Mode I delamination growth of multidirectional composite laminates under fatigue loading
暂无分享,去创建一个
Libin Zhao | Jianyu Zhang | R. Bao | Lei Peng | B. Fei | Hongqin Yang
[1] Gerald Pinter,et al. Development of a standardized procedure for the characterization of interlaminar delamination propagation in advanced composites under fatigue mode I loading conditions , 2009 .
[2] A. Canteli,et al. Interlaminar crack initiation and growth rate in a carbon-fibre epoxy composite under mode-I fatigue loading , 2008 .
[3] J. Botsis,et al. Bridging tractions in mode I delamination: Measurements and simulations , 2008 .
[4] Peter Davies,et al. A status report on delamination resistance testing of polymer-matrix composites , 2008 .
[5] Masaki Hojo,et al. Mode I delamination fatigue properties of interlayer-toughened CF/epoxy laminates , 2006 .
[6] A. Szekrényes,et al. Advanced beam model for fiber-bridging in unidirectional composite double-cantilever beam specimens , 2005 .
[7] A. Morais,et al. 2960 - MODE I INTERLAMINAR FRACTURE OF CARBON/EPOXY MULTIDIRECTIONAL LAMINATES , 2004 .
[8] Leif Asp,et al. Mixed-mode delamination growth in carbon-fibre composite laminates under cyclic loading , 2004 .
[9] P.M.S.T. de Castro,et al. Mode-I interlaminar fracture of carbon/epoxy cross-ply composites , 2002 .
[10] Emile S. Greenhalgh,et al. Delamination Growth and Thresholds in a Carbon/Epoxy Composite under Fatigue Loading , 2001 .
[11] V. Tamužs,et al. Progressive delamination and fiber bridging modeling in double cantilever beam composite specimens , 2001 .
[12] M. Benzeggagh,et al. Initiation and bifurcation mechanisms of cracks in multi-directional laminates , 2000 .
[13] J. G. Williams,et al. Delamination Fracture of Multidirectional Carbon-Fiber/Epoxy Composites under Mode I, Mode II and Mixed-Mode I/II Loading , 1999 .
[14] Peter Davies,et al. Standard Test Methods for Delamination Resistance of Composite Materials: Current Status , 1998 .
[15] George A. Kardomateas,et al. Growth of internal delaminations under cyclic compression in composite plates , 1994 .
[16] C. Gustafson,et al. Effect of matrix resin on delamination fatigue crack growth in CFRP laminates , 1994 .
[17] J. G. Williams,et al. The Effects of Geometry, Rate and Temperature on the Mode I, Mode II and Mixed-Mode I/II Interlaminar Fracture of Carbon-Fibre/Poly(ether-ether ketone) Composites , 1990 .
[18] T. Adachi,et al. Mode I fatigue delamination of Zanchor-reinforced CF/epoxy laminates , 2010 .
[19] D. Le,et al. A total fatigue life model for mode I delaminated composite laminates , 2006 .
[20] Tong Earn Tay,et al. Characterization and analysis of delamination fracture in composites: An overview of developments from 1990 to 2001 , 2003 .
[21] F. Brandt. New load introduction concept for improved and simplified delamination beam testing , 1998 .
[22] J. Williams,et al. Mechanics and mechanisms of delamination in a poly(ether sulphone)—Fibre composite , 1990 .
[23] Masaki Hojo,et al. Effect of stress ratio on near-threshold propagation of delimination fatigue cracks in unidirectional CFRP , 1987 .
[24] John D. Whitcomb,et al. Characterization of Mode I and mixed-mode delamination growth in T300/5208 graphite/epoxy , 1985 .
[25] W. S. Johnson. Delamination and Debonding of Materials , 1985 .