Unprecedented atomic surface of silicon induced by environmentally friendly chemical mechanical polishing.

Silicon (Si) dominates the integrated circuit (IC), semiconductor, and microelectronic industries. However, it is a challenge to achieve a sub-angstrom surface of Si. Chemical mechanical polishing (CMP) is widely used in the manufacturing of Si, while toxic and polluted slurries are usually employed in CMP, resulting in pollution to the environment. In this study, a novel environmentally friendly CMP was developed, in which a slurry is composed of ceria, hydrogen peroxide, sodium pyrophosphate, sodium carboxymethyl cellulose, sodium carbonate, and deionized water. After CMP, the surface roughness Sa was 0.067 nm with a measurement area of 50 × 50 μm2, and a sub-angstrom surface is achieved. To the best of our knowledge, it is the lowest surface roughness in such a large area. Transmission electron microscopy shows that the thickness of the damaged layer after CMP is 2.8 nm. X-ray photoelectron spectroscopy and infrared Fourier transformation reveal that during CMP, a redox reaction firstly took place between Ce3+ and Ce4+. Si and ceria are hydroxylated, forming Si-OH and Ce-OH, then dehydration and condensation occur, generating Si-O-Ce. These findings propose new insights to fabricate a sub-angstrom surface of Si for use in IC, semiconductor, and microelectronic industries.

[1]  Zhenyu Zhang,et al.  Atomic-scale surface of fused silica induced by chemical mechanical polishing with controlled size spherical ceria abrasives , 2023, Journal of Manufacturing Processes.

[2]  Dongdong Liu,et al.  Environment-friendly chemical mechanical polishing for copper with atomic surface confirmed by transmission electron microscopy , 2023, Colloids and Surfaces A: Physicochemical and Engineering Aspects.

[3]  Shibo Zhang,et al.  Study of the humidity-controlled CeO2 fixed-abrasive chemical mechanical polishing of a single crystal silicon wafer , 2022, Tribology International.

[4]  Chao Zhang,et al.  Synthesis and polishing characteristics of a novel green GO/diamond hybrid slurry under ultrasonic technology , 2022, Ceramics International.

[5]  D. Guo,et al.  An insight into polishing slurry for high quality and efficiency polishing of diamond , 2022, Tribology International.

[6]  Longfei Ren,et al.  Investigation of fluoride and silica removal from semiconductor wastewaters with a clean coagulation-ultrafiltration process , 2022, Chemical Engineering Journal.

[7]  M. Jamshidi,et al.  Silanizing Nano SiO2 and Its Application in Recycled Nitrile Rubber to Prepare Super Oil Resistant/Superhydrophobic/Superoleophilic Oil/Water Separator , 2022, Journal of Environmental Chemical Engineering.

[8]  Hanxiao Wang,et al.  Control of the Micro-Defects on the Surface of Silicon Wafer in Chemical Mechanical Polishing , 2022, ECS Journal of Solid State Science and Technology.

[9]  Zhenyu Zhang,et al.  A novel slurry for chemical mechanical polishing of single crystal diamond , 2021 .

[10]  Emily A. Smith,et al.  Non-Innocent Role of the Ceria Support in Pd-Catalyzed Halophenol Hydrodehalogenation , 2021, ACS Catalysis.

[11]  Jin-Goo Park,et al.  Investigation of the effect of different cleaning forces on Ce-O-Si bonding during oxide post-CMP cleaning , 2021 .

[12]  J. Bowers,et al.  Laser soliton microcombs heterogeneously integrated on silicon , 2021, Science.

[13]  Zheng Wang,et al.  The Role of Ceria in a Hybrid Catalyst toward Alkaline Water Oxidation. , 2020, ChemSusChem.

[14]  Jie Cheng,et al.  RE (La, Nd and Yb) doped CeO2 abrasive particles for chemical mechanical polishing of dielectric materials: Experimental and computational analysis , 2020 .

[15]  R. Kang,et al.  Effects of pressure and slurry on removal mechanism during the chemical mechanical polishing of quartz glass using ReaxFF MD , 2020 .

[16]  Z. Wang,et al.  Roles and mechanism analysis of chitosan as a green additive in low-tech node copper film chemical mechanical polishing , 2020 .

[17]  A. Fratalocchi,et al.  Perfect secrecy cryptography via mixing of chaotic waves in irreversible time-varying silicon chips , 2019, Nature Communications.

[18]  Y. Gan,et al.  Morphological and crystallographic evolution of patterned silicon substrate etched in TMAH solutions , 2019 .

[19]  L. Qian,et al.  Effect of counter-surface chemistry on defect-free material removal of monocrystalline silicon , 2019, Wear.

[20]  C. Ballif,et al.  25.1%-Efficient Monolithic Perovskite/Silicon Tandem Solar Cell Based on a p-type Monocrystalline Textured Silicon Wafer and High-Temperature Passivating Contacts , 2019, ACS Energy Letters.

[21]  R. F. Zhang,et al.  Influences of Na2SiO3 and EDTA-ZnNa2 concentration on properties of zinc-containing coatings on WE43 magnesium alloys , 2018, Surface and Coatings Technology.

[22]  T. Hayat,et al.  Selective Immobilization of Highly Valent Radionuclides by Carboxyl Functionalized Mesoporous Silica Microspheres: Batch, XPS, and EXAFS Analyses , 2018, ACS Sustainable Chemistry & Engineering.

[23]  Weidong Zhou,et al.  Flexible Transient Optical Waveguides and Surface‐Wave Biosensors Constructed from Monocrystalline Silicon , 2018, Advanced materials.

[24]  K. Uvdal,et al.  Cerium oxide nanoparticles with antioxidant capabilities and gadolinium integration for MRI contrast enhancement , 2018, Scientific Reports.

[25]  Xinchun Lu,et al.  Nanomanufacturing of silicon surface with a single atomic layer precision via mechanochemical reactions , 2018, Nature Communications.

[26]  P. M. Pandey,et al.  Use of chemical oxidizers with alumina slurry in Double Disk Magnetic Abrasive Finishing for improving surface finish of Si (100) , 2018 .

[27]  Irmandy Wicaksono,et al.  Corrugation Architecture Enabled Ultraflexible Wafer‐Scale High‐Efficiency Monocrystalline Silicon Solar Cell , 2018 .

[28]  J. Lahann,et al.  Dehydration and dehydroxylation of C-S-H phases synthesized on silicon wafers , 2018 .

[29]  S. Andreescu,et al.  Interaction, transformation and toxicity assessment of particles and additives used in the semiconducting industry. , 2018, Chemosphere.

[30]  W. Zaghdoudi,et al.  “Enhancement of the photoluminescence property of hybrid structures using single-walled carbon nanotubes/pyramidal porous silicon surface” [J. Alloy. Comp. 731 (2018) 978–984] , 2018, Journal of Alloys and Compounds.

[31]  Jacob M. Taylor,et al.  A coherent spin–photon interface in silicon , 2017, Nature.

[32]  Tao Chen,et al.  Material removal model of ultrasonic elliptical vibration-assisted chemical mechanical polishing for hard and brittle materials , 2017 .

[33]  Xinhuan Niu,et al.  Effect of a novel chelating agent on defect removal during post-CMP cleaning , 2016 .

[34]  Xi Zhang,et al.  Cucurbit[8]uril-Containing Multilayer Films for the Photocontrolled Binding and Release of a Guest Molecule. , 2016, Langmuir : the ACS journal of surfaces and colloids.

[35]  Zhenghe Xu,et al.  The pH-dependant attachment of ceria nanoparticles to silica using surface analytical techniques , 2015 .

[36]  Xiaodong Wang,et al.  Humidity Dependence of Tribochemical Wear of Monocrystalline Silicon. , 2015, ACS applied materials & interfaces.

[37]  P. Bera,et al.  XPS studies on the interaction of CeO2 with silicon in magnetron sputtered CeO2 thin films on Si and Si3N4 substrates , 2013 .

[38]  E. Vanea,et al.  XPS and Raman study of zinc containing silica microparticles loaded with insulin , 2013 .

[39]  B. Yan,et al.  Development of hot melt adhesive pad and its application to polishing of monocrystalline silicon , 2012 .

[40]  Shenghai Yang,et al.  Effects of Process Parameters on Electrochemical Characteristics of Silicon Wafers during Chemical Mechanical Polishing , 2009 .

[41]  Jiwang Yan,et al.  Nondestructive measurement of machining-induced amorphous layers in single-crystal silicon by laser micro-Raman spectroscopy , 2008 .

[42]  Songlin Feng,et al.  Ceria concentration effect on chemical mechanical polishing of optical glass , 2007 .

[43]  A. Eyring,et al.  Concentration of Ce3+ and Oxygen Vacancies in Cerium Oxide Nanoparticles , 2006 .

[44]  J. Gardella,et al.  Development of Ti Kα x radiation for electron spectroscopy for chemical analysis of polymer surfaces , 1989 .

[45]  G. Hollinger.  Structures chimique et electronique de l'interface SiO2-Si , 1981 .

[46]  T. Fang,et al.  Revealing the mechanisms for inactive rolling and wear behaviour on chemical mechanical planarization , 2022, Applied Surface Science.

[47]  Bin Wu,et al.  A review: green chemical mechanical polishing for metals and brittle wafers , 2021, Journal of Physics D: Applied Physics.

[48]  Michael D. Feit,et al.  Microscopic Removal Function and the Relationship Between Slurry Particle Size Distribution and Workpiece Roughness During Pad Polishing , 2014 .

[49]  H. Konno,et al.  X-ray photoelectron spectra of hexavalent iron , 1980 .