Degradation Behavior and Accelerated Weathering of Composite Boards Produced from Waste Tetra Pak® Packaging Materials

Manufacturing panels from Tetra Pak® (TP) packaging material might be an alternative to conventional wood-based panels. This study evaluated some chemical and physical properties as well as biological, weathering, and fire performance of panels with and without zinc borate (ZnB) by using shredded TP packaging cartons. Such packaging material, a worldwide well-known multilayer beverage packaging system, is composed of cellulose, low-density polyethylene (LDPE), and aluminum (Al). Panels produced from waste TP packaging material were also examined by FT-IR to understand the fungal deterioration and extent of degradation after accelerated weathering. Before FT-IR investigations, panel specimens were ground under nitrogen atmosphere due to non-uniformity of the composite material. The FT-IR results showed that fungal degradation occurred in the natural polymer of the panel matrix. Although the natural polymer is mostly composed of cellulose, there were also small amounts of polyoses and lignin. It was seen that especially polyose and lignin bands in FT-IR spectra were affected more than cellulose bands by fungal attack. No changes were observed by the fungi in the plastic component (LDPE) of the matrix; however, LDPE seemed more sensitive to weathering than cellulose. Incorporation of ZnB at loading level of 1% (w/w) did not contribute fire performance of the panels when compared to control panel specimens, while a loading level of 10% improved fire performance considering test parameters such as mass loss, ignition time and peak heat release rate.

[1]  S. Pişkin,et al.  Thermal degradation characteristic of Tetra Pak panel boards under inert atmosphere , 2013, Korean Journal of Chemical Engineering.

[2]  A. McDonald,et al.  Effects of wood species on durability and chemical changes of fungal decayed wood plastic composites , 2011 .

[3]  H. Heise,et al.  Degradation profile of polyethylene after artificial accelerated weathering , 2003 .

[4]  R. Stollberger,et al.  Detection of fungal wood decay using Magnetic Resonance Imaging , 2001, Holz als Roh- und Werkstoff.

[5]  O. Faix,et al.  Classification of Lignins from Different Botanical Origins by FT-IR Spectroscopy , 1991 .

[6]  G. Dai,et al.  Effect of hydrothermal environment on moisture absorption and mechanical properties of wood flour–filled polypropylene composites , 2002 .

[7]  K. J. Harrington,et al.  Infrared Spectra of Eucalyptus regnans F. Muell. and Pinus radiata D. Don , 1964 .

[8]  J. Yanik,et al.  Pyrolysis of the tetra pak. , 2009, Waste management.

[9]  R. Singh,et al.  An overview on the degradability of polymer nanocomposites , 2005 .

[10]  M. Gürü,et al.  Manufacturing low density boards from waste cardboards containing aluminium , 2007 .

[11]  F. J. Fuentes-Talavera,et al.  Evaluation of accelerated decay of wood plastic composites by Xylophagus fungi. , 2009 .

[12]  M. Hidalgo.  Manufacturing rigid board by packaging waste containing aluminum and polyethylene , 2011 .

[13]  Craig Clemons,et al.  Wood-plastic composites in the United States: the interfacing of two industries , 2002 .

[14]  Z. Candan,et al.  Fungicide and insecticide properties of cardboard panels made from used beverage carton with veneer overlay , 2010 .

[15]  N. Cabrera,et al.  The water absorption behaviour of all-polypropylene composites and its effect on mechanical properties , 2010 .

[16]  T. Yoshimura,et al.  Wood and Bamboo-PP Composites: Fungal and Termite Resistance, Water Absorption, and FT-IR Analyses , 2013 .

[17]  J. J. Morrell,et al.  Water sorption characteristics of two wood-plastic composites , 2004 .

[18]  T. Peijs,et al.  Effects of environmental conditions on mechanical and physical properties of flax fibers , 2001 .

[19]  L. Alzate-Gaviria,et al.  Effect of biological degradation by termites on the flexural properties of pinewood residue/recycled high‐density polyethylene composites , 2013 .

[20]  A. Pitman,et al.  FTIR studies of the changes in wood chemistry following decay by brown-rot and white-rot fungi , 2003 .

[21]  Chaowen Wu,et al.  Pyrolysis of tetra pack in municipal solid waste , 2001 .

[22]  F. Mantia,et al.  Accelerated weathering of polypropylene/wood flour composites , 2008 .

[23]  M. Felisberti,et al.  Composite of low-density polyethylene and aluminum obtained from the recycling of postconsumer aseptic packaging , 2006 .

[24]  Laurent M. Matuana,et al.  Characterization of weathered wood–plastic composite surfaces using FTIR spectroscopy, contact angle, and XPS ☆ , 2007 .

[25]  R. Runkel,et al.  Zur Kenntnis des thermoplastischen Verhaltens von Holz , 1951, Holz als Roh- und Werkstoff.

[26]  M. Wålinder,et al.  MOISTURE SORPTION IN ARTIFICIALLY AGED WOOD-PLASTIC COMPOSITES , 2012 .

[27]  Xiaoming Du,et al.  Contamination Characteristics and Degradation Behavior of Low-Density Polyethylene Film Residues in Typical Farmland Soils of China , 2006, Journal of environmental science and health. Part. B, Pesticides, food contaminants, and agricultural wastes.

[28]  Salim Hiziroglu,et al.  Physical and mechanical properties of cardboard panels made from used beverage carton with veneer overlay , 2008 .

[29]  Liangchi Zhang,et al.  Grinding-hardening with liquid nitrogen: Mechanisms and technology , 2007 .

[30]  Gary T. Howard,et al.  Biodegradation of polyurethane: a review , 2002 .

[31]  S. Karlsson,et al.  Comparison of water absorption in natural cellulosic fibres from wood and one-year crops in polypropylene composites and its influence on their mechanical properties , 2004 .

[32]  M. Davis.  A Rapid Modified Method for Compositional Carbohydrate Analysis of Lignocellulosics by High pH Anion-Exchange Chromatography with Pulsed Amperometric Detection (HPAEC/PAD) , 1998 .

[33]  T. Buffeteau,et al.  Photo- and Bio-Degradation Processes in Polyethylene, Cellulose and their Blends Studied by ATR-FTIR and Raman Spectroscopies , 2005 .