Thermal expansion coefficient and thermomechanical properties of SiN(x) thin films prepared by plasma-enhanced chemical vapor deposition.

We present a new method based on fast Fourier transform (FFT) for evaluating the thermal expansion coefficient and thermomechanical properties of thin films. The silicon nitride thin films deposited on Corning glass and Si wafers were prepared by plasma-enhanced chemical vapor deposition in this study. The anisotropic residual stress and thermomechanical properties of silicon nitride thin films were studied. Residual stresses in thin films were measured by a modified Michelson interferometer associated with the FFT method under different heating temperatures. We found that the average residual-stress value increases when the temperature increases from room temperature to 100°C. Increased substrate temperature causes the residual stress in SiN(x) film deposited on Si wafers to be more compressive, but the residual stress in SiN(x) film on Corning glass becomes more tensile. The residual-stress versus substrate-temperature relation is a linear correlation after heating. A double substrate technique is used to determine the thermal expansion coefficients of the thin films. The experimental results show that the thermal expansion coefficient of the silicon nitride thin films is 3.27×10(-6)°C(-1). The biaxial modulus is 1125 GPa for SiN(x) film.

[1]  M. Takeda,et al.  Fourier transform profilometry for the automatic measurement of 3-D object shapes. , 1983, Applied optics.

[2]  D. Gerstenberg,et al.  Physics of Thin Films , 1964 .

[3]  R. N. Karekar,et al.  Stress in Thin Films Due to Volume Change on Solidification , 1973, May 16.

[4]  Jeremy Thurn,et al.  Evaluation of film biaxial modulus and coefficient of thermal expansion from thermoelastic film stress measurements , 2004 .

[5]  R. W. Hoffman,et al.  Stress distributions and thin film mechanical properties , 1981 .

[6]  C. Weng,et al.  Thermoviscoelastic stresses in thin films/substrate system , 2007 .

[7]  Gunnar Suchaneck,et al.  Low-temperature PECVD-deposited silicon nitride thin films for sensor applications , 2001 .

[8]  Steven M. Yalisove,et al.  Stress anisotropy and stress gradient in magnetron sputtered films with different deposition geometries , 2006 .

[9]  The measurement of anisotropic stress in obliquely-deposited thin films by fast Fourier transform and Gaussian filter , 2011 .

[10]  Hsi-Chao Chen,et al.  Reduction of residual stress in optical silicon nitcide thin films prepared by radio-frequency ion beam sputtering deposition , 2010 .

[11]  G. Stoney.  The Tension of Metallic Films Deposited by Electrolysis , 1909 .

[12]  M. Maeda,et al.  Stress evaluation of radio-frequency-biased plasma-enhanced chemical vapor deposited silicon nitride films , 1998 .

[13]  W. Macy,et al.  Two-dimensional fringe-pattern analysis. , 1983, Applied optics.

[14]  R. Swanepoel.  Determination of the thickness and optical constants of amorphous silicon , 1983 .

[15]  John Robertson,et al.  Low temperature growth of silicon nitride by electron cyclotron resonance plasma enhanced chemical vapour deposition , 2001 .

[16]  C. Tien,et al.  Measuring residual stress of anisotropic thin film by fast Fourier transform. , 2010, Optics express.

[17]  M. Takeda,et al.  Fourier-transform method of fringe-pattern analysis for computer-based topography and interferometry , 1982 .

[18]  K. Chung,et al.  Microstructure and properties of silicon nitride thin films deposited by reactive bias magnetron sputtering , 1998 .

[19]  R. K. Pandey,et al.  Growth and characterization of silicon nitride films for optoelectronics applications , 2004 .

[20]  Shaopeng Ma,et al.  Full-field measurement of nonuniform stresses of thin films at high temperature. , 2011, Optics express.

[21]  R. K. Pandey,et al.  Effect of deposition temperature on the chemical properties of thermally deposited silicon nitride films , 2005 .

[22]  F. Tay,et al.  A new fabrication method for low stress PECVD - SiN x layers , 2006 .