Plastic flow and work hardening of Al alloy matrices during ultrasonic consolidation fibre embedding process

SiC fibres and single mode (SM) optical fibres were successfully embedded in Al alloys matrices through ultrasonic consolidation (UC). The plastic flow of Al alloy matrices was visualized after anodization by optical microscopy with polarized light. Grain and sub-grain sizes of Al alloys before and after UC and work hardening of matrices due to plastic flow during UC process, were studied. The results show that UC process increases the hardness of alloy matrices, especially at regions proximal to fibres, with work hardening following the Hall–Petch relationship for both grains and sub-grains. During UC process, work hardening is mainly caused by bulk plastic deformation with no significant effect from friction at foil/foil interface. For the consolidated materials tested, work hardening in a 3003 O matrix is higher than that in a 6061 O matrix. In addition, plastic deformation of a 3003 O matrix in SM fibre embedded samples is smaller than that in SiC fibre embedded samples, which may have been influenced by the different embedding processes.

[1]  E. Hall,et al.  The Deformation and Ageing of Mild Steel: III Discussion of Results , 1951 .

[2]  Rupert C. Soar,et al.  Characterisation of aluminium alloy 6061 for the ultrasonic consolidation process , 2003 .

[3]  Vladimir Astashev,et al.  Ultrasonic cutting as a nonlinear (vibro-impact) process , 1998 .

[4]  D. Moon.  Grain size and dislocation density in recrystallized siliconiron , 1971 .

[5]  Brent Stucker,et al.  Use of ultrasonic consolidation for fabrication of multi‐material structures , 2007 .

[6]  S. Mannan,et al.  Grain size dependence of the deformation behaviour of cadmium , 1975 .

[7]  Brent Stucker,et al.  Process Parameters Optimization for Ultrasonically Consolidated Fiber-Reinforced Metal Matrix Composites , 2006 .

[8]  F. Blaha,et al.  Plastizitätsuntersuchungen von metallkristallen in ultraschallfeld , 1959 .

[9]  B. Stucker,et al.  Effect of process parameters on bond formation during ultrasonic consolidation of aluminum alloy 3003 , 2006 .

[10]  R. Mathiesen,et al.  Elastic strain and texture evolution during tensile testing of peak-hardened Al-Mg-Si-profiles , 2008 .

[11]  H. Engqvist,et al.  Determination of the average grain size of cemented carbides , 2003 .

[12]  C. Robinson,et al.  Improving Linear Weld Density in Ultrasonically Consolidated Parts , 2006 .

[13]  Brady Aydelotte,et al.  Accessing the elastic–plastic properties closure by rotation and lamination , 2008 .

[14]  Rupert C. Soar,et al.  Fabrication of metal-matrix composites and adaptive composites using ultrasonic consolidation process , 2005 .

[15]  John L. Johnson,et al.  Grain size measurement methods and models for nanograined WC–Co , 2008 .

[16]  R. C. Soar,et al.  Ultrasonic consolidation for embedding SMA fibres within aluminium matrices , 2004 .

[17]  Charalabos C. Doumanidis,et al.  Enhanced diffusion and phase transformations during ultrasonic welding of zinc and aluminum , 2005 .

[18]  D. H. Sansome,et al.  Review of the application of ultrasonic vibrations to deforming metals , 1975 .

[19]  R. Honeycombe,et al.  Plastic Deformation of Metals , 1932, Nature.

[20]  Rupert C. Soar,et al.  A model for weld strength in ultrasonically consolidated components , 2005 .

[21]  Phill Dickens,et al.  Optimum process parameters for ultrasonic consolidation of 3003 aluminium , 2004 .

[22]  Rupert Soar,et al.  Method for embedding optical fibers in an aluminum matrix by ultrasonic consolidation. , 2005, Applied optics.

[23]  Brent Stucker,et al.  An experimental determination of optimum processing parameters for Al/SiC metal matrix composites made using ultrasonic consolidation , 2007 .

[24]  B. Langenecker.  Effects of Ultrasound on Deformation Characteristics of Metals , 1966, IEEE Transactions on Sonics and Ultrasonics.