The effect of front pyramid heights on the efficiency of homogeneously textured inline-diffused screen-printed monocrystalline silicon wafer solar cells

The majority of industrial monocrystalline silicon (c-Si) wafer solar cells are alkaline textured (at least the illuminated surface) to reduce reflection and increase absorption of incident light. Therefore, understanding the influence of front pyramid heights on the solar cell parameters is essential for further improving cell efficiency. In this work we report the impact of pyramid height on the performance of inline-diffused c-Si solar cells. Three alkaline texture processes with potassium silicate additives are optimised to result in homogeneous coverage of pyramids. By modifying the process, surface textures with small (∼5 μm maximum), medium (∼6 μm maximum) and large (∼8 μm maximum) pyramid heights are formed. The impact of pyramid size on cell parameters is experimentally studied using industrial-grade 156-mm pseudo-square p-type Czochralski wafers. It is found that within the pyramid size range studied here, there is no significant variation in effective minority carrier lifetime, reflectance, open-circuit voltage or short-circuit current. However, fill factor and hence efficiency is significantly impacted by pyramid size. While cells in all three groups demonstrate high fill factor (>79%), it is shown that an average fill factor gain of up to 1% absolute can be achieved by using the best-suited texture process.

[1]  P. Verlinden,et al.  The Surface Texturization of Solar-cells - a New Method Using V-grooves With Controllable Sidewall Angles , 1992 .

[2]  C. Backus,et al.  On black solar cells or the tetrahedral texturing of a silicon surface , 1976, IEEE Transactions on Electron Devices.

[3]  Surface Characteristics of (100) Silicon Anisotropically Etched in Aqueous KOH , 1996 .

[4]  K. Bothe,et al.  Impact of oxygen on the permanent deactivation of boron–oxygen-related recombination centers in crystalline silicon , 2010 .

[5]  M. E. Buck,et al.  Experimental optimization of an anisotropic etching process for random texturization of silicon solar cells , 1991, The Conference Record of the Twenty-Second IEEE Photovoltaic Specialists Conference - 1991.

[6]  A. Cuevas,et al.  Electronic properties of light-induced recombination centers in boron-doped Czochralski silicon , 1999 .

[7]  Ronald A. Sinton,et al.  A quasi-steady-state open-circuit voltage method for solar cell characterization , 2000 .

[8]  Thorsten Trupke,et al.  Advanced luminescence based effective series resistance imaging of silicon solar cells , 2008 .

[9]  D. Schroder.  Semiconductor Material and Device Characterization , 1990 .

[10]  Jan Kegel,et al.  IPA-free Texturization of n-type Si Wafers: Correlation of Optical, Electronic and Morphological Surface Properties☆ , 2013 .

[11]  Gunnar Schubert,et al.  Experimental evidence of direct contact formation for the current transport in silver thick film metallized silicon emitters , 2011 .

[12]  R. M. Swanson,et al.  Measurement of the emitter saturation current by a contactless photoconductivity decay method , 1985 .

[13]  Fast Alkaline Etching of Monocrystalline Wafers in KOH/CHX , 2008 .

[14]  Armin G. Aberle,et al.  Generalized analysis of quasi-steady-state and quasi-transient measurements of carrier lifetimes in semiconductors , 1999 .

[15]  P. Basu,et al.  18.7% Efficient inline-diffused screen-printed silicon wafer solar cells with deep homogeneous emitter etch-back , 2013 .

[16]  E. Wefringhaus,et al.  Influence of Surface Topography on the Glass Coverage in the Contact Formation of Silver Screen-Printed Si Solar Cells , 2013, IEEE Journal of Photovoltaics.

[17]  E. Palik,et al.  Etching roughness for (100) silicon surfaces in aqueous KOH , 1991 .

[18]  F. Khan,et al.  Regulated low cost pre-treatment step for surface texturization of large area industrial single crystalline silicon solar cell , 2010 .

[19]  Vinodh Shanmugam,et al.  Influence of random pyramid surface texture on silver screen-printed contact formation for monocrystalline silicon wafer solar cells , 2015 .

[20]  Deren Yang,et al.  Formation of various pyramidal structures on monocrystalline silicon surface and their influence on the solar cells , 2013 .

[21]  P. Basu,et al.  Liquid silicate additive for alkaline texturing of mono-Si wafers to improve process bath lifetime and reduce IPA consumption , 2013 .