference (Transducers '97).

[5]  W. Brown,et al.  Effect of deposition conditions on thermo-mechanical properties of free standing silicon-rich silicon nitride thin film , 2012 .

[6]  O. Paul,et al.  Process Temperature–Dependent Mechanical Properties of Polysilicon Measured Using a Novel Tensile Test Structure , 2007, Journal of Microelectromechanical Systems.

[7]  Johannes G.E. Gardeniers,et al.  LPCVD silicon‐rich silicon nitride films for applications in micromechanics, studied with statistical experimental design* , 1996 .

[8]  A. G. Noskov,et al.  Correlation between stress and structure in chemically vapour deposited silicon nitride films , 1988 .

[9]  James M. Olson,et al.  Analysis of LPCVD process conditions for the deposition of low stress silicon nitride. Part I: preliminary LPCVD experiments , 2002 .

[10]  Frans Spaepen,et al.  Interfaces and stresses in thin films , 2000 .

[11]  J. Wołoszyn.  A method for controlling residual film stress in LPCVD polysilicon films for surface micromachined MEMS , 2004, 2004 IEEE/SEMI Advanced Semiconductor Manufacturing Conference and Workshop (IEEE Cat. No.04CH37530).

[12]  Patrick J. French,et al.  Polysilicon: a versatile material for microsystems , 2002 .

[13]  Shou-Yi Chang,et al.  Effect of residual stresses on mechanical properties and interface adhesion strength of SiN thin films , 2009 .

[14]  O. Paul,et al.  Advanced silicon microstructures, sensors, and systems , 2007 .

[15]  Jan G. Korvink,et al.  MEMS: A Practical Guide to Design, Analysis, and Applications , 2005 .

[16]  T. P. Ma,et al.  Making Silicon Nitride Film a Viable Gate Dielectric , 1998 .

[17]  Prasanna Kumar Sahu,et al.  Estimation of analog/RF figures-of-merit using device design engineering in gate stack double gate MOSFET , 2015 .

[18]  J. G. E. Gardeniersa,et al.  LPCVD silicon-rich silicon nitride films for applications in micromechanics , studied with statistical experimental design * , 1996 .

[19]  Bruce M. Clemens,et al.  Crystallite coalescence: A mechanism for intrinsic tensile stresses in thin films , 1999 .