Cu–ZnO and Cu–ZnO/Al2O3 Catalysts for the Reverse Water-Gas Shift Reaction. The Effect of the Cu/Zn Ratio on Precursor Characteristics and on the Activity of the Derived Catalysts

Comparison is made between Cu–ZnO and alumina-supported Cu–ZnO as catalysts for the reverse water-gas shift (RWGS) reaction. For both types of catalyst the Cu/Zn ratio has been varied between Cu-rich and Zn-rich compositions. By applying X-ray diffractometry, X-ray line broadening, optical reflectance spectroscopy and other techniques the effects on the structural and physical properties of the hydroxycarbonate precursors, the calcined products and the ultimately derived catalysts are determined. The presence of alumina decreases the crystallite size of the CuO and ZnO particles produced on calcination and at high Cu/Zn ratios increases the dispersion of copper in the final catalyst. The activities of the catalysts for the RWGS reaction at 513K are compared and the most active are shown to be those which are Cu rich (Cu/Zn > 3) and contain alumina as support. The activities of all the catalysts can be rationalized by referring the activity to unit surface area of copper metal.

[1]  D. Stirling,et al.  Catalytic Activity of Reduced CuxZn(1-x)O and CuO/CuxZn(1-x)O in CO2/H2 Reactions , 1993 .

[2]  F. Garbassi,et al.  XPS study on the low-temperature CO shift reaction catalyst: II. The effects of the addition of alumina and reaction conditions , 1984 .

[3]  Shin-ichiro Fujita,et al.  Mechanism of the reverse water gas shift reaction over Cu/ZnO catalyst , 1992 .

[4]  G. Chinchen,et al.  Sensitive and insensitive reactions on copper catalysts: the water-gas shift reaction and methanol synthesis from carbon dioxide , 1991 .

[5]  S. Ghose.  The crystal structure of hydrozincite, Zn5(OH)6(CO3)2 , 1964 .

[6]  R. Höppener,et al.  Preparation and characterization of stable copper/zinc oxide/alumina catalysts for methanol systhesis , 1986 .

[7]  S. Fujita,et al.  Mechanisms of Methanol Synthesis from Carbon Dioxide and from Carbon Monoxide at Atmospheric Pressure over Cu/ZnO , 1995 .

[8]  G. D. Piero,et al.  Catalysts for low-temperature methanol synthesis. II: Catalytic behavior of Cu/Zn/Al mixed oxides , 1985 .

[9]  G. Ertl,et al.  Handbook of Heterogeneous Catalysis , 1997 .

[10]  R. Sahay,et al.  Study of copper—zinc oxide catalysts, characterisation of the coprecipitate and mixed oxide , 1989 .

[11]  F. Trifiró,et al.  Catalysts for low-temperature methanol synthesis. I. A study of the reduction process , 1982 .

[12]  P. Porta,et al.  Characterization of copper-zinc mixed oxide system in relation to different precursor structure and morphology , 1991 .

[13]  Richard G. Herman,et al.  Catalytic synthesis of methanol from COH2: I. Phase composition, electronic properties, and activities of the Cu/ZnO/M2O3 catalysts , 1979 .

[14]  G. D. Piero,et al.  Catalysts for low-temperature methanol synthesis: preparation of Cu-Zn-Al mixed oxides via hydrotalcite-like precursors , 1984 .

[15]  Jens K. Nørskov,et al.  A Kinetic Model of Methanol Synthesis , 1995 .

[16]  R. Herman,et al.  Precursors of the copper-zinc oxide methanol synthesis catalysts , 1985 .

[17]  R. A. Hadden,et al.  Relationship between the copper surface area and the activity of CuO/ZnO/Al2O3 water-gas shift catalysts , 1995 .

[18]  G. Moretti,et al.  Structural characterization of malachite-like coprecipitated precursors of binary CuOZnO catalysts , 1988 .

[19]  M. S. Spencer.  Precursors of copper/zinc oxide catalysts , 2000 .

[20]  R. Feidenhans'l,et al.  In situ cell for combined XRD and on-line catalysis tests : studies of Cu-based water gas shift and methanol catalysts , 1991 .

[21]  S. Fujita,et al.  Mechanism of the formation of precursors for the Cu/ZnO methanol synthesis catalysts by a coprecipitation method , 1995 .

[22]  G. Lin,et al.  Novel conception of the methanol synthesis mechanism on conventional Cu-containing catalysts , 2000 .