Preparation of porous chromium oxide nanotubes using carbon nanotubes as templates and their application as an ethanol sensor

Chromium oxide nanotubes were successfully prepared using multi-walled carbon nanotubes (MWCNTs) as a template via a supercritical fluid-mediated route. In this method, with chromium (III) nitrate nonahydrate as precursor, chromium oxide was first deposited on MWCNTs in supercritical ethanol in the presence of NH(4)HCO(3). The as-prepared chromium oxide/MWCNT nanocomposites were characterized by transmission electron microscopy, x-ray diffraction, infrared spectroscopy and thermogravimetric analysis. It was demonstrated that the MWCNTs were coated with a layer of amorphous Cr(2)O(3)·xH(2)O. The thickness of the Cr(2)O(3)·xH(2)O sheath on MWCNTs could be tuned by manipulating the ratio of precursor to MWCNTs. Calcining the composites at 550 °C, the MWCNTs were removed, producing polycrystalline α-Cr(2)O(3) nanotubes. The as-prepared α-Cr(2)O(3) sample was used as a sensor material to detect ethanol vapor, and it was demonstrated that the α-Cr(2)O(3) nanotubes exhibited good performance even at 400 °C.

[1]  C. Brinker,et al.  Ordered nanocrystal/silica particles self-assembled from nanocrystal micelles and silicate. , 2006, Chemical communications.

[2]  R. Ku,et al.  Electrical conductivity in sputter-deposited chromium oxide coatings , 1985 .

[3]  Zhenzhong Yang,et al.  General synthetic route toward functional hollow spheres with double-shelled structures. , 2005, Angewandte Chemie.

[4]  W. Han,et al.  Synthesizing boron nitride nanotubes filled with SiC nanowires by using carbon nanotubes as templates , 1999 .

[5]  Liyi Shi,et al.  Carbon nanotube assisted synthesis of CeO2 nanotubes , 2007 .

[6]  Alex Zettl,et al.  Coating Single-Walled Carbon Nanotubes with Tin Oxide , 2003 .

[7]  Zhong Lin Wang,et al.  Nanobelts of Semiconducting Oxides , 2001, Science.

[8]  Yi Zhang,et al.  A novel method to prepare Cr2O3 nanoparticles , 2008 .

[9]  F. Cavani,et al.  Chemical and Physical Characterization of Alumina-Supported Chromia-Based Catalysts and Their Activity in Dehydrogenation of Isobutane , 1996 .

[10]  I. Wachs,et al.  Surface chemistry of supported chromium oxide catalysts , 1993 .

[11]  Charles M Lieber,et al.  Synthesis of CdS and ZnS nanowires using single-source molecular precursors. , 2003, Journal of the American Chemical Society.

[12]  Hao Tan,et al.  Alumina‐Template Synthesis of Fluorescent RuO2 Nanotubes Derived from Ru3(CO)12 Clusters , 2006 .

[13]  B. Bhushan,et al.  Tribological studies of chromium oxide films for magnetic recording applications , 1997 .

[14]  G. Fusco,et al.  Fluidized bed reactors for paraffins dehydrogenation , 1992 .

[15]  Li Wang,et al.  NO2 sensing characteristics of WO3 thin film microgas sensor , 2003 .

[16]  Yi Zhang,et al.  Studies on thermal dehydration of hydrated chromic oxide. , 2003, Journal of colloid and interface science.

[17]  H. Imai,et al.  Direct preparation of anatase TiO2 nanotubes in porous alumina membranes , 1999 .

[18]  G. Park,et al.  Ruthenium Oxide Nanotube Arrays Fabricated by Atomic Layer Deposition Using a Carbon Nanotube Template , 2003 .

[19]  Bongsoo Kim,et al.  A novel Cr2O3 thin film on stainless steel with high sorption resistance , 1999 .

[20]  J. K. Hurst,et al.  Light-controlled molecular switches modulate nanocrystal fluorescence. , 2005, Journal of the American Chemical Society.

[21]  T. Hyeon,et al.  Fabrication of hollow palladium spheres and their successful application to the recyclable heterogeneous catalyst for suzuki coupling reactions. , 2002, Journal of the American Chemical Society.

[22]  Jin-Song Hu,et al.  Pt hollow nanospheres: facile synthesis and enhanced electrocatalysts. , 2004, Angewandte Chemie.

[23]  Caruso,et al.  Nanoengineering of inorganic and hybrid hollow spheres by colloidal templating , 1998, Science.

[24]  S. Mann,et al.  MORPHOSYNTHESIS OF CALCIUM CARBONATE (VATERITE) MICROSPONGES , 1999 .

[25]  I. P. Saraswat,et al.  Characterization of chromium oxide hydrate gel , 1984 .

[26]  Younan Xia,et al.  One‐Dimensional Nanostructures: Synthesis, Characterization, and Applications , 2003 .

[27]  Uri Banin,et al.  Synthesis and size-dependent properties of zinc-blende semiconductor quantum rods , 2003, Nature materials.

[28]  Yadong Li,et al.  ZnSe semiconductor hollow microspheres. , 2003, Angewandte Chemie.

[29]  P. Berdahl.  Pigments to Reflect the Infrared Radiation From Fire , 1995 .

[30]  L. Gao,et al.  A Facile Route to Prepare Mesoporous Anatase TiO2 Nanotubes Assembly , 2006 .

[31]  Heon-Jin Choi,et al.  Single-crystal gallium nitride nanotubes , 2003, Nature.

[32]  Deyu Li,et al.  Fabrication of silica nanotube arrays from vertical silicon nanowire templates. , 2003, Journal of the American Chemical Society.

[33]  A. Wokaun,et al.  Surface structure of crystalline and amorphous chromia catalysts for the selective catalytic reduction of nitric oxide II. Diffuse reflectance FTIR study of thermal treatment and oxygen adsorption , 1992 .

[34]  B. Weckhuysen,et al.  Alkane dehydrogenation over supported chromium oxide catalysts , 1999 .

[35]  Weidong Yang,et al.  Shape control of CdSe nanocrystals , 2000, Nature.

[36]  Shaobin Wang,et al.  Dehydrogenation of ethane with carbon dioxide over supported chromium oxide catalysts , 2000 .

[37]  M. Mcdaniel,et al.  An XPS study of the Phillips Cr/silica polymerization catalyst , 1982 .

[38]  U. Ozkan,et al.  Complete oxidation of ethanol, acetaldehyde and ethanol/methanol mixtures over copper oxide and copper-chromium oxide catalysts , 1993 .

[39]  Buxing Han,et al.  A Highly Efficient Chemical Sensor Material for H2S: α‐Fe2O3 Nanotubes Fabricated Using Carbon Nanotube Templates , 2005 .

[40]  P. Marcus,et al.  Supported chromia catalysts for oxidation of organic compounds , 2000 .

[41]  G. Ghiotti,et al.  Infrared study of surface properties of .alpha.-chromia. I. Preparation and adsorption of water, heavy water, and carbon monoxide , 1971 .

[42]  N. Du,et al.  Porous Indium Oxide Nanotubes: Layer‐by‐Layer Assembly on Carbon‐Nanotube Templates and Application for Room‐Temperature NH3 Gas Sensors , 2007 .

[43]  Qing Peng,et al.  Vanadium Pentoxide Nanobelts: Highly Selective and Stable Ethanol Sensor Materials , 2005 .

[44]  T. Morimoto,et al.  Thermal decomposition of chromium oxide hydroxide: I. Effect of particle size and atmosphere , 1985 .

[45]  Bing Xu,et al.  Magnetic-dipolar-interaction-induced self-assembly affords wires of hollow nanocrystals of cobalt selenide. , 2006, Angewandte Chemie.

[46]  M. Mcdaniel.  The state of Cr(VI) on the Phillips polymerization catalyst: II. The reaction between silica and CrO2Cl2 , 1982 .

[47]  A. Imhof,et al.  Synthesis of Monodisperse Colloidal Spheres, Capsules, and Microballoons by Emulsion Templating , 2005 .

[48]  Changxi Miao,et al.  Preparation of Highly Active Cr2O3-SiO2 Catalyst by Sol-Gel Method for Ethylbenzene Dehydrogenation in the Presence of CO2 , 2006 .

[49]  M. Casaletto,et al.  Chromia/zirconia catalysts with Cr content exceeding the monolayer. A comparison with chromia/alumina and chromia/silica for isobutane dehydrogenation , 1998 .

[50]  P. Alivisatos.  The use of nanocrystals in biological detection , 2004, Nature Biotechnology.

[51]  Charles M. Lieber,et al.  A laser ablation method for the synthesis of crystalline semiconductor nanowires , 1998, Science.

[52]  Charles M. Lieber,et al.  Synthesis and characterization of carbide nanorods , 1995, Nature.

[53]  Yong Wang,et al.  Highly Reversible Lithium Storage in Porous SnO2 Nanotubes with Coaxially Grown Carbon Nanotube Overlayers , 2006 .

[54]  Gabor A. Somorjai,et al.  Formation of Hollow Nanocrystals Through the Nanoscale Kirkendall Effect , 2004, Science.

[55]  E. Samulski,et al.  Fabrication and characterization of nanotubular semiconductor oxides In2O3 and Ga2O3 , 2001 .

[56]  Peidong Yang,et al.  Silicon Vertically Integrated Nanowire Field Effect Transistors , 2006 .