Electromigration reliability of redistribution lines in wafer-level chip-scale packages

Wafer-level chip-scale packages (WLCSPs) have become subject to the same drive for miniaturization as all electronic packages. The I/O count is increasing and ball pitch is shrinking at the expense of trace pitch and in turn, current densities are increasing. This leads to current crowding and Joule heating in the vicinity of solder joints and under bump metallurgy (UBM) structures where resistance values change significantly. These phenomena are responsible for structural damage of redistribution line (RDL)/UBM and UBM/solder interconnects due to ionic diffusion or electromigration. In this work, sputtered Al and electroplated Cu RDLs are examined and quantified by three-dimensional electrothermal coupling analysis. Results provide a guideline for estimating maximum allowable currents and electromigration lifetime.

[1]  H.-U. Schreiber,et al.  Activation energies for the different electromigration mechanisms in aluminum , 1981 .

[2]  Leonard C. Feldman,et al.  Electronic thin film science : for electrical engineers and materials scientists , 1996 .

[3]  G. Reimbold,et al.  Evidence of grain-boundary versus interface diffusion in electromigration experiments in copper damascene interconnects , 2003 .

[4]  I. Blech.  Electromigration in thin aluminum films on titanium nitride , 1976 .

[5]  Yi-Shao Lai,et al.  An experimental investigation of current stressing on wafer-level chip-scale packages , 2006, 2006 8th Electronics Packaging Technology Conference.

[6]  King-Ning Tu,et al.  Effect of current crowding on void propagation at the interface between intermetallic compound and solder in flip chip solder joints , 2006 .

[7]  Y. Lai,et al.  Calibration of Electromigration Reliability of Flip-Chip Packages by Electrothermal Coupling Analysis , 2006 .

[8]  Yi-Shao Lai,et al.  Redistribution in wafer level chip size packaging technology for high power device applications: Process and design considerations , 2010, Microelectron. Reliab..

[9]  Y. Lai,et al.  Electromigration Reliability and Morphologies of Cu Pillar Flip-Chip Solder Joints with Cu Substrate Pad Metallization , 2008, 2008 58th Electronic Components and Technology Conference.

[10]  B. Burton,et al.  The Contribution of Grain-Boundary Diffusion to Creep at Low Stresses , 1970 .

[11]  King-Ning Tu,et al.  Solder Joint Technology: Materials, Properties, and Reliability , 2007 .

[12]  Yi-Shao Lai,et al.  Electromigration Reliability of 96.5Sn–3Ag–0.5Cu Flip-Chip Solder Joints With Au/Ni/Cu or Cu Substrate Pad Metallization , 2009 .

[13]  Yi-Shao Lai,et al.  Characteristics of current crowding in flip-chip solder bumps , 2006, Microelectron. Reliab..

[14]  Yi-Shao Lai,et al.  Electrothermal coupling analysis of current crowding and Joule heating in flip-chip packages , 2006, Microelectron. Reliab..

[15]  James R. Lloyd,et al.  Electromigration in Thin Film Conductors , 1997 .

[16]  K. Tu.  Recent advances on electromigration in very-large-scale-integration of interconnects , 2003 .