Size-effect on concentration quenching in Yb3+-doped Y3Al5O12 nano-crystals

Abstract Ytterbium-doped nano-crystalline powders of yttrium aluminium garnet Y 3 Al 5 O 12 (Yb 3+ -doped YAG) have been prepared by a modified Pechini method. The morphology of the annealed materials was observed using SEM images. The structure and the average crystalline grain sizes have been determined by X-ray powder diffraction measurements. An increase in elongated spherical crystalline grain sizes from 20 to 50 nm has been observed with annealing temperature increasing from 800 to 1200 °C. The Yb 3+ concentration dependence of both luminescence spectra and lifetimes has been investigated and compared with those reported for the Yb 3+ -doped YAG bulk single crystals. Decays of Yb 3+ 2 F 5/2 excited state, much longer in nano-crystalline powders than in bulk single crystals, are discussed in terms of refractive index dependence.

[1]  K. Shimizu,et al.  A ductile ceramic eutectic composite with high strength at 1,873 K , 1997, Nature.

[2]  H. Jenssen,et al.  Fluorescence lifetimes for neodymium-doped yttrium aluminum garret and yttrium oxide powders , 1982 .

[3]  C. Bowden,et al.  Spectroscopic study of Yb doped oxide crystals for intrinsic optical bistability , 2000, Nonlinear Optics: Materials, Fundamentals, and Applications. Technical Digest. Postconference Edition. TOPS Vol.46 (IEEE Cat. No.00CH37174).

[4]  Ken-ichi Ueda,et al.  72 W Nd:Y3Al5O12 ceramic laser , 2001 .

[5]  C. Goutaudier,et al.  Crystal growth, Yb3+ spectroscopy, concentration quenching analysis and potentiality of laser emission in Ca1−XYbXF2+X , 2004 .

[6]  T. Parthasarathy,et al.  Deformation Behavior of an Al2O3─Y3Al5O12 Eutectic Composite in Comparison with Sapphire and YAG , 1993 .

[7]  Akio Ikesue,et al.  Fabrication and Optical Properties of High‐Performance Polycrystalline Nd:YAG Ceramics for Solid‐State Lasers , 1995 .

[8]  G. Boulon.  Why so deep research on Yb3+-doped optical inorganic materials? , 2008 .

[9]  Fuxi Gan,et al.  Dependence of the Yb 3+ emission cross section and lifetime on temperature and concentration in yttrium aluminum garnet , 2003 .

[10]  C. Goutaudier,et al.  Radiative and non-radiative energy transfers in Yb3+-doped sesquioxide and garnet laser crystals from a combinatorial approach based on gradient concentration fibers , 2003 .

[11]  R. Buchanan,et al.  Energy Levels of Yb 3 + in Gallium and Aluminum Garnets. I. Spectra , 1967 .

[12]  R. Meltzer,et al.  Dependence of fluorescence lifetimes of Y2O3 : Eu3+ nanoparticles on the surrounding medium , 1999 .

[13]  Akio Ikesue,et al.  Scattering in Polycrystalline Nd:YAG Lasers , 2005 .

[14]  R. I. Zakharchenya,et al.  Radiative transitions and spectral-hole burning in MgO: Cr3+ nanocrystals , 2003 .

[15]  Kunio Yoshida,et al.  Synthesis of Nd3+,Cr3+‐codoped YAG Ceramics for High‐Efficiency Solid‐State Lasers , 1995 .

[16]  W. Stręk,et al.  Luminescence properties of Nd:YAG nanoceramics prepared by low temperature high pressure sintering method , 2007 .

[17]  Hirotoshi Sato,et al.  Spectroscopic properties, concentration quenching, and prediction of infrared laser emission of Yb 3+ -doped KY 3 F 10 cubic crystal , 2007 .

[18]  Eiichiro Nakazawa,et al.  Cooperative Luminescence in YbPO 4 , 1970 .