论文信息 - Rate capability of lithium intercalation into nano-porous graphitized carbons

Rate capability of lithium intercalation into nano-porous graphitized carbons

Abstract Nano-porous graphitized carbons were successfully prepared by using mono-dispersed SiO 2 colloidal crystal as a template and mesophase pitch as a carbon source with final heat treatment temperatures (HTT) of 1000–2500 °C. Rate capability of lithium intercalation/de-intercalation of the nano-porous graphitized carbons was investigated. 35–60% of capacities were retained when the current density was increased from 37.2 mA g − 1 to 372 mA g − 1 . Electrochemical impedance spectra indicated that formation of SEI layers caused increased polarization.

[1] G. G. Stokes. "J." , 1890, The New Yale Book of Quotations.

[2] N. Nakashima,et al. A Mesoporous Nanocomposite of TiO2 and Carbon Nanotubes as a High‐Rate Li‐Intercalation Electrode Material , 2006 .

[3] R. Huggins. Solid State Ionics , 1989 .

[4] T. Kudo,et al. Electrochemical Study of High Electrochemical Double Layer Capacitance of Ordered Porous Carbons with Both Meso/Macropores and Micropores , 2007 .

[5] R. Hurt,et al. Liquid crystal surface anchoring of mesophase pitch , 2003 .

[6] T. Kudo,et al. High Power Battery Electrodes Using Nanoporous V2O5/Carbon Composites , 2007 .

[7] T. Abe,et al. Surface Film Formation on a Graphite Negative Electrode in Lithium-Ion Batteries: Atomic Force Microscopy Study on the Effects of Film-Forming Additives in Propylene Carbonate Solutions , 2001 .

[8] T. Abe,et al. Graphitized Carbon Nanobeads with an Onion Texture as a Lithium‐Ion Battery Negative Electrode for High‐Rate Use , 2005 .

[9] T. Kudo,et al. Interconnected macroporous TiO2 (anatase) as a lithium insertion electrode material , 2004 .

[10] T. Kudo,et al. Electric double layer capacitance on hierarchical porous carbons in an organic electrolyte , 2008 .