Development of a real-time AC/DC data acquisition technique for studies of AC corrosion of pipelines

Abstract In this work, the alternating current (AC), 60 Hz in frequency, corrosion of 16Mn pipeline steel was studied in a simulated soil solution by weight loss and polarization curve measurements, real-time AC/DC (direct current) signal data acquisition (DAQ), and surface characterization. The developed DAQ is capable of separating the DC and AC voltage components from the recorded total reading, providing mechanistic information about the steel corrosion in the presence of AC interference. The corrosion of steel is enhanced by the applied AC current density from 0 to 400 A/m 2 . With the further increase to 600 A/m 2 and 800 A/m 2 , the corrosion rate of the steel decreases, which is attributed to the formation of a compact corrosion product layer on the steel surface at sufficiently high AC current densities, and a compact film is formed on the steel surface. While AC could enhance corrosion of the steel, only a very small percentage of AC current is involved in the steel dissolution (acts as Faradaic current). The vast majority of AC either participates in the charging–discharging process (acts as non-Faradaic current) of the double-charge layer or gets involved in the redox reaction of water.

[1]  Luciano Lazzari,et al.  Influence of AC on Corrosion Kinetics for Carbon Steel, Zinc and Copper , 2005 .

[2]  S. Lalvani,et al.  A revised model for predicting corrosion of materials induced by alternating voltages , 1996 .

[3]  Allen J. Bard,et al.  Electrochemical Methods: Fundamentals and Applications , 1980 .

[4]  Luciano Lazzari,et al.  AC corrosion. Part 2: Parameters influencing corrosion rate , 2010 .

[5]  Y. Hosokawa,et al.  New Cathodic Protection Criteria Based on Direct and Alternating Current Densities , 2004 .

[6]  Guoan Zhang,et al.  On the fundamentals of electrochemical corrosion of X65 steel in CO2-containing formation water in the presence of acetic acid in petroleum production , 2009 .

[7]  L. Lazzari,et al.  AC corrosion - Part 1: Effects on overpotentials of anodic and cathodic processes , 2010 .

[8]  Yufeng Cheng,et al.  Mechanistic investigation of hydrogen-enhanced anodic dissolution of X-70 pipe steel and its implication on near-neutral pH SCC of pipelines , 2007 .

[9]  S. Lalvani,et al.  The corrosion of carbon steel in a chloride environment due to periodic voltage modulation: Part I , 1995 .

[10]  T. Tan,et al.  A.c. corrosion of nickel in sulphate solutions , 1988 .

[11]  J. Gavarri,et al.  Degradation mechanism of electrodes subjected to alternating potentials: modeling and protection , 2002 .

[12]  Y. F. Cheng,et al.  Effect of alternating current on corrosion and effectiveness of cathodic protection of pipelines , 2012 .

[13]  M. Ormellese,et al.  Effect of AC interference on cathodic protection monitoring , 2011 .

[14]  S. Lalvani,et al.  A periodic voltage modulation effect on the corrosion oF Cu-Ni Alloy , 1995 .

[15]  S. Lalvani,et al.  A theoretical approach for predicting AC-induced corrosion , 1994 .

[16]  D. Chin,et al.  The a.c. corrosion of stainless steel—II. The breakdown of passivity of ss304 in neutral aqueous solutions , 1985 .

[17]  Y. F. Cheng,et al.  Effects of alternating current on corrosion of a coated pipeline steel in a chloride-containing carbonate/bicarbonate solution , 2010 .